Glass fiber infiltrating agent composition as well as preparation method and application thereof
A technology of glass fiber and sizing agent, applied in the field of composite materials, can solve the problems of damage to the properties of carbon nanomaterials, cumbersome chemical reaction grafting process, and reduced mechanical properties of glass fibers, etc., so as to avoid the defects of chemical reaction grafting process. Effect
Active Publication Date: 2014-02-12
CHONGQING POLYCOMP INT
View PDF11 Cites 34 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, the high temperature required for chemical vapor deposition will lead to the reduction of the mechanical properties of the glass fiber itself, and the c
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0028] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.
[0029] Preparation of glass fiber sizing compositions (Experiment 1-Experiment 6):
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more
Abstract
The invention provides a glass fiber infiltrating agent composition. The glass fiber infiltrating agent composition comprises a carbon nano material, a dispersant, a polymer emulsion, a coupling agent and a solvent in a mass ratio of (0.05-3):(0.025-4):(0.15-5):(0.05-1.25):(8-49). The infiltrating agent composition has good stability, the deposition of the carbon nano material on fiber surfaces is realized by coating the infiltrating agent composition on glass fiber surfaces, the performance of the glass fibers and the carbon nano material can not be damaged, and the mechanical property and thermal conductivity of the glass fibers and a composite material thereof can be effectively improved at the same time.
Description
technical field [0001] The invention belongs to the technical field of composite materials, and relates to a glass fiber sizing composition, a preparation method and an application thereof. Specifically, coating the sizing composition on the glass fiber can effectively improve the thermal conductivity and mechanical properties of the glass fiber and its composite material. Background technique [0002] Glass fiber has the advantages of high mechanical strength, good insulation, strong heat resistance, and good corrosion resistance, and is widely used in the reinforcement of resin-based composite materials. Due to the low surface activity of glass fiber, when used as a composite material reinforcement, it often has the disadvantages of poor compatibility with the matrix resin and weak interfacial interaction. The interface is an extremely important microstructure of composite materials. It acts as a "bridge" connecting the reinforcement and the matrix, and has a crucial impa...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
IPC IPC(8): C03C25/44C08K9/06C08K7/14
Inventor 彭珂任冬友
Owner CHONGQING POLYCOMP INT
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap