Explosion-proof heat-preservation multifunctional sheet material of foaming concrete sandwich and preparation method of material

A foamed concrete, multi-functional technology, used in thermal insulation, chemical instruments and methods, hydraulic material layered products, etc. , to achieve the effect of simple construction process and strong anti-explosion ability

Inactive Publication Date: 2014-08-20
XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing ordinary external wall insulation boards will suffer devastating damage under the explosion and explosive impact of external loads, and may damage the main structure of the building. The splashes formed on the surface of the building under the impact load will also May endanger people's lives and property

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Explosion-proof heat-preservation multifunctional sheet material of foaming concrete sandwich and preparation method of material
  • Explosion-proof heat-preservation multifunctional sheet material of foaming concrete sandwich and preparation method of material
  • Explosion-proof heat-preservation multifunctional sheet material of foaming concrete sandwich and preparation method of material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] A Preparation of explosion-proof lightweight mortar outer guard plate:

[0050] 1) 725 high-strength cement and water are mixed according to the mass ratio of 0.4:1, and the total weight is 55 kg. Add it into the mixer and stir for 8 minutes;

[0051] 2) Add 40 kg of lightweight aggregate shale ceramsite, 3 kg of starch ether, and 2 kg of latex powder to the slurry formed in step 1) and stir for 6 minutes;

[0052] 3) After stirring evenly, pour it into the mold, add a layer of metal grid reinforcement layer when pouring half, and then pour the remaining half, the thickness is about 5-20mm;

[0053] 4) Then carry out moisturizing maintenance according to the traditional process, and finally release the mold;

[0054] B preparation of foam concrete core:

[0055] 1) Mix 20 kg of foaming agent hydrogen peroxide, 0.5 kg of VA-01 emulsion or styrene-butadiene emulsion, and 156 kg of water and stir for 2 minutes to make it uniform;

[0056] 2) 50 kilograms of 32.5R Portla...

Embodiment 2

[0060] Explosion-proof lightweight mortar outer guard plate:

[0061] 1) Mix 52.5R sulfoaluminate cement and water according to the mass ratio of 0.5:1, the total weight is 70 kg, add it into the mixer and stir for 5 minutes;

[0062] 2) In the slurry formed in step 1), add 45 kilograms of light aggregate pumice or tuff, polymer modification additive lignocellulose, 2 kilograms of hydroxypropyl methylcellulose (HPMC) or polypropylene fiber, latex powder 3 Kilograms were stirred and stirred for 5 minutes;

[0063] 3) After stirring evenly, pour it into the mold, add a layer of metal grid reinforcement layer when pouring half, and then pour the remaining half, the thickness is about 5-20mm;

[0064] 4) Then carry out moisturizing maintenance according to the traditional process, and finally release the mold;

[0065] B preparation of foam concrete core:

[0066] 1) Mix 30 kg of LC-2 composite cement foaming agent, 0.3 kg of hydraulic calcium stearate emulsion or vinyl-acrylat...

Embodiment 3

[0071] Explosion-proof lightweight mortar outer guard plate:

[0072] 1) Mix 62.5R slag portland cement and water according to the mass ratio of 0.7:1, and the total weight is 50 kg, add it into the mixer for stirring, and stir for 3 minutes;

[0073] 2) In the slurry formed in step 1), add 25 kilograms of industrial waste light aggregate slag, fly ash ceramsite or natural coal gangue, 4 kilograms of macromolecular modification additive polyvinyl alcohol micropowder, and 1 kilogram of latex powder to stir, Stir for 3 minutes;

[0074] 3) After stirring evenly, pour it into the mold, add a layer of metal grid reinforcement layer when pouring half, and then pour the remaining half, the thickness is about 5-20mm;

[0075] 4) Then carry out moisturizing maintenance according to the traditional process, and finally release the mold;

[0076] B preparation of foam concrete core:

[0077] 1) Mix 12 kg of foaming agent sodium lauryl sulfate (K12), 0.4 kg of VA-01 emulsion, and 216 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of an explosion-proof heat-preservation multifunctional sheet material of a foaming concrete sandwich. The sheet material comprises an outer wall heat-preservation sheet material core body; and explosion-proof light mortar outer protection plates are respectively spliced on the surfaces of the two sides of the outer wall heat-preservation sheet material core body. The explosion-proof heat-preservation multifunctional sheet material of the foaming concrete sandwich has stronger explosion-proof capability and can be used for protecting the safety and stability of a main body structure of a building under the effect of protecting an explosive load; and the heat-preservation, heat-insulation, fireproof, environmentally-friendly performances and the like of the explosion-proof heat-preservation multifunctional sheet material are better than those of like products. The method comprises the following steps of: A, preparing an explosion-proof and light-weight mortar outer protection plate; and B, preparing a foaming concrete core body. The heat-preservation, heat-insulation, fireproof, environmentally-friendly performances and the like of the explosion-proof heat-preservation multifunctional sheet material are better than those of like products and the construction process is simple. Panels on the two sides of the explosion-proof heat-preservation multifunctional sheet material of the foaming concrete sandwich are made of high-strength and light-weight mortar and the strength of the panels is higher. When the panels are cast and molded, a metal grid reinforcing layer is additionally arranged so that the panels have stronger anti-explosion capability.

Description

technical field [0001] The invention relates to an explosion-proof and heat-preserving multifunctional plate with a foamed concrete sandwich, which belongs to the field of new wall heat-preserving materials. Suitable for external wall insulation requirements of industrial or civil buildings. Background technique [0002] With the continuous improvement of people's quality of life, the performance requirements for building exterior wall insulation panels are also getting higher and higher. Although the performances of the existing thermal insulation boards such as light weight, thermal insulation, and fire prevention basically meet the requirements, their explosion-proof performance is not satisfactory. Existing ordinary external wall insulation boards will suffer devastating damage under the explosion and explosive impact of external loads, and may damage the main structure of the building. The splashes formed on the surface of the building under the impact load will also ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): E04B1/80B32B13/04C04B38/02C04B28/04C04B28/06C04B28/08
Inventor 邵珠山王新宇桂学张艳玲
Owner XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap