One-time reinforcing bar-arranging and rapid forming method of magnesite composite agricultural shed support

A composite material, agricultural greenhouse technology, applied in ceramic molding machines, manufacturing tools, etc., can solve the problems of low work efficiency, difficult to form dense slurry, not suitable for large-scale production, etc., to achieve dense structure, no honeycomb, smooth surface. Effect

Inactive Publication Date: 2011-12-21
NANCHANG UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The work efficiency of these greenhouse support forming methods is very low, which is not suitable for large-scale production, and the slurry is not easy to form and dense

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-time reinforcing bar-arranging and rapid forming method of magnesite composite agricultural shed support
  • One-time reinforcing bar-arranging and rapid forming method of magnesite composite agricultural shed support
  • One-time reinforcing bar-arranging and rapid forming method of magnesite composite agricultural shed support

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The forming mold can be made of fiberglass, and its shape is a quarter circle. The inner edge formwork (1) and the outer edge formwork (2) respectively have an end plate, and the inner edge formwork (1) and the outer edge formwork (2) are aligned and positioned through the end plates, and fixed by four fastening clips (3). The 6 bamboo tendons (6) are interspersed and assembled by the stainless steel wire mesh (5) and installed in the mold (4) at one time, so that the bamboo tendons are evenly distributed at equal distances in the mould.

[0019] The composite slurry of magnesite composite material is poured into the greenhouse bracket mold equipped with 6 bamboo bars at one time, and the greenhouse bracket is placed on a 1000mm×4000mm vibrating table. % of the curing room with mold curing 8h demoulding, continue curing at room temperature to 7d after demoulding can be put into use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a one-time reinforcing bar-arranging and rapid forming method of a magnesite composite agricultural shed support, a forming mold consists of an inner edge mold plate, an outer edge mold plate and tightening clamps, wherein the inner edge mold plate and the outer edge mold plate respectively have end plates, and the inner edge mold plate and the outer edge mold plate are aligned and positioned through the end plates and further fixed by the 3-7 tightening clamps; 4-8 bamboo reinforcing bars are arranged in the mold, interpenetrated and assembled by a stainless steel wire mesh and then mounted in the mold once; and magnesite composite slurry which is well stirred is poured into the mold once, compacted by vibration on a vibration table and then stricken off, curing with the mold is carried out in a curing chamber with the temperature of 40 DEG C and the relative humidity of 60%-70% for 8h, then demolding is carried out, and the curing is continuously carried at room temperature till 7d after the demolding, thereby being put into use. The one-time reinforcing bar-arranging and rapid forming method has high forming efficiency, convenient assembly and disassembly of the mold, smooth surface of a formed product and dense structure.

Description

technical field [0001] The invention belongs to the field of magnesite composite material manufacturing, and relates to a rapid prototyping method for preparing magnesite composite material for agricultural greenhouse supports. Background technique [0002] Magnesite composite agricultural greenhouse support is made of magnesium oxychloride gelling material (prepared with light-burned magnesium oxide and magnesium chloride hexahydrate solution) to add light filler or foaming agent to make the quality lighter, and add modifiers, etc. after stirring The plastic slurry is poured and formed in the mold. In order to improve the bearing capacity of the material, the mold needs to be clothed with glass fiber mesh cloth or bamboo bars for reinforcement. At present, the commonly used preparation method is to use artificial wooden molds, lined with PVC plastic boards as moulds, and the stirred magnesite slurry should be layered with glass fiber mesh cloth or bamboo bars, generally 3 t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B28B1/14B28B1/087
Inventor 黄少文习海平
Owner NANCHANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap