High-nickel multi-element positive electrode material for lithium secondary battery and preparation method thereof

A lithium secondary battery and positive electrode material technology, applied in secondary batteries, battery electrodes, electrical components, etc., can solve problems such as poor processing performance, low initial discharge capacity, and poor high-temperature storage performance, and achieve good cycle performance, Excellent abnormal temperature electrochemical performance, storage performance and good processing performance

Active Publication Date: 2017-09-01
HUNAN SHANSHAN NEW ENERGY CO LTD
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The material obtained by this method has excellent electrochemical performance and storage performance, but poor high-temperature storage performance
[0005] CN201110456525 Chinese patent discloses a Li 3 PO 4 Nickel-based multi-component materials coated with metal oxides have good material safety, but low initial discharge capacity and poor processing performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-nickel multi-element positive electrode material for lithium secondary battery and preparation method thereof
  • High-nickel multi-element positive electrode material for lithium secondary battery and preparation method thereof
  • High-nickel multi-element positive electrode material for lithium secondary battery and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A high-nickel multi-element positive electrode material for a lithium secondary battery of the present invention, comprising a base material and a composite cladding layer outside the base material, the base material being the positive electrode material Li 1.05 Ni 0.8 co 0.1 mn 0.1 o 2 ; The composite coating layer uniformly coated on the outer surface of the substrate is a mixture of lithium zirconium oxide and lithium phosphorus oxide. Lithium zirconium oxide is Li 2 ZrO 3 , Li 6 Zr 2 o 7 and Li 4 ZrO 4 . Lithium phosphorus oxide is Li 3 PO 4 .

[0037] The content of the total impurity lithium on the surface of the high-nickel multi-element positive electrode material surface after the surface modification of the present embodiment is 0.070%, which is 0.32 times that before modification, and the Li in the total impurity lithium 2 CO 3 and LiOH content are 0.195% and 0.115%, respectively.

[0038] The preparation method of the high-nickel multi-elemen...

Embodiment 2

[0074] A high-nickel multi-component positive electrode material for a lithium secondary battery of the present invention, comprising a base material and a composite coating layer outside the base material, the base material being a binary positive electrode material Li 1.07 Ni 0.815 co 0.15 al 0.035 o 2 The composite coating layer uniformly coated on the outer surface of the substrate is a mixture of lithium zirconium oxide, lithium titanium oxide, lithium aluminum oxide and lithium phosphorus oxide. Lithium zirconium oxide is Li 2 ZrO 3 , lithium titanium oxide is Li 2 TiO 3 , lithium aluminum oxide is LiAlO 2 , the lithium phosphorus oxide is Li 3 PO 4 .

[0075] The content of the total impurity lithium on the surface of the high-nickel multi-element positive electrode material surface after the surface modification of this embodiment is 0.072%, which is 0.21 times that before modification, and the content of the total impurity lithium is the remaining Li on the ...

Embodiment 3

[0082] A high-nickel multi-component positive electrode material for a lithium secondary battery of the present invention, comprising a base material and a composite coating layer outside the base material, the base material being a binary positive electrode material Li 1.04 Ni 0.8 co 0.2 o 2 ; The composite coating layer uniformly coated on the outer surface of the substrate is a mixture of lithium zirconium oxide, lithium aluminum oxide and lithium phosphorus oxide. Lithium zirconium oxide is Li 2 ZrO 3 , lithium aluminum oxide is LiAlO 2 , the lithium phosphorus oxide is Li 3 PO 4 and Li 4 P 2 o 7 .

[0083] The content of the total impurity lithium on the surface of the high-nickel multi-element positive electrode material surface after the surface modification of this embodiment is 0.059%, which is 0.32 times that before modification, and the content of the total impurity lithium is the remaining Li on the surface of the substrate. 2 CO 3 and lithium element c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

A high-nickel multi-element positive electrode material for a lithium secondary battery comprises a base material and a composite cladding layer outside the base material, the general formula of the base material is LiaNi1-x-yCoxMyO2, wherein M is at least one of Mn and Al, a, x and y respectively represent the molar ratios of Li, Co and M in the base material, a is not smaller than 1 and not greater than 1.2, 1-x-y is not smaller than 0.6 and not greater than 1, x is greater than 0 and not greater than 0.4, and y is not smaller than 0 and not greater than 0.4; and the composite cladding layer is a mixture containing lithium phosphorus oxide and at least one of lithium zirconium / lithium titanium / lithium aluminum oxides. A preparation method of the positive electrode material comprises the following steps: preparing the base material; adding a metallic Zr / Ti / Al-containing compound, and carrying out high temperature heat treatment to obtain a lithium zirconium / lithium titanium / lithium aluminum oxide coated base layer; and adding phosphate, and carrying out low temperature heat treatment to obtain the high-nickel multi-element positive electrode material for the lithium secondary battery. The high-nickel multi-element positive electrode material has the advantages of low alkalinity, small gas swelling degree, good processability and good electrochemical performances.

Description

technical field [0001] The invention relates to a positive electrode material for a lithium battery and a preparation method thereof, in particular to a high-nickel positive electrode material for a lithium secondary battery and a preparation method thereof. Background technique [0002] The rapid development of science and technology has increased people's demand for mobile power. Compared with traditional secondary batteries, lithium-ion secondary batteries have the advantages of high voltage, small size, high energy density, long service life, low self-discharge, wide operating temperature range, short charge and discharge time, no environmental pollution, and no memory effect It has been widely used in modern digital products such as mobile phones and notebook computers, and large-capacity lithium-ion batteries have also begun to be used in electric vehicles. In lithium-ion batteries, the performance of the positive electrode material determines the performance of the e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/485H01M4/505H01M4/525H01M10/0525
CPCH01M4/485H01M4/505H01M4/525H01M10/0525Y02E60/10
Inventor 周惠李旭蒋湘康谭欣欣王志兴彭文杰袁荣忠李智华
Owner HUNAN SHANSHAN NEW ENERGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com