A detection method for hot stamping performance of anodized aluminum

A detection method, the technology of anodized aluminum, applied in the direction of copying/marking, general parts of printing machinery, printing, etc., can solve the problems of anodized aluminum waste, poor hot stamping performance, etc., achieve simple detection method, save preparation time, Material saving effect

Active Publication Date: 2016-03-23
襄阳金飞环彩色包装有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a detection method for the hot stamping performance of anodized aluminum, which solves the problem that the hot stamping performance is found to be poor after the anodized aluminum has been put into production in the past, resulting in the waste of anodized aluminum

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A detection method for hot stamping performance of anodized aluminum
  • A detection method for hot stamping performance of anodized aluminum

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A method for detecting hot stamping performance of anodized aluminum comprises the following steps, and each step is specifically described.

[0031] S1. Prepare hot stamping equipment for anodized aluminum verification, check whether the temperature control sensor, pressure sensor and pressure closing time indication are normal, and check whether the electrical circuit and safety protection devices are normal.

[0032] S2. Prepare a bronzing verification plate with graphics. The bronzing verification plate is a red copper plate with a thickness of 1.5 mm, a length of 12 cm, and a width of 8 cm; wherein the graphic text on the bronzing verification plate is completed by computer-controlled micro-carving , the graphics and text include lines of different thicknesses and solid areas, the thickness of the lines includes 0.1mm lines, 0.25mm lines, 0.4mm lines and 0.5mm lines, and the spacing between adjacent lines includes 0.05 mm pitch, 0.08mm pitch, 0.15mm pitch, and 0.3m...

Embodiment 2

[0040] A method for detecting hot stamping performance of anodized aluminum comprises the following steps, and each step is specifically described.

[0041] S1. Prepare hot stamping equipment for anodized aluminum verification, check whether the temperature control sensor, pressure sensor and pressure closing time indication are normal, and check whether the electrical circuit and safety protection devices are normal.

[0042] S2. Prepare a bronzing verification plate with graphics. The bronzing verification plate is a brass plate with a thickness of 3.0mm, a length of 5cm, and a width of 5cm; wherein the graphics and texts on the bronzing verification plate are made by computer-controlled micro-carving Completed, the graphics and text include lines of different thicknesses and solid areas, the thickness of the lines includes lines of 0.6mm, 0.7mm, 0.9mm and 1.0mm, and the distance between adjacent lines includes 0.1mm spacing, 0.2mm spacing, 0.4mm spacing and 0.5mm spacing, t...

Embodiment 3

[0049] A method for detecting hot stamping performance of anodized aluminum comprises the following steps, and each step is specifically described.

[0050] S1. Prepare hot stamping equipment for anodized aluminum verification, check whether the temperature control sensor, pressure sensor and pressure closing time indication are normal, and check whether the electrical circuit and safety protection devices are normal.

[0051] S2. Prepare a bronzing verification plate with graphics. The bronzing verification plate is a steel plate with a thickness of 5.0 mm, a length of 15 cm, and a width of 15 cm; wherein the graphic text on the bronzing verification plate is completed by computer-controlled micro-carving , the graphics include lines of different thicknesses and solid areas, the thickness of the lines includes lines of 1.5mm, 1.65mm, 1.8mm and 2.0mm, and the distance between adjacent lines includes 0.5 mm pitch, 0.6mm pitch, 0.8mm pitch, and 1.0mm pitch.

[0052] S3. Install...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
widthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for detecting alumite hot stamping performance. Gold stamping equipment capable displaying and adjusting hot stamping temperature, hot stamping pressure and pressing time to perform hot stamping on the cut part of alumite; if the hot stamping is clear, the hot stamping performance of the alumite is qualified, and the parameters of the hot stamping temperature, the hot stamping pressure and the pressing time are recorded; if the hot stamping is obscure, the hot stamping performance of the alumite is unqualified. Detection of the alumite before production can avoid waste of alumite, production time occupation of production equipment, and efficiency can be increased.

Description

technical field [0001] The invention relates to the technical field of printing, in particular to a method for detecting hot stamping performance of anodized aluminum. Background technique [0002] Post-press processing technology, as the post-printing process, is widely used in the production process of various printed products, among which bronzing process is especially widely used. Bronzing has bright patterns and clear edges, which can embellish graphics and texts to make the finishing point and increase product quality. The role of added value. [0003] The material used for hot stamping is mainly anodized aluminum material. The structure and production process of this material are complex. Many factors in the production process have a great impact on the quality of the product, especially the hot stamping performance of the product. Therefore, how to quickly and accurately identify the anodized aluminum Hot stamping performance has become the most concerned issue for ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B41F33/00B41M5/382
Inventor 罗代璋李树军李双劲陈思涛张建平
Owner 襄阳金飞环彩色包装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap