Electric brush for ABS system and preparation method thereof

A technology of anti-lock braking system and electric brush, which is applied in the direction of brush manufacturing, circuit, current collector, etc., to achieve low noise, ensure normal and safe use, and smooth friction

Active Publication Date: 2013-01-02
丽水市长新电器制造有限公司
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no reliable similar product in China

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electric brush for ABS system and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] This brush for ABS braking anti-lock braking system includes a brush body and lead wires, and the brush body includes ultrafine electrolytic copper powder, cementing powder, modifier, ultrafine electrolytic copper powder, cementing powder, modifier The weight ratio is: 46 to 52 parts of ultrafine electrolytic copper powder, 52 to 46 parts of cementing powder, and 2 parts of modifier; the cementing powder includes high-purity carbon fiber powder, artificial graphite powder, high-purity sub-nanometer graphite powder, crystal Graphite powder, graphitized carbon black powder, rare earth tungsten disulfide composite material, high temperature resistant phenolic resin, the weight ratio is as follows:

[0040] High-purity carbon fiber powder 1.0-3.0 parts,

[0041] 23-27 parts of artificial graphite powder,

[0042]25-35 parts of high-purity sub-nanometer graphite powder,

[0043] 18-22 parts of crystal graphite powder,

[0044] 3-8 parts of graphitized carbon black powder,...

Embodiment 2

[0073] cementing powder preparation

[0074] 1. Preparation of cementing powder and modifier

[0075] ① The preparation process of cementing powder is the same as that in Example 1.

[0076] ② The ratio of each component of cementing powder is:

[0077] 1.0 parts of high-purity carbon fiber powder,

[0078] 23 parts of artificial graphite powder,

[0079] 25 parts of high-purity sub-nanometer graphite powder,

[0080] 18 parts of crystal graphite powder,

[0081] 3 parts of graphitized carbon black powder,

[0082] Rare earth tungsten disulfide composite material 2.5 parts,

[0083] High temperature resistant phenolic resin 5 parts.

[0084] ③ The ratio of each component of the modifier is:

[0085] 0.20 parts of silver sulfide powder,

[0086] 0.20 parts of antimony powder,

[0087] Zinc powder 0.5 part.

[0088] 2, the molding powder preparation and follow-up process are the same as embodiment one.

[0089] The results of the final product are shown in Table 1 an...

Embodiment 3

[0091] cementing powder preparation

[0092] 1. Preparation of cementing powder and modifier

[0093] ① The preparation process of cementing powder is the same as that in Example 1.

[0094] ② The ratio of each component of cementing powder is:

[0095] 3.0 parts of high-purity carbon fiber powder,

[0096] 27 parts of artificial graphite powder,

[0097] 35 parts of high-purity sub-nanometer graphite powder,

[0098] 22 parts of crystal graphite powder,

[0099] 8 parts of graphitized carbon black powder,

[0100] Rare earth tungsten disulfide composite material 4.5 parts,

[0101] High temperature resistant phenolic resin 15 parts.

[0102] ③ The ratio of each component of the modifier is:

[0103] 1.30 parts of silver sulfide powder,

[0104] Antimony powder 1.5 parts,

[0105] Zinc powder 1.5 parts.

[0106] 2, the molding powder preparation and follow-up process are the same as embodiment one.

[0107] The results of the final product are shown in Table 1 and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to view more

Abstract

An electric brush for ABS (Anti-skid Brake System) comprises a brush body and a lead-out wire, wherein the brush body comprises 46 to 52 parts by weight of superfine electrolytic copper powder, 52 to 46 parts by weight of cementing powder and 2 parts by weight of modifier at; the cementing powder comprises 1.0 to 3.0 parts of high-purity carbon fiber powder, 23 to 27 parts of artificial graphite powder, 25 to 35 parts of high-purity sub-nanometer graphite powder, 18 to 22 parts of crystal graphite powder, 3 to 8 parts of graphitized carbon black powder, 2.5 to 4.5 parts of rare-earth tungsten disulfide composites and 5 to 15 parts of high-temperature resistant phenolic resin; and the modifier comprises 0.20 to 1.30 parts of vulcanization silver powder, 0.20 to 1.5 parts of stibonium powder and 0.5 to 1.5 parts of zinc powder. The chemical stability, the lubricating property, the electrical conductivity, the high-temperature resistance and the abrasion resistance of the electric brush provided by the invention are much better than that of the existing products.

Description

technical field [0001] The invention relates to an electric brush, in particular to an electric brush with super long service life, especially stable and reliable output power, which is suitable for electric energy transmission of motors in ABS brake anti-lock braking systems of automobiles and a preparation method thereof. Background technique [0002] Automobile braking system is closely related to the safe driving of automobiles. In case of an emergency, a vehicle that is not equipped with an ABS system has no time to brake slowly in stages and can only be trampled to death immediately. Due to the sprinting inertia of the vehicle, dangerous situations such as sideslip, deviation of the driving track, and uncontrolled direction of the vehicle body may occur in an instant. The invention of the ABS automobile anti-lock braking system has greatly improved the safety of the automobile in emergency situations. It is a safety device that can effectively prevent the wheel from ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01R39/22H01R43/12
Inventor 陈华安
Owner 丽水市长新电器制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap