High-performance power accumulator and preparation method thereof

A power type, battery technology, applied in lead-acid batteries, lead-acid battery electrodes, battery electrodes, etc., can solve the problems of low-temperature and high-current discharge of batteries, shedding of positive active materials, and low utilization of active materials, etc., to prolong life. , the effect of improving electrical conductivity and improving utilization

Active Publication Date: 2013-11-27
TIANNENG GRP JIANGSU TECH
View PDF7 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a high-performance power storage battery. The composition ratio and preparation method of the positive and negative plates are different, which can effectively solve the problem of shedding of the active material of the positive electrode, poor discharge of the battery at low temperature and high current, and the utilization rate of the active material. low, poor consistency of battery packs, and short service life, the performance index is obviously superior to that of ordinary lead-acid batteries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance power accumulator and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A high-performance power storage battery, including a positive plate and a negative plate,

[0021] The positive plate lead paste is prepared from the following components by weight: 1000 parts of lead powder, 100 parts of deionized water, 70 parts of sulfuric acid solution with a mass percentage concentration of 50%, 0.6 parts of polyester fiber, 4 parts of polyaniline, four alkali 8 parts of formula lead sulfate, 1 part of stannous sulfate;

[0022] The negative plate lead paste is prepared from the following components by weight: 1000 parts of lead powder, 90 parts of deionized water, 70 parts of sulfuric acid solution with a mass percent concentration of 50%, 0.6 parts of polyester fiber, 8 parts of barium sulfate, and 1 part of lignin , 0.5 parts of super carbon black.

Embodiment 2

[0024] A high-performance power storage battery, including a positive plate and a negative plate,

[0025] The positive plate lead paste is prepared from the following components by weight: 1000 parts of lead powder, 110 parts of deionized water, 90 parts of sulfuric acid solution with a concentration of 50% by mass, 0.8 parts of polyester fiber, 8 parts of polyaniline, four Basic lead sulfate 15 parts, stannous sulfate 2.3 parts;

[0026] The negative plate lead paste is prepared from the following components by weight: 1000 parts of lead powder, 110 parts of deionized water, 100 parts of sulfuric acid solution with a mass percent concentration of 50%, 0.8 parts of polyester fiber, 10 parts of barium sulfate, 2.5 parts of lignin, super Carbon black 2.2.

Embodiment 3

[0028] A high-performance power storage battery, including a positive plate and a negative plate,

[0029] The positive plate lead paste is prepared from the following components by weight: 1000 parts of lead powder, 120 parts of deionized water, 100 parts of sulfuric acid solution with a concentration of 50% by mass, 0.6-0.9 parts of polyester fiber, 4-10 parts of polyaniline 8-20 parts of tetrabasic lead sulfate, 1-3 parts of stannous sulfate;

[0030] The negative plate lead paste is prepared from the following components by weight: 1000 parts of lead powder, 95 parts of deionized water, 90 parts of sulfuric acid solution with a mass percent concentration of 50%, 0.9 parts of polyester fiber, 12 parts of barium sulfate, 3 parts of lignin, super carbon black3.

[0031] The positive and negative plate lead pastes of the above-mentioned embodiments are prepared according to the following steps respectively:

[0032] Positive plate lead paste production steps, according to th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-performance power accumulator and a preparation method thereof. Graphite is substituted by a novel conductive agent, namely, polyaniline, in the lead paste of a positive plate; the conductivity of a mixture of the polyaniline and lead dioxide is improved by 12.5 times; acetylene black is substituted by a novel conductive agent, namely, super carbon black, in the lead paste of a negative plate, the specific surface area of the super carbon black is 130-190m<2> / g, and the adsorption is high. During preparation, water is firstly added, then an additive is added, the water and the additive are mixed and then lead powder is added, while the original steps of adding the additive firstly, adding the lead powder, adding the water and then stirring are changed, so that the additive is well dispersed. According to the high-performance power accumulator and the preparation method thereof, the utilization rate of an active material is effectively improved, the consistency of the battery is improved, the discharge depth of the battery is great, and the cycle life is long.

Description

technical field [0001] The invention relates to the technical field of storage batteries, in particular to a high-performance power storage battery and a preparation method thereof. Background technique [0002] At present, electric vehicles are an environmentally friendly means of transportation in my country. Lead-acid batteries for electric vehicles are the core components of electric vehicles. They are used in large quantities. They are high-rate recyclable batteries. The design requirements are reasonable and the process control requirements are strict. The performance of lead-acid battery products is mainly reflected in: 1. charge acceptance capacity; 2. low-temperature high-current discharge capacity; 3. active material utilization rate; 4. reaction area; 5. service life. [0003] For power batteries, the depth of discharge should be deep and the cycle life should be long. The formula and manufacturing method of the positive and negative plate lead paste largely deter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/06H01M4/14H01M4/62H01M4/16
CPCY02E60/126Y02E60/10
Inventor 王斌方明学史忠立顾中洋张慧李军李春景陈战营
Owner TIANNENG GRP JIANGSU TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap