A kind of production method of rose-colored rare earth doped quartz tube with low hydroxyl

A rare earth doping and production method technology, applied in glass forming, glass manufacturing equipment, manufacturing tools and other directions, can solve the problems of easy fading, inconsistent color uniformity, large diameter range and wall thickness error, etc., to achieve technical results Obvious, consistent color uniformity, small diameter range and wall thickness error

Active Publication Date: 2016-02-10
连云港龙立石英制品有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The technical content closest to the red quartz tube: the red quartz tube produced by using high-purity quartz raw materials doped with rare earth element oxides. Magnesium 0.1-5%, after being mixed with high-purity quartz raw materials and evenly dried, red quartz tubes can be produced directly after being put into a continuous melting furnace, but the coloring effect is not good, the error of the tube diameter range and wall thickness is large, and it is easy to fade. Inconsistent color uniformity
[0003] The technical content closest to the blue quartz tube: the blue quartz tube produced by doping rare earth element oxides with high-purity quartz raw materials. Titanium 0.1-5%, cobalt oxide 0.1-5%, after being mixed with high-purity quartz raw materials and evenly dried, the blue quartz tube can be directly produced after being put into a continuous melting furnace, but the coloring effect is not good, and the range of tube diameter and wall thickness The error is large, and it is easy to fade, and the color uniformity is inconsistent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] A kind of production method of low hydroxyl rose color rare earth doped quartz tube, concrete steps are as follows:

[0019] (1) Selection of raw materials: select high-purity quartz, of which SiO 2 ≥99.99999%, used as doping raw material for rose quartz tube doped with rare earth element nitrating agent;

[0020] (2) Stirring: mix 0.1-15% samarium nitrate, 0.1-15% aluminum nitrate, 0.1-15% potassium nitrate, 0.1-15% zinc nitrate, 0.1-15% barium nitrate, 0.1 ~ 15% sodium nitrate and various nitrating agents, using warm water not greater than 80°C, the total amount of water not greater than 60 kg of the weight of various nitrating agents is mixed with raw materials;

[0021] (3) Dilution: adding strong hydrofluoric acid no greater than 15% of the total amount of various nitrating agents to dilute and accelerate the reaction, so that various nitrating agents can be evenly mixed;

[0022] (4) Doping: Doping with high-purity quartz powder 80-160 mesh, after being evenly s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method of a low-hydroxyl rosy rare-earth-doped quartz tube. The invention belongs to the technical field of quartz tube production. The method comprises the steps that: (1) raw materials are selected, wherein high-purity quartz is selected; (2) stirring is carried out, wherein various rare earth nitrating agents such as samarium nitrate are added into the raw material, and mixing and stirring are carried out; (3) dilution is carried out, wherein strong hydrofluoric acid is added, and a dilution reaction is carried out; (4) doping is carried out, wherein the material is doped with a high-purity quartz powder material; and the mixture is placed into a high-temperature-resistant quartz tube; (5) bake-drying is carried out, wherein high-temperature continuous bake-drying is carried out, such that the various rare earth nitrating agents completely penetrating into the quartz powder material; (6) melting is carried out, wherein the material is molten in a continuous melting furnace; through tube-drawing machine drawing, an integrally colored rosy quartz tube is obtained; and (7) decarboxylation is carried out, wherein the rosy quartz tube is subjected to high-temperature decarboxylation in a vacuum decarboxylation furnace. The method is mainly used in the aspect of quartz tube manufacturing.

Description

technical field [0001] The invention relates to the technical field of quartz tube manufacture, in particular to a production method of a rose-colored rare earth-doped quartz tube with low hydroxyl. Background technique [0002] The technical content closest to the red quartz tube: the red quartz tube produced by using high-purity quartz raw materials doped with rare earth element oxides. Magnesium 0.1-5%, after being mixed with high-purity quartz raw materials and evenly dried, red quartz tubes can be produced directly after being put into a continuous melting furnace, but the coloring effect is not good, the error of the tube diameter range and wall thickness is large, and it is easy to fade. Inconsistent color uniformity. [0003] The technical content closest to the blue quartz tube: the blue quartz tube produced by doping rare earth element oxides with high-purity quartz raw materials. Titanium 0.1-5%, cobalt oxide 0.1-5%, after being mixed with high-purity quartz raw...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03B20/00
Inventor 单军成
Owner 连云港龙立石英制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products