High-strength high-toughness low-odor polypropylene composition and preparation method and usage thereof

A polypropylene composition, high-strength and high-toughness technology, applied in the polymer field, can solve the problems of low comprehensive mechanical properties and impact performance, and achieve the effects of stable product quality, good application prospects, and simple production process flow

Active Publication Date: 2012-10-31
滁州格美特科技有限公司
View PDF3 Cites 44 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In recent years, people have done a lot of work around these requirements. The patent CN200510026760.0 relates to a low-odor polypropylene compound, but it is mainly talcum powder filled polypropylene, and the comprehensive mechanical properties of the material, especially the impact properties, are relatively low. Low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) 47 parts of homopolypropylene, 30 parts of copolymerized polypropylene, 3 parts of maleic anhydride grafted polypropylene PP-G1001, 0.1 part of antioxidant 1010, 0.2 part of antioxidant 168, 0.2 part of deodorant W1000 , add to the high-speed mixer and mix for 3 to 5 minutes;

[0030] (2) Then add this mixture into the lower hopper of the extruder, and at the same time, add 20 parts of continuous glass fibers through the side feeding port by controlling the feeding and the speed of the main machine, and jointly extrude and granulate. The temperature in each zone of the twin-screw is set from 170°C increments to 215°C.

Embodiment 2

[0032] (1) 36 parts of homopolypropylene, 30 parts of copolymerized polypropylene, 4 parts of maleic anhydride grafted polypropylene PP-G1001, 0.1 part of antioxidant 1010, 0.2 part of antioxidant 168, 0.4 part of deodorant W1000 , add to the high-speed mixer and mix for 3 to 5 minutes;

[0033] (2) Then add this mixture into the lower hopper of the extruder, and at the same time, add 30 parts of continuous glass fibers through the side feed port by controlling the feeding and the main engine speed, and jointly extrude and granulate. The temperature in each zone of the twin-screw is set from 170°C increments to 215°C.

Embodiment 3

[0035] (1) Prepare 42 parts of homopolypropylene, 30 parts of copolymerized polypropylene, 8 parts of maleic anhydride grafted polypropylene PP-G, 0.1 part of antioxidant 1010, 0.2 part of antioxidant 168, 0.6 part of Flavor agent W1000, add to high-speed mixer and mix for 3-5 minutes;

[0036] (2) Then add this mixture into the lower hopper of the extruder, and at the same time, add 20 parts of continuous glass fibers through the side feeding port by controlling the feeding and the speed of the main machine, and jointly extrude and granulate. The temperature in each zone of the twin-screw is set from 170°C increments to 215°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of high polymers and relates to a high-strength high-toughness low-odor polypropylene composition and a preparation method and usage thereof. The high-strength high-toughness low-odor polypropylene composition comprises the following components in parts by weight: 50 to 80 parts of polypropylene, 2 to 9 parts of compatilizer, 0 to 10 parts of thermoplastic elastomer, 0.1 to 0.5 part of antioxidant, 0.2 to 1 part of deodorant and 15 to 35 parts of glass fiber. The composition selects low-odor homopolymerized and copolymerized polypropylene matrix resins, selects a low-odor compatilizer and a reactive deodorant simultaneously, and is simple in production process flow, high in production efficiency, continuous in production process and stable in product quality. The composition maintains the advantages of the polypropylene matrix, and additionally has the capacity of enhancing the strength and the toughness are improved, and reducing the odor is reduced, so that the composition has the comprehensive performance of high strength, high toughness and low odor; and moreover, the requirement on the automotive trim comfort can be well met, and the composition has a good application prospect.

Description

technical field [0001] The invention belongs to the technical field of polymers, and relates to a high-strength, high-toughness and low-odor polypropylene composition, a preparation method and application thereof. Background technique [0002] In recent years, due to the requirements of automobile lightweight and energy saving and emission reduction, plastic materials are more and more used in automobile interior and exterior trims. Polypropylene (PP) is widely used in interior and exterior parts of automobiles due to its low price, easy recycling, small specific gravity, high surface hardness, high elasticity, heat resistance, chemical stability, and good insulation. Bars, anti-scratch strips, door panels, instrument panels, pillars, lamp housings, glove boxes, armrests, etc. However, as people's awareness of comfort and safety continues to increase, people's requirements for the odor, strength and toughness of automotive materials are becoming more and more stringent, req...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/14C08L51/06C08L23/16C08L9/06C08L9/02C08L23/08C08K7/24C08K7/26C08K7/14
Inventor 邵灵芝
Owner 滁州格美特科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap