Red translucent crystal glue material and manufacturing method thereof

A translucent and crystal glue technology, applied in the field of crystal glue materials, can solve the problems of short service life, easy oxidation and discoloration, poor transparency, etc.

Inactive Publication Date: 2012-08-15
浙江银太郎动漫文化股份有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is mainly divided into two types: colored translucent and colorless and transparent. The existing colored translucent crystal glue materials are mainly composed of PVA, water, borax and pigments. Cracking, poor transparency and easy to oxidize and discolor, short service life
Especially the red translucent crystal glue material with red industrial pigment added, the service life is only 6-10 months

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Red translucent crystal glue material and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A red translucent crystal glue material, made of the following components by weight percentage:

[0046] PVA powder: 25%;

[0047] Water: 57.6%;

[0048] Borax: 0.7%;

[0049] Carboresin: 5%;

[0050] Propylene glycol: 8%;

[0051] Vanillin: 0.01%;

[0052] Clove oil: 0.02%;

[0053] Amyl acetate: 0.02%;

[0054] Carmine: 0.07%;

[0055] Tartaric acid: 0.03%;

[0056] Sorbic acid: 0.05%;

[0057] Sodium dodecylbenzenesulfonate: 0.5%;

[0058] Acrylamide-acrylate copolymer cross-linked product: 3%;

[0059] The acrylamide-acrylate copolymerized cross-linked product is composed of 55% of acrylamide, 34% of potassium acrylate, 10% of water and 1% of N,N-methylenebisacrylamide.

[0060] Acrylamide-acrylate copolymerized cross-linked product is a water-retaining agent. Its preparation method is: add acrylamide to acrylic acid aqueous solution, stir at room temperature, then add N,N-methylenebisacrylamide (NNMBA), heat up To 35°C and keep the temperature constant ...

Embodiment 2

[0069] A red translucent crystal glue material made of the following components by weight percentage:

[0070] PVA powder: 28%;

[0071] Water: 54.54%;

[0072] Borax: 0.9%;

[0073] Carboresin: 8%;

[0074] Propylene glycol: 6%;

[0075] Vanillin: 0.02%;

[0076] Clove oil: 0.01%;

[0077] Amyl acetate: 0.02%;

[0078] Carmine: 0.05%;

[0079] Tartaric acid: 0.02%;

[0080] Sorbic acid: 0.04%;

[0081] Sodium dodecylbenzenesulfonate: 0.4%;

[0082] Acrylamide-acrylate copolymer cross-linked product: 2%;

[0083] The acrylamide-acrylic acid salt copolymerized cross-linked product is composed of 56% of acrylamide, 34% of potassium acrylate, 9.5% of water and 0.5% of N,N-methylenebisacrylamide accounting for its total weight.

[0084] The preparation method of the acrylamide-acrylate copolymerized cross-linked product and the preparation method of the above-mentioned red translucent crystal glue material are the same as in Example 1.

Embodiment 3

[0086] A red translucent crystal glue material made of the following components by weight percentage:

[0087] PVA powder: 20%;

[0088] Water: 58.85%;

[0089] Borax: 0.6%;

[0090] Carboresin: 7%;

[0091] Glycerin: 9%;

[0092] Vanillin: 0.01%;

[0093] Clove oil: 0.03%;

[0094] Amyl acetate: 0.01%;

[0095] Carmine: 0.05%;

[0096] Tartaric acid: 0.04%;

[0097] Sorbic acid: 0.01%;

[0098] Sodium dodecylbenzenesulfonate: 0.4%;

[0099] Acrylamide-acrylate copolymer cross-linked product: 4%;

[0100] The acrylamide-acrylate copolymerized cross-linked product is composed of 56% of acrylamide, 33% of potassium acrylate, 10% of water and 1% of N,N-methylenebisacrylamide.

[0101] The preparation method of the acrylamide-acrylate copolymerized cross-linked product and the preparation method of the above-mentioned red translucent crystal glue material are the same as in Example 1.

[0102] The following is a partial performance comparison table between the existing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a red translucent crystal glue material and a manufacturing method of the red translucent crystal glue material. The red translucent crystal glue material is manufactured by a way that PVA (polyvinyl acetate) powder, water, sodium borate, carbomer resin, propylene glycol or glycerol, vanillin, clove oil, amyl acetate, carmine, tartaric acid, sorbic acid, sodium dodecyl benzene sulfonate and an acrylamide-acrylate copolymerized crosslinked material are sequentially mixed, emulsified and stirred, and finally sodium borate water is added in the mixed solution for solidification. The translucent crystal glue material has the advantages of good moisturizing effect, bright color, stable color, high transparency and long service life, and is unlikely to crack in the air and unlikely to discolor. The transparency of the red translucent crystal glue material provided by the invention is up to above 50%, and the service life is up to above 18 months.

Description

technical field [0001] The invention relates to a crystal glue material and a preparation method of the crystal glue material. Background technique [0002] Crystal glue materials are mainly used to prepare interior decoration pieces, decoration pieces, some stylistic utensils and soft elastic toys. It is mainly divided into two types: colored translucent and colorless and transparent. The existing colored translucent crystal glue materials are mainly composed of PVA, water, borax and pigments. Cracking, poor transparency and easy oxidative discoloration, short service life. Especially the red translucent crystal glue material added with red industrial pigment has a service life of only 6 to 10 months. Contents of the invention [0003] The purpose of the present invention is to provide a red translucent crystal glue material with good moisturizing effect, not easy to crack when placed in the air, stable color, good transparency and long service life. [0004] Another o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L29/04C08L33/26C08K13/02C08K3/38C08K5/053C08K5/13C08K5/101C08K5/092C08K5/09C08K5/42
Inventor 杜京财
Owner 浙江银太郎动漫文化股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More