A multifunctional catalytic composition

A composition and mixture technology, applied in catalytic cracking, chemical/physical process, physical/chemical process catalyst, etc., can solve the problem of high gasification temperature

Active Publication Date: 2015-09-23
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a catalytic composition suitable for cracking conversion of heavy raw materials and promoting coke gasification in view of the high gasification temperature problem of the catalytic composition used for cracking gasification in the prior art , to overcome the problem of high gasification temperature of the prior art catalytic composition during use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A multifunctional catalytic composition
  • A multifunctional catalytic composition
  • A multifunctional catalytic composition

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] In the preparation process of the mesoporous silicon-aluminum material of the present invention, the aluminum source can be various aluminum sources conventionally used in the preparation process of the mesoporous silicon-aluminum material, for example, it can be selected from aluminum nitrate, aluminum sulfate or aluminum chloride. one or more of .

[0044] In the preparation process of the mesoporous silica-alumina material of the present invention, the silicon source can be various silica-alumina conventionally used in the preparation process of the mesoporous silica-alumina material, such as silica gel, water glass, sodium silicate, tetraethyl At least one of silicon, silicon oxide, silica sol and silica gel.

[0045] In the preparation process of the mesoporous silica-alumina material of the present invention, the alkaline solution can be various conventional alkaline solutions, for example, it can be one of ammonia water, potassium hydroxide solution, sodium metaa...

Embodiment approach

[0051] The preparation method of described catalytic composition provided by the present invention, a kind of preferred embodiment, comprises the following steps:

[0052] (1) Mix and beat the non-ion-exchanged mesoporous silica-alumina material with water to obtain a slurry, and then contact the obtained slurry with an inorganic acid at room temperature to 100°C for at least 0.2 hours to obtain a sodium oxide content of not more than 0.2% by weight A mesoporous silica-alumina material, wherein the weight ratio of the non-ion-exchanged mesoporous silica-alumina material, water and inorganic acid is 1:5-30:0.03-0.3;

[0053] (2) Mix and beat potassium-containing compounds, alkaline earth metal compounds and silicon-aluminum components, then dry them into dry materials, and then roast them at 800°C~1150°C, preferably 900°C~1100°C for 1~10 hours, and then get Potassium-containing gasification active components; wherein the molar ratio of alkaline earth metal compounds calculated ...

preparation Embodiment 1

[0068] The mesoporous material SA-2 was prepared according to the preparation method of the mesoporous material in Example 2 published by CN1565733A.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

A multifunctional catalysis composition comprises 1-70wt% of a mesoporous aluminosilicate material, 1-60wt% of a gasification active component, 0-70wt% of clay and 5-98wt% of a heatproof inorganic oxide by oxide, wherein the mesoporous aluminosilicate material has a phase structure of pseudo-boehmite, has an anhydrous chemical expression formula of (0-0.3)Na2O.(40-90)Al2O3.(10-60)SiO2 by weight of oxide, and has a specific surface area of 200-400m<2> / g, a pore volume of 0.5-2.0mL / g, an average aperture of 8-20nm and a most probable aperture of 5-15nm. The catalysis composition is used for the cracking gasification of heavy petroleum hydrocarbons, and realizes a low gasification temperature.

Description

technical field [0001] The present invention relates to a catalytic composition used in the cracking process of heavy petroleum hydrocarbons and the coke gasification combined process produced by cracking, more specifically, relates to a method for processing heavy petroleum hydrocarbons by using thermal cracking or / and catalytic cracking processes It is a multifunctional catalytic composition for the process of producing light fuel from raw materials and gasifying the coke produced in the process into hydrogen or synthesis gas with the participation of gasification agent. Background technique [0002] At present, when catalytic cracking processes heavy and low-quality feedstock oil, it poses challenges to the catalytic cracking process itself and the catalyst. Non-catalytic processing of low-quality heavy oil, including delayed coking, fluidized coking, and flexible coking, has attracted increasing attention. However, the coking process has the problems of high coke yield a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/04C10G11/04C10J3/02
CPCY02P20/52
Inventor 杨雪朱玉霞王子军陈振宇罗一斌张书红汪燮卿
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com