Blue glass coating method and system
A coating system and blue glass technology, applied in chemical instruments and methods, glass/slag layered products, layered products, etc., can solve the problem that coated blue glass is difficult to meet spectroscopic requirements and ring measurement requirements, and cannot control different wavelengths. Problems such as transmittance of light-coated blue glass
Inactive Publication Date: 2016-03-09
SHENZHEN O FILM TECH
View PDF2 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The traditional coating method cannot control the transmittance of different wavelengths of light relative to the coated blue glass, and the selected film system cannot meet the requirements for the transmittance of different wavelengths of light, so it is difficult for the coated blue glass to achieve specific light splitting. Requirements and Ring Test Requirements
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0028] see figure 1 , in one embodiment, a kind of blue glass coating method 100 comprises the following steps:
[0029] Step S110, measuring the transmittance of the blue glass for light of different wavelengths.
[0030] In one embodiment, the transmittance of light having integer wavelengths can be measured.
[0031] In one embodiment, the transmittance of light of different wavelengths is measured, the wavelength of the measured light is a continuous integer greater than 380nm and less than 1200nm, that is, the wavelength of the measured light starts at 380nm and increases to 1200nm.
[0032] In step S120, a spectral curve of the blue glass is formed according to the transmittance of different wavelengths.
[0033] Since the wavelength of the light of the measured wavelength is continuously distributed, and the blue glass has a transmittance for each wavelength of light, so the wavelength is taken as the abscissa, and the transmittance is used as the ordinate, then the ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a method for plating a film on blue glass. The method comprises the following steps of: measuring the transmittance of the blue glass relative to lights with different wavelengths; forming a light-splitting curve of the blue glass according to the transmittance for different wavelengths; selecting a film system according to the light-splitting curve; plating the film according to the film system. The method is characterized in that the transmittance of the blue glass relative to the lights with different wavelengths is measured, the curve is formed according to the measured transmittance, and is the inherent light-splitting curve of the blue glass, the film system is selected according to the light-splitting curve of the blue glass, and the film is plated on the blue glass according to the film system. The film system selected according to the light-splitting curve of the blue glass can meet the requirement of the transmittance of the lights with different wavelengths. According to the method disclosed by the invention, the transmittance of the blue glass relative to the lights with different wavelengths can be controlled so as to meet the different light-transmitting requirements of the blue glass relative to the lights with different wavelengths. The invention also provides a system for plating the film on the blue glass.
Description
technical field [0001] The invention relates to glass coating technology, in particular to a blue glass coating method and system. Background technique [0002] In the traditional coating technology, since the glass has a fixed transmittance, the transmittance of the glass is measured, and the film system is selected according to the transmittance to achieve a certain light transmission effect. However, because blue glass has different transmittances for light of different wavelengths, blue glass itself has an inherent spectral curve. The traditional coating method cannot control the transmittance of different wavelengths of light relative to the coated blue glass, and the selected film system cannot meet the requirements for the transmittance of different wavelengths of light, so it is difficult for the coated blue glass to achieve specific light splitting. requirements and ring testing requirements. Contents of the invention [0003] Based on this, it is necessary to p...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine