Multistage and ordered In2O3 structures growing along TiO2 nanofiber surfaces and preparation method

A nanofiber, surface growth technology, applied in the direction of nanotechnology, nanotechnology, chemical instruments and methods, etc., can solve the problems of inability to prepare, and achieve high permeability, high specific surface area, good photocatalytic performance and electrical conductivity Effect

Inactive Publication Date: 2013-10-02
ZHEJIANG SCI-TECH UNIV
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] There are many ways to prepare diindium trioxide: high-frequency oxygen blowing method, nitrate decomposition method, indium

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multistage and ordered In2O3 structures growing along TiO2 nanofiber surfaces and preparation method
  • Multistage and ordered In2O3 structures growing along TiO2 nanofiber surfaces and preparation method
  • Multistage and ordered In2O3 structures growing along TiO2 nanofiber surfaces and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] In the present invention 2 o 3 A method for preparing a multi-level ordered structure, comprising the following steps:

[0026] (1) Preparation of TiO by hydrothermal method 2 Nanofiber substrate: Put the titanium sheet into acetone for ultrasonic cleaning and put it in a drying oven for drying; then place the titanium sheet in a reaction kettle and immerse it in a NaOH solution with a concentration of 2mol / L; put the reaction kettle in a resistance furnace Heat at 220°C-240°C for 2-10 hours and then cool down naturally; take out the titanium sheet, rinse it with distilled water, and dry it to get the desired surface long and multi-wall tough TiO 2 Nanofiber substrate.

[0027] (2) Preparation of multi-level ordered In by magnetron sputtering 2 o 3 Structure: will In 2 o 3 Target and TiO prepared in step 1 2 The nanofiber substrate is placed in a multi-target magnetron sputtering apparatus, the target step distance is adjusted to 3cm-4cm, argon gas is introduced...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an In2O3 oriented growth structure, flower-like structure, dendritic structure, hollowed structure and tetrahedral structure along TiO2 nanofiber surfaces and a preparation method. The TiO2 nanofiber is prepared by the hydro-thermal synthesis method. The In2O3 is prepared by the magnetron sputtering technology. The In2O3 oriented growth, flower-like, dendritic, hollowed and tetrahedral structures are multistage and ordered, and are advantaged by high specific surface area, high permeability, good photocatalytic performance and conductivity.

Description

technical field [0001] The invention relates to a multi-level ordered In 2 o 3 structure, especially involving a TiO 2 Oriented growth structure, flower-like structure, dendritic structure, hollow-out structure, tetrahedral structure displayed on the surface of the nanofiber and a preparation method thereof. Background technique [0002] Dioxide (In 2 o 3 ) Indium is an extended product of indium, which is a frequently used raw material in resistive touch screens, mainly used in fluorescent screens, glass, ceramics, chemical reagents, etc. In addition, it is widely used in traditional fields such as colored glass, ceramics, mercury substitution for alkaline manganese batteries, and chemical reagents. In recent years, it has been widely used in high-tech fields such as the optoelectronic industry and military fields. It is especially suitable for processing into indium tin oxide (ITO) targets, manufacturing transparent electrodes and transparent heat reflector materials,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01G15/00B82Y30/00B82Y40/00
Inventor 陈旭董文钧
Owner ZHEJIANG SCI-TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap