Antibacterial ABS (acrylonitrile butadiene styrene) plastic and preparation method thereof

An ABS plastic and raw material technology, applied in the field of antibacterial ABS plastic and its preparation, can solve the problems that the antibacterial properties of antibacterial plastic products cannot be fully exerted, the antibacterial purpose cannot be achieved, the antibacterial agent is easily inactivated, and the like, and can achieve good gloss, Long-lasting antibacterial effect, easy-to-produce effect

Inactive Publication Date: 2014-03-05
CHANGAN UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since this method is carried out at room temperature and is obtained by conventional methods, the antibacterial properties of the prepared antibacterial plastic products cannot be fully exerted. At the same time, with the release of the antibacterial agent, the antibacterial activity is getting smaller and smaller, and the antibacterial agent is easily inactivated. , fail to achieve the purpose of antibacterial

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial ABS (acrylonitrile butadiene styrene) plastic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The antibacterial ABS plastic of this embodiment is made of the following raw materials in percentage by weight: ABS plastic master batch 98.5%, acrylonitrile 1%, nano-silver 0.05%, dispersant 0.03%, antioxidant 0.42%; Described ABS plastic master batch is ABS HI100Y of LG Chemical Company; the mass purity of the acrylonitrile ≥ 98%; the average particle diameter of the nano-silver is 5nm; the dispersant is zeolite, and the antioxidant is antioxidant JX-168; The dispersant can also be silica, bentonite, sepiolite or diatomaceous earth, and the antioxidant can also be antioxidant MD-1024, antioxidant JX-1076 or antioxidant 702.

[0022] The preparation method of the antibacterial ABS plastic of the present embodiment may further comprise the steps:

[0023] Step 1, adding acrylonitrile, nano-silver and dispersant to the agitator by weight percentage, stirring at a speed of 40 revolutions per minute for 30 minutes to obtain mixed auxiliary materials;

[0024] Step 2. Aft...

Embodiment 2

[0028] The present embodiment is the same as Embodiment 1, and the difference is that antibacterial ABS plastic is made of the following raw materials by weight percentage: ABS plastic masterbatch 94.5%, acrylonitrile 5%, nano silver 0.001%, dispersant 0.002%, antibacterial Oxidant 0.497%; The ABS plastic master batch is ABS HI100Y of LG Chemical Company; The mass purity of the acrylonitrile is more than or equal to 98%; The average particle diameter of the nano-silver is 20nm; The dispersant is silica, and the antioxidant is Antioxidant JX-168; The dispersant described in this embodiment can also be zeolite, bentonite, sepiolite or diatomaceous earth, and antioxidant can also be antioxidant MD-1024, antioxidant JX-1076 or antioxidant Agent 702.

Embodiment 3

[0030] This embodiment is the same as Example 1, except that the antibacterial ABS plastic is made of the following raw materials in weight percentage: ABS plastic masterbatch 95.91%, acrylonitrile 3.6%, nano silver 0.04%, dispersant 0.05%, antibacterial Oxidant 0.4%; The ABS plastic masterbatch is ABS HI100Y of LG Chemical Company; The mass purity of the acrylonitrile ≥ 98%; The average particle diameter of the nano-silver is 30nm; The dispersant is bentonite, and the antioxidant is Antioxidant JX-168; The dispersant described in this embodiment can also be zeolite, silica, sepiolite or diatomaceous earth, and antioxidant can also be antioxidant MD-1024, antioxidant JX-1076 or antioxidant Agent 702.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antibacterial ABS (acrylonitrile butadiene styrene) plastic, which is prepared from the following raw materials in percentage by weight: 94.5 to 98.5 percent of ABS plastic masterbatch, 1.0 to 5.0 percent of acrylonitrile, 0.001 to 0.05 percent of nano-silver, 0.002 to 0.05 percent of dispersant, and 0.1 to 0.5 percent of antioxidant. The invention also discloses a preparation method of the antibacterial ABS plastic, which comprises the following steps of: uniformly mixing the acrylonitrile, the nano-silver and the dispersant to obtain a mixed auxiliary material; heating, stirring and mixing the mixed auxiliary material, the ABS plastic masterbatch, the antioxidant and an organic solvent in a stainless steel stirrer to obtain a mixed raw material; and extruding and granulating the mixed raw material to obtain the antibacterial ABS plastic. The preparation method has a simple process; and the prepared antibacterial plastic has strong bacteria resistance, and a lasting antibacterial effect.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to an antibacterial ABS plastic and a preparation method thereof. Background technique [0002] At present, plastic products play a very important role in people's daily life and industrial and agricultural production. With the wide popularization and application of plastic products in the field of daily necessities, people frequently come into contact with and use plastic products, thus the requirements for plastic products are getting higher and higher. People often add some nanoscale silver, copper, zinc and other ions with bactericidal and antibacterial functions to plastic products to endow plastics with antibacterial functions. At present, antibacterial plastics have received widespread attention. [0003] The surface gloss of acrylonitrile-butadiene-styrene copolymer (ABS) material is good, and the casing of most electrical appliances is prepared by it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L55/02C08K13/02C08K5/315C08K3/08C08K3/34
Inventor 费晓华杨胜科赵钺陈静
Owner CHANGAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com