Lead-free silver and aluminum slurry for solar photocell and preparation method of slurry

A technology of photovoltaic cells and solar energy, applied in conductive materials dispersed in non-conductive inorganic materials, cable/conductor manufacturing, circuits, etc., can solve the problems of lead in inorganic glass powder, environmental pollution, etc. Ohmic contact, the effect of improving photoelectric conversion efficiency

Active Publication Date: 2012-10-03
JIANGSU RUIDE NEW ENERGY TECH
View PDF6 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The inorganic glass powder used in the known solar silicon photocell aluminum electronic pas...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A lead-free silver-aluminum paste for solar photovoltaic cells, characterized in that the paste is made of 80% silver powder, aluminum powder and copper powder, 15% organic binder, 2% inorganic glass powder, 3% The composition of additives, the total mass is 100%; the purity of the silver powder, aluminum powder and copper powder is ≥99.9%, the average particle size is 3 μm, and the spherical silver powder, aluminum powder and copper powder are covered with a nitride protective layer on the surface; Described organic binder is made up of 0.5% butyl carbitol, 1.5% resin, 1% rosin, 11% diethylene glycol methyl ether, 6% diethylene glycol butyl ether, 65% by mass percent % cyclohexanone and 15% n-butanol, the total mass is 100%; the inorganic glass powder is 3% titanium dioxide by mass percentage, 70% boric acid, 5% aluminum oxide, 20% oxide Antimony is composed of 2% zirconia, and the total mass is 100%; the additive is composed of 45% Span by mass percentage, and 55% pum...

Embodiment 2

[0044] The invention is a lead-free silver-aluminum paste for solar photovoltaic cells. The paste is composed of 75% silver powder, aluminum powder and copper powder, 18% organic binder, 5% inorganic glass powder, 2% The composition of additives, the total mass is 100%; the purity of the silver powder, aluminum powder and copper powder is ≥99.9%, the average particle size is 3 μm, and the surface is covered with a nitride protective layer. Spherical and / or flake-shaped silver powder, aluminum powder and copper powder; the organic binder consists of 1% butyl carbitol, 2% resin, 3% rosin, 11% diethylene glycol methyl ether, 9% diethylene glycol by mass percentage Alcohol butyl ether, 60% cyclohexanone and 14% n-butanol are composed of 100% total mass; the inorganic glass powder is 1% titanium dioxide by mass percentage, 75% boric acid, 3% aluminum oxide , 19% of antimony oxide, 2% of zirconia, the total mass is 100%; the additive is composed of 35% of Siban by mass percentage, 6...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Finenessaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses lead-free silver and aluminum slurry for a solar photocell. The slurry is prepared from raw materials in percent by mass as follows: 75-80% of silver powder, aluminum powder and copper powder, 15-20% of organic bond, 1-5% of inorganic glass powder, and 1-5% of additive; the purities of the silver powder, the aluminum powder and the copper powder are more than or equal to 99.9%; the organic bond is prepared from the following materials in percent by mass of: 0.5-2% of butyl carbitol, 1-2.5% of resin, 1-4% of rosin, 11-13% of ethylene glycol monomethyl ether, 5-9% of diethylene glycol monobutyl ether, 65-75% of cyclohexanone and 10-20% of n-butyl alcohol; the inorganic glass powder is prepared from the following materials in percent by mass of: 1-3% of titanium dioxide, 55-75% of boric acid, 3-5% of aluminium sesquioxide, 15-25% of antimony oxide and 2-5% of zirconium oxide; and the additive is prepared from the following materials in percent by mass of: 35-45% of span and 55-65% of pump oil. The lead-free silver and aluminum slurry prepared by the raw material has the advantages of good weldability and strong adhesion and meets the lead-free environmental friendless requirement.

Description

technical field [0001] The invention relates to an electronic paste for solar silicon cells, in particular to a lead-free silver-aluminum paste for solar photovoltaic cells and a preparation method thereof. Background technique [0002] Solar energy is an inexhaustible, pollution-free, noise-free new energy source. Solar cells are green and environmentally friendly renewable energy semiconductor devices that directly convert solar energy into electrical energy. The preparation of its electronic paste is mostly made of silver paste, silver-aluminum paste, and aluminum paste. Aluminum paste has cheap price and stable electrical performance. Aluminum and silicon are easy to form PN junctions, have long-wave response characteristics, have good ohmic contact characteristics with silicon wafers or ceramic substrates, and have good aging resistance. Therefore aluminum electronic paste is selected as the material for the back field of silicon solar cells. [0003] In order to re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01B1/22H01B13/00
Inventor 戈士勇
Owner JIANGSU RUIDE NEW ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap