Production method of composite material stirring wing

A composite material and production method technology, applied in casting molding equipment, molds, cores, etc., to achieve the effects of improving tensile strength and elongation, improving metal passivation performance, and improving comprehensive mechanical performance indicators

Inactive Publication Date: 2013-08-21
QINGDAO YUXIN VEHICLE ENG
View PDF9 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention proposes a method for producing composite material stirring wings, which solves the production problem of stirring wings with high safety and reliability in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of composite material stirring wing
  • Production method of composite material stirring wing
  • Production method of composite material stirring wing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0079] A method for producing a composite material stirring wing, comprising the following steps:

[0080] (1) Wax pressing process, using a wax pressing machine to make a wax mold, repairing the flash and burrs of the wax mold, and then assembling the wax mold to the pouring system, and welding the wax mold and the pouring system to form a wax tree;

[0081] (2) In the shell making process, the surface of the wax tree is coated with a coating with silica sol as a binder. When the coating does not flow, the upper layer of sand is sprinkled, and dried and solidified; similarly, the second layer of coating is sprinkled with the upper layer of sand; Starting from the third layer, paint with water glass as the binder, and sprinkle the upper layer of sand, and dry for 3-5 hours after each layer of paint to obtain the coated mold shell;

[0082] (3) Dewaxing process, put the coated mold shell into hot water above 95°C, and melt the wax in it to form a cavity mold shell;

[0083] (4...

Embodiment 2

[0094] A method for producing a composite material stirring wing, comprising the following steps:

[0095] (1) In the process of wax pressing, the prepared wax paste is injected into the wax press machine, and the wax mold is prepared by using the mold; at the same time, the wax mold is prepared with the wax paste to prepare the wax mold of the pouring system. The wax mold is repaired with burrs, and then the wax mold is assembled on the pouring system, and the wax mold and the pouring system are welded to form a wax tree;

[0096] (2) In the shell making process, the surface of the wax tree is coated with a coating with silica sol as a binder. When the coating does not flow, the upper layer of sand is sprinkled, and dried and solidified; similarly, the second layer of coating is sprinkled with the upper layer of sand; From the third layer, paint with water glass as a binder, and sprinkle the upper layer of sand, and dry for 3 hours after each coat of paint to obtain a coated ...

Embodiment 3

[0109] A method for producing a composite material stirring wing, comprising the following steps:

[0110] (1) In the process of wax pressing, the prepared wax paste is injected into the wax press machine, and the wax mold is prepared by using the mold; at the same time, the wax mold is prepared with the wax paste to prepare the wax mold of the pouring system. The wax mold is repaired with burrs, and then the wax mold is assembled on the pouring system, and the wax mold and the pouring system are welded to form a wax tree;

[0111] (2) In the shell making process, the surface of the wax tree is coated with a coating with silica sol as a binder. When the coating does not flow, the upper layer of sand is sprinkled, and dried and solidified; similarly, the second layer of coating is sprinkled with the upper layer of sand; From the third layer, paint with water glass as a binder, and sprinkle the upper layer of sand, and dry for 4 hours after each layer of paint to obtain a coated...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention provides a production method of a composite material stirring wing. The method comprises the following steps of: (1) wax pressing process; (2) shell making process; (3) dewaxing process; (4) roasting process; (5) composite material smelting process; (6) clean sand pouring process; (7) sprue removing and cleaning process; and (8) heat treatment process. The production method can be used for producing the stirring wing with high safety and reliability, and the high-quality composite material stirring wing can be produced by the method.

Description

technical field [0001] The invention relates to the technical field of stirring wing materials, in particular to a production method of a composite material stirring wing. Background technique [0002] The stirring wings in the vehicle-mounted bottom mortar mixing and conveying mechanism bear the surface friction and impact fatigue caused by the alternating load of mortar during work. This working condition requires that the stirring wings must have the following functional indicators: (1) The surface hardness is high to adapt to the wear-resistant working environment; (2) The product structure is dense, and the core has appropriate toughness to adapt to the impact of alternating loads. This can overcome the impact fatigue fracture of the product caused by the material brittleness brought about by high hardness. [0003] The main parameters of the existing stirring wings are: unit weight 3.60Kgs / piece; main wall thickness 15mm; outline main dimension 300*200*130mm. The mai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22C9/04B22C9/22C22C38/28C22C33/04
Inventor 任石鑫
Owner QINGDAO YUXIN VEHICLE ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap