Multielement composite cathode material for lithium secondary battery and preparation method thereof

A lithium secondary battery and multi-element composite technology, which is applied to battery electrodes, electrical components, circuits, etc., can solve the problems of incomplete reaction, high-temperature gas expansion of ternary positive electrode materials, etc., and achieve improved structural stability, cycle performance and Thermal stability, low inflation effect

Active Publication Date: 2013-11-20
HUNAN SHANSHAN NEW ENERGY CO LTD
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But due to the presence of TiO in the reaction 2 The introduction of TiO 2 It is a relatively active substance, which will cause the decomposition of the electrolyte. If TiO 2 Incomplete reaction with residual 1000ppm lithium carbonate will lead to Li-containing 2 TiO 3 The ternary cathode material has the problem of high temperature gas expansion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multielement composite cathode material for lithium secondary battery and preparation method thereof
  • Multielement composite cathode material for lithium secondary battery and preparation method thereof
  • Multielement composite cathode material for lithium secondary battery and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The lithium secondary battery of the present embodiment is used multi-component composite cathode material, and its chemical formula is Li 1.08 Ni 2 / 5 co 1 / 5 mn 2 / 5 Mg 0.01 o 2 (PO 4 ) 0.0027 , in powder form.

[0021] Its preparation method:

[0022] (1) Weigh Ni 2 / 5 co 1 / 5 mn 2 / 5 (OH) 2 Represented nickel-cobalt-manganese compound (average particle size D50=10.0μm measured by laser particle size analyzer, tap density 2.05g / cm 3 , spherical powder particles) 280.00g, lithium carbonate 122.19g and magnesium carbonate 2.57g, dry mixed, placed in a muffle furnace, and then sintered at 900°C for 10h, cooled, crushed, sieved, and the chemical formula is Li 1.08 Ni 2 / 5 co 1 / 5 mn 2 / 5 Mg 0.01 o 2 represented by Compound A;

[0023] (2) The Li was measured by acid-base titration 1.08 Ni 2 / 5 co 1 / 5 mn 2 / 5 Mg 0.01 o 2 The residual lithium element content of material is 658ppm, weighs 200g above-mentioned synthetic Li 1.08 Ni 2 / 5 co 1 / 5 mn 2 / 5 Mg 0.01 ...

Embodiment 2

[0026] The lithium secondary battery of the present embodiment is used multi-component composite cathode material, and its chemical formula is Li 1.04 Ni 1 / 2 co 1 / 5 mn 3 / 10 Zr 0.01 o 2 (PO 4 ) 0.0017 , in powder form;

[0027] Its preparation method:

[0028] (1) Weigh Ni 1 / 2 co 1 / 5 mn 3 / 10 (OH) 2 Represented nickel-cobalt-manganese compound (average particle size D50=8.0μm measured by laser particle size analyzer, tap density 1.60g / cm 3, powder particle shape similar to spherical) 280.00g, lithium carbonate 116.89g, zirconia 3.74g, dry mixing, placed in a muffle furnace, and then sintered at 850°C for 20h, crushed after cooling, sieved, and the chemical formula is Li 1.04 Ni 1 / 2 co 1 / 5 mn 3 / 10 Zr 0.01 o 2 represented by Compound A;

[0029] (2) The Li was measured by acid-base titration 1.04 Ni 1 / 2 co 1 / 5 mn 3 / 10 Zr 0.01 o 2 The residual lithium element content of the material is 451ppm, weigh 200g of the above-mentioned synthesized Li 1.04 Ni 1 / 2 co...

Embodiment 3

[0032] The lithium secondary battery of the present embodiment is used multi-component composite cathode material, and its chemical formula is Li 1.12 Ni 3 / 5 co 1 / 5 mn 1 / 5 al 0.01 o 2 (PO 4 ) 0.0054 , in powder form.

[0033] Its preparation method:

[0034] (1) Weigh Ni 3 / 5 co 1 / 5 mn 1 / 5 (OH) 2 Represented nickel-cobalt-manganese compound (average particle diameter D50=13.5μm measured by laser particle size analyzer, tap density 2.25g / cm 3 , powder particle shape similar to spherical) 280.00g, lithium carbonate 125.07g and alumina 1.54g, dry mixed, placed in a muffle furnace, then sintered at 750°C for 20h, cooled, crushed, sieved, and the chemical formula is Li 1.12 Ni 3 / 5 co 1 / 5 mn 1 / 5 al 0.01 o 2 represented by Compound A;

[0035] (2) The Li was measured by acid-base titration 1.12 Ni 3 / 5 co 1 / 5 mn 1 / 5 al 0.01 o 2 The residual lithium element content of the material is 1221ppm, weigh 200g of the above-mentioned synthesized Li 1.12 Ni 3 / 5 co 1 / 5 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

A multielement composite cathode material for a lithium secondary battery and a preparation method thereof. The chemical formula of the multielement composite cathode material for a lithium secondary battery is LiaNixCoyMn1-x-yMzO2(PO4)b, wherein M is selected from one or two elements of Mg, Al, Zr, Ba. Sr and B; 0.8<=a<=1.2; 0<x<1; 0<y<1; x+y<=1; 0.0005<=z<=0.02; 0<b<=0.02. The preparation method comprises the following steps: weighing NixCoyMn1-x-y(OH)2, lithium salts or lithium oxide or lithium hydroxide, and compounds containing the element M, mixing, sintering at 700-950 DEG C for 6-24 hours, cooling, crushing, sieving to obtain a compound A expressed as LiaNixCoyMn1-x-yMzO2; testing residual lithium element content of the compound A, adding a phosphorus-containing compound, performing heat treatment at 300-900 DEG C for 2-10 hours, cooling, crushing, and sieving. The multielement composite cathode material for a lithium secondary battery has good cycle performance, and low expansion; a cathode of a lithium secondary battery prepared by the material has good working performance.

Description

technical field [0001] The invention relates to a positive electrode material for a lithium secondary battery and a preparation method thereof, in particular to a multi-component composite positive electrode material for a lithium secondary battery and a preparation method thereof. Background technique [0002] Nickel cobalt lithium manganese oxide is a ternary doped lithium ion battery cathode material, which integrates LiCoO 2 , LiNiO 2 and m -LiMnO 2 The characteristics of the three layered materials, its performance is better than any of the above single-component positive electrode materials, and there is an obvious ternary synergistic effect: by introducing Co, it can reduce the mixed cation occupancy and effectively stabilize the layered structure of the material; The introduction of Ni can increase the capacity of the material; by introducing Mn, not only can the cost of the material be reduced, but also the safety of the material can be improved. The basic physi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/505H01M4/525
CPCY02E60/122Y02E60/10
Inventor 赵艳敏李旭袁荣忠王志兴
Owner HUNAN SHANSHAN NEW ENERGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com