Low-cost, low-density and high-CaO corundum castable and preparation method thereof

A technology for corundum-based castables, applied in the field of low-cost, low-density, high-CaO corundum-based castables and its preparation, can solve the problems of restricting large-scale promotion and application, energy waste, unfavorable energy saving, etc., and achieve volume stability and cost reduction , the effect of heat loss reduction

Inactive Publication Date: 2012-06-20
SINOSTEEL LUOYANG INST OF REFRACTORIES RES
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 2. When the corundum castable is not eroded by slag and other media, the existing high-purity corundum castable is not conducive to energy saving due to its high density and high thermal conductivity, and it is easy to cause energy waste
[0006] 3. High-purity corundum castables

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Example 1: Raw material components and proportions (percentage by weight) are 78% of fused white corundum granular aggregate, 5% of fused white corundum fine powder, 4% of industrial alumina powder, 8% of activated alumina micropowder, pure aluminum Calcium acid cement 5%; the addition of water reducing agent is 0.05% of the total weight of raw materials.

Embodiment 2

[0029] Example 2: Raw material components and ratio (percentage by weight) are 55% of sintered tabular corundum granular aggregate, 10% of sintered tabular corundum fine powder, 16% of industrial alumina powder, 4% of activated alumina micropowder, pure aluminum Calcium acid cement 15%; the addition of water reducing agent is 0.20% of the total weight of raw materials.

Embodiment 3

[0030] Example 3: Raw material components and ratio (percentage by weight) are 25% of sintered tabular corundum granular aggregate, 40% of fused white corundum particles, 9% of fused white corundum fine powder, 4% of industrial alumina powder, active 12% of alumina micropowder, 10% of pure calcium aluminate cement; the addition of water reducing agent is 0.30% of the total weight of raw materials.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a low-cost, low-density and high-CaO corundum castable and a preparation method thereof. The low-cost, low-density and high-CaO corundum castable is prepared by adding industrial alumina powder on the basis of the conventional common corundum castable. Volume expansion caused by calcium hexaluminate generated in the corundum castable is compensated by using volume contraction caused by phase change of industrial alumina at a high temperature, so that the contradiction between the adding amount of cement and the volume stability of the castable is solved successfully. The invented castable has low volume density and low thermal conductivity coefficient, energy loss caused by the application of the castable to a high-temperature kiln can be reduced, and the aim of saving energy is fulfilled. The industrial alumina powder is added, so that the cost of the castable is reduced in a certain degree, and the competitive advantage of the castable is enhanced. The corundum castable prepared with the method can be widely applied in the high-temperature industrial fields of steel and iron, non-ferrous metals, ceramics, petrifaction, and the like.

Description

technical field [0001] The invention belongs to the technical field of inorganic non-metallic materials. In particular, it relates to a low-cost, low-density, high-CaO corundum castable and a preparation method thereof. Background technique [0002] Compared with shaped refractory products, unshaped refractory materials have developed rapidly in all countries in the world because of their advantages in production, labor productivity, construction efficiency, material consumption, and energy saving. Castables, one of the main varieties of unshaped refractory materials, are increasingly used in high-temperature parts instead of shaped products. The high-purity corundum castable is made of corundum as the main crystal phase, combined with calcium aluminate cement and alumina micropowder, and its composition is Al 2 o 3 -CaO binary system, the temperature of the liquid phase is as high as 1900 ℃. During the first heat treatment or use, as the temperature rises, the CaO in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/66C04B35/101
Inventor 李志刚张振燕李红霞禄向阳
Owner SINOSTEEL LUOYANG INST OF REFRACTORIES RES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap