Hormone hydrogel rooting film

A hydrogel and hormone technology, applied in the directions of biocides, plant growth regulators, plant growth regulators, etc., can solve the problems of unsatisfactory production effect, many technical steps, difficult to master, etc., and achieves saving seedling input and seedling survival. High rate and the effect of reducing water loss

Inactive Publication Date: 2013-11-20
濮阳市林业科学院
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Comprehensive use of the above technical measures, although the rooting survival rate of cuttings has been improved, but there are many technical steps, difficult to master, unstable, high cost and other shortcomings, the production effect is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The hormone hydrogel rooting film of the present invention is prepared according to the following raw material ratio and steps:

[0016] a, the weight ratio of raw materials:

[0017] Water: 800; polyvinyl alcohol: 60; concentration of 2.5% glycerin: 30; hormone: 0.08;

[0018] The hormone is prepared by mixing indolebutyric acid potassium salt, naphthalene acetic acid sodium salt, and diethyl hexanoate according to a weight ratio of 10:50:3;

[0019] b. Preparation steps:

[0020] Step 1: Put water in the container, add polyvinyl alcohol to swell for 30 minutes, place the container in a water bath, heat up to 80°C, and completely dissolve the polyvinyl alcohol into a transparent liquid; then cool down to 60°C, use Concentrated hydrochloric acid adjusts the pH value of the solution to 1;

[0021] In the second step, add glycerol with a concentration of 2.5% to the solution obtained in the first step to react for 50 minutes, and cool down to 30° C. to obtain a hydroge...

Embodiment 2

[0024] The hormone hydrogel rooting film of the present invention is prepared according to the following raw material ratio and steps:

[0025] a, the weight ratio of raw materials:

[0026] Water: 1000; polyvinyl alcohol: 70; concentration of 2.5% glycerin: 35; hormone: 0.1;

[0027] The hormone is prepared by mixing indolebutyric acid potassium salt, naphthalene acetic acid sodium salt, and diethyl hexanoate according to a weight ratio of 10:50:3;

[0028] b. Preparation steps:

[0029] Step 1: Put water in the container, add polyvinyl alcohol to swell for 30 minutes, place the container in a water bath, heat up to 85°C, and completely dissolve the polyvinyl alcohol into a transparent liquid; then cool down to 60°C, use Concentrated hydrochloric acid adjusts the pH value of the solution to 1.5;

[0030] In the second step, add glycerol with a concentration of 2.5% to the solution obtained in the first step to react for 60 minutes, and cool down to 35° C. to obtain a hydro...

Embodiment 3

[0033] The hormone hydrogel rooting film of the present invention is prepared according to the following raw material ratio and steps:

[0034] a, the weight ratio of raw materials:

[0035] Water: 1200; polyvinyl alcohol: 90; concentration of 2.5% glycerol: 45; hormone: 0.2;

[0036] The hormone is prepared by mixing indolebutyric acid potassium salt, naphthalene acetic acid sodium salt, and diethyl hexanoate according to a weight ratio of 10:50:3;

[0037] b. Preparation steps:

[0038] Step 1: Put water in the container, add polyvinyl alcohol to swell for 30 minutes, place the container in a water bath, heat up to 90°C, and completely dissolve the polyvinyl alcohol into a transparent liquid; then cool down to 60°C, use Concentrated hydrochloric acid adjusts the pH value of the solution to 2;

[0039] In the second step, add glycerol with a concentration of 2.5% to the solution obtained in the first step to react for 70 minutes, and cool down to 40° C. to obtain a hydroge...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a hormone hydrogel rooting film, which is prepared by the steps of: swelling polyvinyl alcohol at normal temperature for 30min, and heating for completely dissolving polyvinyl alcohol to obtain a transparent liquid; cooling, adjusting the pH value of the solution with concentrated hydrochloric acid, adding glycerol and reacting to prepare a hydrogel liquid; and adding hormone to the hydrogel liquid and stirring. When in use, the hormone hydrogel rooting film is spread on the surface of a hard branch cutting shoot, so that a gel film is formed on the surface of the hard branch cutting shoot above the ground so as to achieve the purpose of reducing the moisture of the cutting shoot from dissipation, and a gel film is formed on the surface of the hard branch cutting shoot under the ground so as to keep a moisture state in soil and play a role of slowly releasing hormone to stimulate the rooting of the cutting shoot, thus the rooting critical stage of the hard branch cutting shoot is prolonged and the rooting survival rate of the hard branch cutting shoot is improved. The technical scheme disclosed by the invention is simple and convenient, high in raising seedling survival rate and significant in economic and social benefits, and saves seedling-raising investment by more than 10%.

Description

technical field [0001] The invention relates to the field of tree hard branch cutting and seedling cultivation, in particular to a hormone hydrogel rooting film. Background technique [0002] Hard branch cutting is one of the commonly used methods for asexual propagation of trees. It has the advantages of low production cost, fast propagation speed, abundant branch sources, and the ability to maintain the excellent traits of the female parent. Some tree species that are easier to take root, such as European and American poplars, willows, etc., have been a conventional and mature technology for hard branch cutting seedlings. But some tree species that are difficult to take root such as ginkgo, eucalyptus, poplar tomentosa, jujube etc., the technical problem of adopting hard branch cuttings to directly cut seedlings under field conditions has not been better resolved. Due to the lack of ready-made root primitives in the branches of difficult-to-root trees, the callus tissue a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A01N43/38A01N37/12A01N37/10A01N25/04A01P21/00A01G1/00
Inventor 杨合廷王淑利李洁茹魏红任冬焕张溃珍李应华杨玉巧李传省唐丽英苏衍修王少敏杨利花王晓军黄秋萍谢守江吉洪坤屈朝彬杨旭琦张杜娟崔迷俭李舒梅赵若冰
Owner 濮阳市林业科学院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap