UV (ultraviolet) cured high-rigidity wear-resistant flame-retardant coating material and preparation method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A flame retardant coating, high hardness technology, applied in the field of UV curing coating materials, can solve the problems of poor mechanical properties of coatings, high cost, complex synthesis process, etc.
Inactive Publication Date: 2012-07-25
SHANGHAI UNIV
View PDF7 Cites 20 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, its disadvantage is that the synthesis process of phosphorus and nitrogen-containing acrylic resin
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0030] Embodiment 1 (the following are all in parts by mass), the components of functional sol and the proportioning ratio thereof are:
[0031] Composition Mass percentage content wt%
[0032] Ethyl Tetrasilicate 30%
[0033] Trimethyl borate 0%
[0034] Trimethyl phosphite 20%
[0035] Gamma-Methacryloxytrimethoxysilane 45%
[0036] Deionized water 5%
[0037] Acetic acid 0.5%
Embodiment 2
[0038] Embodiment 2 (below all in mass percentage), the component of functional sol and proportioning thereof are:
[0039] Composition Mass percentage content wt%
[0040] Ethyl Tetrasilicate 30%
[0041] Trimethyl borate 15%
[0042]Trimethyl phosphite 15%
[0043] Gamma-methacryloxytrimethoxysilane 35%
[0044] Deionized water 5%
[0045] Acetic acid 0.5%
Embodiment 3
[0046] Embodiment 3 (below all in mass percentage), the component of functional sol and proportioning thereof are:
[0047] Composition Mass percentage content wt%
[0048] Ethyl Tetrasilicate 20%
[0049] Trimethyl borate 15%
[0050] Trimethyl phosphite 15%
[0051] Gamma-Methacryloxytrimethoxysilane 45%
[0052] Deionized water 5%
[0053] Acetic acid 0.5%
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a UV (ultraviolet) cured high-rigidity wear-resistant flame-retardant coating material and a preparation method thereof. The UV cured high-rigidity wear-resistant flame-retardant coating material comprises components including, by weight, 20-70% of UV curing resin, 20-50% of active diluent, 5-40% of functional sol, 3-5% of initiator and 0.1-0.6% of flatting agent, wherein the functional sol is sol containing flame-retardant element prepared by sol-gel method, functional filler is at least one of organically-modified talcum powder and montmorillonoid and particles with evident diameter gradient. Rigidity, wear resistance and flame retardant of the coating material can be improved greatly after the coating material is coated on base material. The UV cured high-rigidity wear-resistant flame-retardant coating material can be applied to the surfaces of furniture, wood floor and plastics.
Description
technical field [0001] The invention relates to a UV curable coating material, in particular to a bright or matte UV curable high-hardness wear-resistant flame-retardant coating material. Background technique [0002] Since the 21st century, with the improvement of the per capita living standard in our country, people generally attach importance to the quality of life and decorate the home environment more and more. As some flammable decorative materials such as wood, fiber, plastic and rubber enter the home environment in large quantities, the problem of their flame retardancy and fire resistance has become increasingly prominent. While enjoying the comfort and comfort of the family, people gradually realize the importance and urgency of fire safety in the home environment, which puts forward higher requirements for the safety performance of building decoration materials. At the same time, with the rapid development of my country's economy and the substantial improvement o...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more