Raw material ball calcinations method of self-thermal-insulating ceramsite external wall panel
A raw material ball and self-insulation technology, which is applied in the direction of heat preservation, ceramic products, building components, etc., to achieve the effect of good fire resistance
Active Publication Date: 2014-03-05
JIANGXI THE FIRST CONSTR ENG CORP
View PDF3 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] And, especially in the event of an open flame, the existing self-insulating siding contains a large amount of organic materials, which can cause serious accidents
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0034] The present invention will be described in further detail below, so that those skilled in the art can implement it with reference to the description.
[0035] The invention provides a method for manufacturing ceramsite self-insulating exterior wall panels, comprising the following steps:
[0036] 1) Stone crushing
[0037] Crushing the leftovers of natural stone with a pulverizer, and sifting out stone powder with a particle size not greater than 50 mesh through a powder vibrating sieve;
[0038] 2) Crushing of cast iron slag
[0039] Pulverize the cast iron slag with a pulverizer, and sieve out the slag powder with a particle size not greater than 80 mesh through a powder vibrating sieve;
[0040] 3) Straw crushing
[0041] The straw is crushed with a pulverizer so that the fiber length does not exceed 2.5 mm;
[0042] 4) Mix water-based stone slurry with a water mass content between 88-90% and the above-mentioned stone powder, slag powder and straw powder accordin...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| diameter | aaaaa | aaaaa |
| particle size | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses a manufacture method of a self-thermal-insulating ceramisite external wall panel. The method includes steps of firstly, fragmenting building stones; secondly, fragmenting cast iron slag; thirdly fragmenting straws; fourthly, mixing waterborne stone slurry containing 88-90% of water with the stone powder, the slag powder and the straw powder, and adding the mixture into a slurrying machine for slurrying; fifthly, dehydrating the mixed slurry through a dehydrator, and drying through a dryer at a temperature of 40-50 DEG C; sixthly, pressing the material obtained in the fifth step into raw meal nodules through a press; seventhly, cooling and drying the raw meal nodules; eighthly, placing the raw meal nodules into a ceramic roaster; ninthly, heating the ceramic roaster to a temperature of 900-950 DEG C; tenthly, mixing cement, sands, intensifier, foaming agent, binder and ceramsite under normal temperature according to proportion; and eleventhly, adding mixed water material into a mould, paving a reinforcing screen on surface, and pressing and forming at a pressure of 400-450N to obtain the self-thermal-insulating external wall panel. The self-thermal-insulating ceramisite external wall panel manufactured by the method is attractive in appearance and economical in process.
Description
technical field [0001] The invention relates to a method for manufacturing a self-insulating exterior wall panel, in particular to a method for making a self-insulating exterior wall panel using ceramsite made from waste materials. Background technique [0002] The common self-insulating exterior wall panels are all fixed on the exterior surface of the wall after the construction of the insulation wall is completed. Therefore, it is required that the outer surface of this self-insulating exterior wall panel is more beautiful, and these materials cannot easily age and release toxic substances as time goes on. [0003] And, especially in case of an open flame, existing self-insulating sidings contain a large amount of organic material, which can cause serious accidents. Contents of the invention [0004] Aiming at the drawbacks of the prior art, the present invention proposes a method for manufacturing ceramsite self-insulating exterior wall panels. The self-insulating exte...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): E04B1/76C04B38/10C04B28/26
CPCY02A30/244
Inventor 刘小宜谌丰毅蓝九元邓小华涂发强罗细驼黄澍唐勇曾艳婷
Owner JIANGXI THE FIRST CONSTR ENG CORP