Supported metallocene catalyst and preparation method and application thereof

A technology of metallocene catalyst and metallocene compound, which is applied in the field of supported metallocene catalyst and its preparation and application, and can solve the problems of low catalytic activity, low polymerization temperature, easy polymer sticking and energy consumption, etc.

Active Publication Date: 2013-03-06
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] The object of the present invention is to overcome the problem that the catalytic activity of the supported metallocene catalyst in the prior art is low, and the polymer obtained when it is used for olefin polymerization is easy to stick to the kettle and has high energy consumption, and provides a catalyst with high catalytic activity, which is used for olefin A supported metallocene catalyst that does not stick to the kettle during polymerization and has a low polymerization temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Supported metallocene catalyst and preparation method and application thereof
  • Supported metallocene catalyst and preparation method and application thereof
  • Supported metallocene catalyst and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0061] The present invention also provides a method for preparing the above-mentioned supported metallocene catalyst, the preparation method comprising: under the protection of an inert gas, ball milling anhydrous magnesium chloride and alkylaluminoxane at a temperature of 15-100°C for 0.1- 100 hours, then under the protection of an inert gas, the carrier is contacted with the first solution for the third time to obtain the carrier after the third contact, and the first solution contains the product obtained by ball milling and the first solvent; The first solvent on the carrier; carrying out the fourth contact between the carrier removed from the first solvent and the second solution to obtain the carrier after the fourth contact, the second solution containing the metallocene compound and the second solvent, wherein, The average particle diameter of the carrier is 20-80 microns, the specific surface area is 550-650 square meters per gram, the pore volume is 0.4-1.2 milliliter...

Embodiment 1

[0099] This example is used to illustrate the supported metallocene catalyst and its preparation method according to the present invention.

[0100] 2.0 grams of triblock copolymer polyethylene oxide-polyoxypropylene-polyoxyethylene (Aldrich Company, P123) and 15 grams of N,N-dimethylformamide (DMF) were added to 11.2 grams of 37% by weight In a solution (pH=4.4) of hydrochloric acid and 64ml of water, stir at 40°C until the polyoxyethylene-polyoxypropylene-polyoxyethylene is completely dissolved, then add 4.45g of tetraethyl orthosilicate to the above solution, 40 After stirring for 1 hour at ℃, add 1 gram of industrial 955 silica gel, stir at 40 ℃ for 0.3 hours, then transfer the solution to a polytetrafluoroethylene-lined reactor, crystallize in an oven at 150 ℃ for 24 hours and then filter , washed with distilled water, and dried to obtain spherical mesoporous silica raw powder.

[0101] The spherical mesoporous silica raw powder obtained in the previous step was calcined...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a supported metallocene catalyst which comprises a carrier, and an alkylaluminoxane / magnesium chloride complex and a metallocene compound which are supported on the carrier; the carrier is spherical mesoporous silica, wherein the carrier has an average particle diameter of 20-80 microns, a specific surface area of 550-650 square meter / g, a pore volume of 0.4-1.2 ml / g, and a most probable pore size of 1-7 nanometers; the metallocene compound has a structure as shown in formula 1. When the supported metallocene catalyst of the invention is used for catalyzing olefin polymerization, the catalytic efficiency for homopolymerization at 70 DEG C is up to 2.3*10<8> gPE / (mol Zr.h), and the catalytic efficiency for copolymerization at 70 DEG C is up to 2.2*10<8> gPE / (mol Zr.h); the supported metallocene catalyst overcomes the defect of kettle adhesion, has a low polymerization temperature, and thus reduces the energy consumption to some extent.

Description

technical field [0001] The invention relates to a supported metallocene catalyst and its preparation method and application. Background technique [0002] Olefin polymerization catalysts are the core of the development of polyolefin technology, and the carrier is a very critical factor in the innovation of catalysts. The carrier not only plays the role of supporting and dispersing the active center, but also may act as a special ligand and active center, thereby improving the activity and selectivity of the catalyst. At present, most olefin polymerization processes (such as gas phase polymerization, slurry polymerization, etc.) need to use supported catalysts to improve the activity of the catalysts. Meet the process requirements, avoid the phenomenon of polymer sticking to the kettle, and improve the shape of the polymer. [0003] Among the various supports used in supported olefin polymerization catalysts, MgCl 2 Carrier is the most widely used and most effective carrie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F4/6592C08F4/02C08F10/02
Inventor 亢宇张明森王洪涛黄文氢郭顺刘长城邱波姜健准
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka