Boron-tungsten-iron-nickel alloy electroplating liquid

A nickel alloy and electroplating solution technology, which is applied in the field of alloy electroplating solution, can solve problems such as limited application range, slow electrodeposition speed, and micro-cracks on the surface, and achieve stable process, low environmental hazards, good corrosion resistance and friction resistance Effect

Inactive Publication Date: 2011-08-24
合鸿新材科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above plating types have disadvantages such as high brittleness (iron-tungsten alloy), slow electrodeposition speed (iron-nickel-tungsten alloy), and microcracks on the surface, which limit their application range.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Take by weighing the mixture of 24 grams of sodium citrate and 12 grams of sodium gluconate, add 1 gram of phytic acid into 1000 milliliters of deionized water, stir until dissolved; then weigh 5 grams of ferrous sulfate (FeSO 4 .7H 2 O), 20 grams of nickel sulfate (NiSO 4 .7H 2 O), added to the above solution, stirred at room temperature until dissolved; then the above solution was heated to 65°C with a water bath, and 40 grams of sodium tungstate (Na 2 WO 4 .2H 2 (0), 5 gram of ammonium sulfate, 2 gram of dimethylamine boranes, join in this solution, stir until dissolving, then add 0.8 milliliters of 1,2-propanediol, 0.8 milliliters of formaldehyde and 0.4 milliliters of dimethylhexynols Mixture, adjust the pH value of the solution to 6 with ammonia water; then heat the solution to 75°C with a water bath, the stainless steel is used as the anode, the workpiece is used as the cathode, and the current density is 8A / dm 2 Under electroplating, a bright tungsten alloy...

Embodiment 2

[0019] Take by weighing the mixture of 60 grams of sodium citrate and 30 grams of sodium gluconate, 8 grams of ascorbic acid and add in 1000 milliliters of deionized water, stir until dissolving; Then weigh 30 grams of ferrous sulfate (FeSO 4 .7H 2 O), 60 grams of nickel sulfate (NiSO 4 .7H 2 O), added to the above solution, stirred at room temperature until dissolved; then the above solution was heated to 65°C with a water bath, and 60 grams of sodium tungstate (Na 2 WO 4 .2H 2 (2), 15 grams of ammonium sulfate, 20 grams of dimethylamine borane, join in this solution, stir until dissolving, then add 4 milliliters of 1,2-propanediol, 4 milliliters of formaldehyde and 2 milliliters of dimethylhexynols Mixture, adjust the pH value of the solution to 7 with ammonia water; then heat the solution to 75°C with a water bath, the stainless steel is used as the anode, the workpiece is used as the cathode, and the current density is 8A / dm 2 Under electroplating, a bright tungsten a...

Embodiment 3

[0021] Take by weighing the mixture of 40 grams of sodium citrate and 20 grams of sodium gluconate, add 4 grams of phytic acid into 1000 milliliters of deionized water, stir until dissolving; then weigh 18 grams of ferrous sulfate (FeSO 4 .7H 2 O), 40 grams of nickel sulfate (NiSO 4 .7H 2 O), added to the above solution, stirred at room temperature until dissolved; then the above solution was heated to 65 ° C with a water bath, and 50 grams of sodium tungstate (Na 2 WO 4 .2H 2 (2), 10 grams of ammonium sulfate, 11 grams of dimethylamine borane, join in this solution, stir to dissolve, then add 2.4 milliliters of 1,2-propanediol, 2.4 milliliters of formaldehyde and 1.2 milliliters of dimethylhexynols Mixture, adjust the pH value of the solution to 7 with ammonia water; then heat the solution to 75°C with a water bath, the stainless steel is used as the anode, the workpiece is used as the cathode, and the current density is 8A / dm 2 Under electroplating, a bright tungsten al...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses boron-tungsten-iron-nickel alloy electroplating liquid which is prepared from the following ingredients: 40-60g / L of sodium tungstate, 5-30g / L of ferrous sulfate, 20-60g / L of nickel sulfate, 2-20g / L of (dimethylamino)borane, 5-15g / L of ammonium sulfate, 36-90g / L of complexing agent, 1-8g / L of stabilizing agent, 2-10ml / L of bright additive and 1000ml of deionized water. Theelectroplating liquid does little harm to the environment, has stable process and simple ingredients, is convenient to operate and can be stored for a long term after preparation. The electroplating liquid does not exhaust acid mist during working and has high current efficiency. The plating prepared from the electroplating liquid has no microcracks on the surface and has good corrosion resistance and abrasion resistance.

Description

technical field [0001] The invention relates to an alloy electroplating solution in the field of material surface treatment, in particular to a boron-tungsten-iron-nickel alloy electroplating solution. Background technique [0002] At present, partial wear and corrosion in the field of petroleum machinery are serious, and there is no satisfactory surface treatment technology that can be used for surface treatment of petroleum machinery, which can be anti-corrosion, wear-resistant and low-cost at the same time. With the continuous consumption of petroleum resources, mining The petroleum environment is getting worse and worse, and the requirements for corrosion resistance and friction resistance of petroleum equipment are getting higher and higher. Therefore, the study of anti-corrosion and wear-resistant technology of petroleum machinery has always been a topic of people's concentration. [0003] A possible solution is to electroplate tungsten alloys. Tungsten cannot be elec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C25D3/56
Inventor 赵汝山李淦
Owner 合鸿新材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap