Environment-friendly colorful tile joint mixture and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of colored tiles and caulking agent, which is applied in the field of tile caulking agent, can solve the problems of waste porcelain powder being difficult to decompose and pollute the environment, and achieve the effects of reducing the possibility of cracks, stabilizing the volume, and improving early strength
Active Publication Date: 2013-06-26
厦门路桥翔通股份有限公司
View PDF4 Cites 38 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] At the same time, as a kind of industrial waste, waste porcelain powder is difficult to de
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0054] The proportion of each component of the environmentally friendly colored tile grout using waste porcelain powder:
[0055] White cement 35%;
[0056] Waste porcelain powder 47.75%;
[0057] Heavy calcium powder 5%;
[0058] Titanium dioxide 10%;
[0059] Redispersible latex powder 1.5%;
[0060] Hydrophobic agent 0.1%;
[0061] Water retaining agent 0.15%;
[0062] 0.4% lignin fiber;
[0063] Water reducing agent 0.1%;
[0064] Pigment 0%.
Embodiment 2
[0066] The proportion of each component of the environmentally friendly colored tile grout using waste porcelain powder:
[0067] White cement 37.5%
[0068] Waste porcelain powder 45.45%
[0069] Heavy calcium powder 10%
[0070] Titanium dioxide 5%;
[0071] Redispersible latex powder 1.25%
[0072] Hydrophobic agent 0.1%;
[0073] Water retaining agent 0.15%;
[0074] 0.4% lignin fiber;
[0075] Water reducer 0.15%;
[0076] Pigment 0%.
Embodiment 3
[0078] The proportion of each component of the environmentally friendly colored tile grout using waste porcelain powder:
[0079] White cement 40%;
[0080] Waste porcelain powder 41.1%;
[0081] Heavy calcium powder 15%;
[0082] Titanium dioxide 0%;
[0083] Redispersible latex powder 1%;
[0084] Hydrophobic agent 0.1%;
[0085] Water retaining agent 0.15%;
[0086] 0.4% lignin fiber;
[0087] Water reducer 0.25%;
[0088] Pigment 2%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an environment-friendly colorful tile joint mixture. The environment-friendly colorful tile joint mixture is characterized by comprising the following components in percentage by weight: 35%-40% of white cement, 40.73%-47.75% of waste porcelain powder, 0-15% of quartz powder, 0-10% of titanium dioxide, 1%-1.5% of re-dispersible emulsion powder, 0.1% of water repellent, 0.15% of water-retaining agent, 0.4% of lignin fiber, 0.1%-0.25% of water reducing agent and 0-2% of pigment. The invention further discloses a preparation method of the environment-friendly colorful tile joint mixture. The consumption of quartz sand and heavy calcium powder is reduced by using the waste porcelain powder as the joint mixture filler; the early strength of the joint mixture is improved by virtue of early strength function of the white cement, so that the construction process requirements are satisfied. The waste porcelain powder is sintered at a high temperature, so that the physical and chemical performances are stable, the volume is stable, and the expansion-shrinkage coefficient is close to that of the tile; the material with the same expansion-shrinkage coefficient is used as the filler, so that the possibility that the tile joint mixture generates cracks can be further reduced.
Description
technical field [0001] The invention relates to a ceramic tile caulking agent used in construction engineering, in particular to an environment-friendly colored ceramic tile caulking agent and a preparation method thereof. Background technique [0002] In modern buildings, tiles have become the main building materials and are widely used in the decoration of the interior and exterior walls and floors of buildings. In order to avoid hollowing between tiles due to thermal expansion and contraction, there must Leave a gap that needs to be filled with tile grout. The tile grout should have an expansion coefficient close to that of the tiles and a certain degree of flexibility, which can expand and contract with the tiles to avoid cracks. The main components of tile grout are cementitious materials, fillers and additives. The cementitious materials endow the grout with adhesion, the additives endow the grout with good workability, flexibility and other functions, and the fillers...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more