Method for leaching positive-negative pole material mixture of waste nickel-metal hydride battery

A technology of waste nickel-hydrogen batteries and mixed materials, applied in the direction of improving process efficiency, etc., can solve the problems of uneconomical industrial pure oxygen for personal use, complicated leaching equipment, and small amount of industrial pure oxygen, etc., and achieve obvious economic and environmental benefits , Reduce pollution control costs, improve the effect of metal leaching rate

Inactive Publication Date: 2014-04-30
SICHUAN NORMAL UNIVERSITY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The equipment of the hydrochloric acid leaching method is highly corroded, and the amount of acid mist generated is large and pollutes the environment
Sulfuric acid leaching consumes more expensive reducing agents (such as hydrogen peroxide, etc.), and the leaching speed is slow and the acid consumption is high
The consumption of nitric acid in the nitric acid leaching method is large, and a large amount of nitrogen oxides will be produced, polluting the environment
All wet processes have the problem of how to economically increase the leaching speed, increase the metal leaching rate, and reduce the consumption of acid and other auxiliary materials.
Although the pure oxygen leaching method in the nitric acid processing industry and the pure oxygen leaching method in the mixed acid processing industry have solved the above problems, the leaching equipment is more complicated, and the amount of industrial pure oxygen required for the leaching of waste batteries is not large, and waste battery treatment enterprises produce on-site Industrial pure oxygen is not economical for personal use, and the storage, transportation and use of industrial pure oxygen are troublesome

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Example 1: Add 100g of the positive and negative mixed materials of nickel-metal hydride waste batteries (containing 55.3% nickel, 6.2% cobalt, and 12.5% ​​rare earth) and 37g ≤ 1.5mm sawdust into a titanium-lined pressure reactor with a volume of 2L. Add 870ml of mixed acid solution with a concentration of sulfuric acid of 1.5mol / L and a concentration of nitric acid of 5g / L, leaching at 50°C to 60°C with airtight stirring (stirring speed 80r / min) for 4 hours, and then carry out liquid-solid separation after leaching to obtain 840ml leaching solution (excluding leaching slag washing water). The leaching rates of nickel, cobalt and rare earths are 99.0%, 98.2% and 8.9% respectively (calculated based on nickel, cobalt and rare earths entering the leaching solution and leaching slag washing solution).

Embodiment 2

[0023] Example 2: Add 500 g of mixed positive and negative electrode materials of waste nickel-metal hydride batteries (containing 55.3% nickel, 6.2% cobalt, and 12.5% ​​rare earth) and 230 g of sawdust ≤ 1.5 mm into a titanium-lined pressure reactor with a volume of 5 L. Add 2700ml of a mixed acid solution with a concentration of sulfuric acid of 3.0mol / L and a concentration of nitric acid of 10g / L, leaching at 70°C to 80°C (stirring speed 70r / min) for 2.0h, and then carry out liquid-solid separation. Obtain 2400ml leaching solution (excluding leaching slag washing water). The leaching rates of nickel, cobalt and rare earth are 99.5%, 99.3% and 7.8% respectively (calculated based on the nickel, cobalt and rare earth entering the leaching solution and leaching slag washing solution).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for leaching a positive-negative pole material mixture of a waste nickel-metal hydride battery. The method comprises the steps of adding the positive-negative pole material mixture which is separated from the waste nickel-metal hydride battery and is subjected to roasting pretreatment, and wood sawdust into a reaction kettle which is resistant to pressure and the corrosion of sulfuric acid and nitric acid, adding a mixed solution of sulfuric acid and nitric acid, and leaching while stirring under closed conditions.

Description

technical field [0001] The invention relates to a method for leaching the positive and negative mixed materials of waste nickel-hydrogen batteries. Background technique [0002] Ni-MH batteries are a type of batteries widely used, and a large amount of waste batteries will be produced after the batteries are scrapped. Because this type of battery contains a large amount of heavy metals, if it is discarded into the environment, it will cause great direct and potential harm to the environment. The positive and negative mixed materials of nickel-metal hydride batteries mainly contain nickel, cobalt and rare earth, and the total content of the three is as high as 75-97%, which is very valuable for recycling. At present, the processes for recovering nickel, cobalt and rare earth from the positive and negative mixed materials of nickel-metal hydride batteries mainly include pyrotechnics and wet processes. The products obtained by the fire process are alloy materials, and it is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B3/06C22B7/00
CPCY02P10/20
Inventor 龙炳清王杰才龚婕
Owner SICHUAN NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com