Oxygen-releasing quick curing patching material as well as preparation method and application of material

A technology of rapid curing and repairing materials, applied in the field of foundry materials, can solve the problems that materials are not suitable for rapid curing methods and long repair time, and achieve the effect of shortening repair curing time, saving materials, and improving curing strength.

Active Publication Date: 2014-09-10
北京仁创合力化工科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For this reason, the technical problem to be solved by the present invention is that the materials used for road surface emergency repair in the prior art are not suitable for fast curing methods, which leads to the problem of longer repair time, and then provides a kind of rapid curing that can release oxygen repair material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The oxygen-releasing fast-curing pavement repair material described in this embodiment is prepared according to the following method from the following components by weight:

[0043] (1) Heat 60 parts of ceramic sand aggregate with a particle size of 70-140 mesh and a specific gravity of 1.8-2.0 to 150-160°C;

[0044] (2) heating and melting 30 parts of thermoplastic phenolic resin, and adding it into the ceramic sand aggregate while it is hot and stirring evenly to obtain a stable coating material;

[0045] (3) Mix 1 part of urotropine and 0.5 part of solid potassium permanganate particles evenly, and add 1.5 parts of water to disperse them evenly;

[0046] (4) Mix the uniform dispersion liquid obtained in step (3) with the coating material obtained in step (2) while it is hot, stir evenly, and heat to evaporate all the water in it;

[0047] (5) Cool the reactant obtained in step (4) to room temperature, crush it to a particle size of 70-140 mesh, and sieve it to obta...

Embodiment 2

[0050] The oxygen-releasing fast-curing pavement repair material described in this embodiment is prepared according to the following method from the following components by weight:

[0051] (1) Heat 95 parts of ceramsite aggregate with a particle size of 70-140 mesh and a specific gravity of 1.7-2.5 to 700-800°C, and then naturally cool to 90-100°C;

[0052] (2) Heat and melt 4 parts of thermoplastic boron phenolic resin, and add it to the ceramsite aggregate while it is hot and stir evenly to obtain a stable coating material;

[0053] (3) Mix 10 parts of urotropine and 1 part of solid potassium chlorate particles evenly, and add 4 parts of water to disperse them evenly;

[0054] (4) Mix the uniform dispersion liquid obtained in step (3) with the coating material obtained in step (2) while it is hot, stir evenly, and heat to evaporate all the water in it;

[0055] (5) Cool the reactant obtained in step (4) to room temperature, crush it to a particle size of 70-140 mesh, and sie...

Embodiment 3

[0058] The oxygen-releasing fast-curing pavement repair material described in this embodiment is prepared according to the following method from the following components by weight:

[0059] (1) Heat 85 parts of small steel ball aggregates with a particle size of 20-40 mesh and a specific gravity of 7.9 to 160-200°C, and then naturally cool to 90-100°C;

[0060] (2) Heat and melt 10 parts of the thermoplastic silicone modified epoxy resin, and add it into the small steel ball aggregate while it is hot and mix evenly to obtain a stable coating material;

[0061] (3) Mix 2 parts of ammonium chloride and 0.6 parts of solid sodium nitrate particles evenly, and add 2.5 parts of water to disperse them evenly;

[0062] (4) Mix the uniform dispersion liquid obtained in step (3) with the coating material obtained in step (2) while it is hot, stir evenly, and heat to evaporate all the water in it;

[0063] (5) Cool the reactant obtained in step (4) to room temperature, crush it to a par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
strengthaaaaaaaaaa
strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of casting materials, and in particular relates to an oxygen-releasing quick curing patching material as well as a preparation method and application of the material in the field of quickly repairing pavements. The oxygen-releasing quick curing patching material provided by the invention consists of 60-95 parts of compact aggregate, 4-30 parts of thermoplastic resin bonder and1-10 parts of a thermal initiation latent curing agent which can induce the thermoplastic resin bonder to be quickly cured in a heated state, and 0.5-1 part of solid oxidant which is heated to release oxygen. The patching material in the heated state can release a small amount of oxygen and support combustion of heat release of combusting substances so as to provide heat required by curing the patching material, and therefore, the purposes of quick curing and repairing are realized.

Description

technical field [0001] The invention belongs to the field of casting materials, and in particular relates to a repair material capable of releasing oxygen when heated and rapidly solidified, a preparation method thereof, and an application in the field of rapid repair of road surfaces. Background technique [0002] With the rapid development of my country's economy, the number of airport runways has increased rapidly, a large number of high-grade highways have been constructed, and the implementation of concrete projects such as city squares and municipal highways has improved the quality of human life and promoted the healthy development of the national economy. Most of the existing roads use concrete construction pavement, which not only has good quality but also has a long service life. However, the maintenance of the concrete pavement after the pavement is damaged during use is more complicated. It needs to be closed and out of service for repair, and it needs to use rel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/10C04B22/08C04B22/12C04B111/72
Inventor 秦升益王振邦汪卫坤
Owner 北京仁创合力化工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap