Magnetic ink and preparation method for ink-jet printing flexible electromagnetic wave absorption film

A magnetic ink and nano-magnetic technology, applied in ink, household utensils, applications, etc., can solve the problems of unfavorable large-scale production, complicated process, high cost, etc., and achieve the effect of clear graphic boundaries, high graphic precision and uniform distribution

Inactive Publication Date: 2011-11-02
UNIV OF ELECTRONIC SCI & TECH OF CHINA
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, methods for preparing electromagnetic wave absorbing and shielding flexible films include magnetron sputtering, vapor ph

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnetic ink and preparation method for ink-jet printing flexible electromagnetic wave absorption film
  • Magnetic ink and preparation method for ink-jet printing flexible electromagnetic wave absorption film
  • Magnetic ink and preparation method for ink-jet printing flexible electromagnetic wave absorption film

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0035] Implementation mode one

[0036] Magnetic ink includes the following components:

[0037] A solvent composed of a mixture of ethanol: isopropanol: deionized water = A: B: C by volume, where 1≤A≤4, 1≤B≤3, 6≤C≤12;

[0038] Solutes are nano-magnetic particles, dispersants, linkers, surfactants, wetting agents and defoamers,

[0039] Calculated by mass ratio, nano magnetic particles: dispersant = x: y, where 4≤x≤25, 1≤y≤3; solvent: linking agent: surfactant: wetting agent: defoamer = a: b: c:d:e, where 86.95≤a≤99.199, 0.3≤b≤5, 0.5≤c≤5, 0≤d≤3, 0.001≤e≤0.05;

[0040] The mass-volume ratio of the nano-magnetic particles to the solvent is 0.002~0.02 g / ml;

[0041] The dispersant is sodium dodecylbenzene sulfonate, sodium oleate or sodium hexametaphosphate, the linking agent is water-based acrylic resin or water-based polyurethane, and the surfactant is polyethylene glycol or alkylphenol poly Oxyethylene ether, the wetting agent is ethylene glycol or sorbitol, and the defoaming agent is ...

Example Embodiment

[0042] Example 1

[0043] Calculated by mass percentage, the components are:

[0044] Ethanol: 15.78%, isopropanol: 7.9%, deionized water: 68.35%, nano magnetic particles: 0.6%, dispersant 0.17%; linking agent: 3%; surfactant: 1.15%; wetting agent: 3% ; Defoamer: 0.05%. The mass-volume ratio of nano-magnetic particles to solvent is 0.006 g / ml;

[0045] The dispersing agent is sodium dodecylbenzene sulfonate, the linking agent is an aqueous acrylic resin, the surfactant is polyethylene glycol, the wetting agent is ethylene glycol, and the defoaming agent is Cetyl alcohol.

Example Embodiment

[0046] Example 2

[0047] Calculated by mass percentage, the components are:

[0048] Ethanol: 11.84%, Isopropanol: 12.36%, Deionized water: 66.34%, Nano magnetic particles: 1.81%, Dispersant 0.45%; Linking agent: 3%; Surfactant: 1.15%; Wetting agent: 3% ; Defoamer: 0.05%. The mass-volume ratio of nano-magnetic particles to solvent is 0.02 g / ml;

[0049] The dispersant is sodium oleate, the linking agent is aqueous polyurethane, the surfactant is alkylphenol polyoxyethylene ether, the wetting agent is sorbitol, and the defoaming agent is polyether Modified silicone.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Coercivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses magnetic ink, and relates to an electronic material technology. The magnetic ink comprises a solvent and a solute, wherein the solvent consists of ethanol, isopropanol and deionized water in a volume ratio of A: B: C, wherein A is more than or equal to 1 and less than or equal to 4, B is more than or equal to 1 and less than or equal to 3, and C is more than or equal to 6 and less than or equal to 12; the solute comprises nano magnetic granules, dispersant, connecting agent, surfactant, wetting agent and defoaming agent; the mass ratio of the nano magnetic granules to the dispersant is x: y, wherein x is more than or equal to 4 and less than or equal to 25, and y is more than or equal to 1 and less than or equal to 3; the ratio of the solvent: the connecting agent: the surfactant: the wetting agent: the defoaming agent is a: b: c: d: e, wherein a is more than or equal to 86.95 and less than or equal to 99.199, b is more than or equal to 0.3 and less than or equal to 5, c is more than or equal to 0.5 and less than or equal to 5, d is more than or equal to 0 and less than or equal to 3, and e is more than or equal to 0.001 and less than or equal to 0.05; and the ratio of the mass of the nano magnetic granules to the volume of the solvent is 0.002 to 0.02 gram per milliliter. The method realizes low-cost production of the large-area electromagnetic wave absorption film and preparation of flexible wave absorption films with high output graph precision, clear graph boundary, uniform distribution and various complex components and images.

Description

technical field [0001] The invention belongs to the technical field of electronic materials. Background technique [0002] After entering the information society, human beings use more and more electrical equipment in production and life, and this trend will continue, so the electromagnetic environmental pollution caused by electromagnetic fields in the living environment is also becoming stronger and stronger. Countries all over the world are paying more and more attention to the research of electromagnetic wave shielding and absorbing materials. Many domestic units have devoted themselves to this research and have achieved initial results. At present, the main measures to control electromagnetic wave pollution are: absorbing, filtering, countering and shielding. There are two types of flexible materials for absorbing and shielding electromagnetic waves: absorbing and reflecting. And this kind of flexible composite material that absorbs and reflects electromagnetic waves ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/10C09D11/38
Inventor 韩满贵蔡黎邓龙江
Owner UNIV OF ELECTRONIC SCI & TECH OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap