Method for preparing titanium sesquioxide material

A technology for titanium dioxide and titanium dioxide, which is applied in the field of preparing titanium dioxide materials, can solve problems such as complicated processes, and achieve the effects of simplifying the preparation process, reducing environmental damage, and widening social and environmental benefits.

Inactive Publication Date: 2012-06-13
GUIZHOU BRANCH CHINA ALUMINUM IND
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These methods, the process is complicated, and contain the volatile substance titanium tetrachloride

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Use titanium dioxide, graphite powder, and titanium carbide as materials, weigh 500 grams of titanium dioxide powder, weigh 100 grams of graphite powder (according to the mass ratio of 5:1), and add 30 grams (mass ratio of 5%) of titanium carbide at the same time, and mix them thoroughly through a ball mill Finally, it was pressed into a billet with a press, and then sintered at 1200°C for 4 hours under a vacuum condition of 10 Pa to successfully prepare dititanium trioxide.

Embodiment 2

[0015] Use titanium dioxide, graphite powder, and titanium carbide as materials, weigh 500 grams of titanium dioxide powder, weigh 200 grams of graphite powder (according to the mass ratio of 5:2), and add 7 grams (mass ratio of 1%) of titanium carbide at the same time, and mix them thoroughly through a ball mill Finally, it was pressed into a billet with a press, and then sintered at 1600 ° C for 2 hours under an argon atmosphere to successfully prepare dititanium trioxide.

Embodiment 3

[0017] Use titanium dioxide, graphite powder, and titanium carbide as materials, weigh 500 grams of titanium dioxide powder, weigh 300 grams of graphite powder (according to the mass ratio of 5:3), and add 0.8 grams (mass ratio of 0.1%) of titanium carbide at the same time, and mix them thoroughly through a ball mill Finally, it was pressed into a billet with a press, and then sintered at 1980 ° C for 18 hours under an argon atmosphere to successfully prepare dititanium trioxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing a titanium sesquioxide material. The method is characterized in that a preparation process uses titanium dioxide and graphite as basic raw materials and carries out the preparation by a hot reduction reaction. The method for preparing the titanium sesquioxide material of the invention uses titanium dioxide and graphite as basic raw materials and carries out the preparation by a high temperature thermal reduction method. The titanium sesquioxide is prepared directly by a one-step carbothermic process, so as to save technological steps and reduce usage of a restorable harmful substance titanium tetrachloride. Therefore, the method reduces cost as well as mitigates environmental pollution.

Description

technical field [0001] The invention relates to a method for preparing dititanium oxide material. Background technique [0002] Titanium-doped sapphire (Ti:Al 2 o 3 ) is the basic raw material for the manufacture of solid-state tunable lasers. It can form very short pulses, and the noise is only one-tenth of that of tunable dye lasers. It has a wide range of applications in remote sensing measurement, lidar, and submarine communications. And titanium-doped sapphire (Ti:Al 2 o 3 ) The basic raw material required for the preparation is reducing titanium dioxide. At present, the method for preparing titanium dioxide is mainly to directly reduce titanium dioxide with hydrogen in the presence of titanium tetrachloride to prepare titanium dioxide. These methods are complicated in process and contain titanium tetrachloride, a volatile substance. Contents of the invention [0003] The purpose of the present invention is to address the deficiencies of the prior art, to provid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01G23/04
Inventor 秦庆东王芳平邱仕麟杨建红柴登鹏李旺兴
Owner GUIZHOU BRANCH CHINA ALUMINUM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products