Method for preparing sulphoaluminate cement by using fluorine-containing sludge

A technology for sulfoaluminate cement and sludge is applied in the field of environmental engineering, which can solve the problems of waste of resources and occupation of landfill resources, and achieve the effect of saving energy and protecting the environment.

Inactive Publication Date: 2012-12-05
苏州伟宇天诚环保科技有限公司
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no comprehensive utilization method for fluorine-containing sludge. After preliminary drying to reduce the moisture content to

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] Example 1: (1) Solidification and drying of fluorine-containing sludge. The sludge with a large fluorine content obtained from the sewage treatment plant was added with a curing agent and a stabilizer, and then mechanically stirred to make the sludge and The curing stabilizer is mixed uniformly. Obtain solidified fluorine-containing sludge. (2) Production of sulphoaluminate cement; 1) Preparation of raw meal. The raw materials used for sulphoaluminate cement are limestone, alumina and gypsum. The specific proportions are: limestone 45%, Al2O3 25%, SiO2 15%, gypsum 12%, fluorine-containing sludge 3%; 2) Clinker firing, raw meal is generally calcined in a rotary kiln at a temperature of 1300~1400℃ The clinker formation process is as follows: at 950℃, C4A3S and C2AS begin to form; at 1100℃, C2S appears; at 1200℃, C2AS disappears and 2C2S·CaSO appears 4 ; At 1250℃, C2S increases; at 1300~1400℃, 2C2S·CaSO 4 Disappear and the clinker burns. 3) Cement preparation, sulphoalumi...

Example Embodiment

[0013] Example 2: (1) Solidification and drying of fluorine-containing sludge. The sludge with a large fluorine content obtained from the sewage treatment plant was added with a curing agent and a stabilizer, and then mechanically stirred to make the sludge and The curing stabilizer is mixed uniformly. Obtain solidified sludge. (2) Production of sulphoaluminate cement, 1) preparing raw meal. The raw materials used for sulphoaluminate cement are limestone, alumina and gypsum. The specific proportions are: limestone 50%, Al2O325%, SiO2 10%, gypsum 14%, fluorine-containing sludge 1%; 2) Clinker firing, raw meal is generally calcined in a rotary kiln, the temperature is 1300~1400℃ During calcination, the clinker formation process is: at 950℃, C4A3S and C2AS begin to form; at 1100℃, C2S appears; at 1200℃, C2AS disappears and 2C2S·CaSO appears 4 ; At 1250℃, C2S increases; at 1300~1400℃, 2C2S·CaSO 4 Disappear and the clinker burns. 3) Cement preparation, sulphoaluminate cement is mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for preparing sulphoaluminate cement by using fluorine-containing sludge, and belongs to the technical field of environmental engineering. The method comprises the following steps that 1, solidifying and desiccating fluorine-containing sludge; and 2, producing sulphoaluminate cement, wherein (1) preparation of raw materials: preparing the sulphoaluminate cement by using the following raw materials in percentage by weight: over 45 percent of CaO, 25 to 35 percent of Al2O3, less than 15 percent of SiO2, over 10 percent of gypsum and 1 to 3 percent of fluorine-containing sludge; (2) burning of chamotte: calcining the raw materials in a rotary kiln at the temperature of between 1,300 and 1,400 DEG C; and (3) preparation of cement: mixing 75 to 80 percent of the chamotte and 20 to 25 percent of the fluorine-containing sludge and grinding the chamotte and the fluorine-containing sludge until a specified specific surface area is reached. According to the method, the aims of innocent, stabilized and recycling use of sludge are achieved by adding the fluorine-containing sludge into the sulphoaluminate cement and burning the mixture of fluorine-containing sludge and the sulphoaluminate cement, so not only energy is saved, but also environment is protected and mankind is benefited.

Description

technical field [0001] The invention belongs to the technical field of environmental engineering, and in particular relates to a method for mixing fluorine-containing sludge into fired sulphoaluminate cement. Background technique [0002] In the field of sewage treatment, the treatment and disposal of sludge, as well as the reduction and recycling of sludge are one of the important issues of environmental protection. Sludge is a by-product of sewage treatment. It is an extremely complex heterogeneous body composed of organic debris, microbial cells, inorganic particles, colloids, etc. Dry sludge usually accounts for 0.3% to 0.5% of the sewage volume or 1% to 2% of the mass. Due to the different sources of sewage, the sludge produced after treatment has different characteristics. It is a special solid waste. Sludge has always been a problem that plagues the normal operation of sewage plants in sewage treatment projects. How to properly treat and dispose of sludge to achieve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B7/36C04B7/32C04B7/24
CPCY02P40/10
Inventor 黄靖宇
Owner 苏州伟宇天诚环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap