Method for increasing reelability percentage of raw silk

A technology for unwinding rate and raw silk, which is applied in silk reeling, chemical post-processing of fibers, textiles and papermaking, etc., can solve the problem of low unwinding rate of raw silk, and achieve the effect of improving the effect of cocoon cooking.

Active Publication Date: 2014-06-25
SHANGLIN ZHONGXING SILK
View PDF7 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But after adopting the above measures, the unwinding rate of raw silk is still low, so it is necessary to provide a method that can further improve the unwinding rate of raw silk

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Add cocoons and permeate in a mass ratio of 1:10 to the vacuum osmosis device. The permeate is prepared by mixing relaxing agent and distilled water at a mass ratio of 1.5:100. The pH of the permeate is adjusted to 8.0. The temperature of the vacuum infiltration treatment is 40°C and the vacuum degree is 0.08Mpa. The vacuum infiltration device is equipped with an ultrasonic emitting component below the liquid surface of the permeate. During the vacuum infiltration treatment, the ultrasonic transmitting component emits ultrasonic waves to the permeate. The ultrasonic power is 40KHZ, and the ultrasonic power is 800W. The time of vacuum infiltration treatment is 3min; The reliever used is the hydrogen peroxide of 20 weight parts, the polyacrylamide of 5 weight parts, 1 weight part of borax, the isomerism tridecanol polyoxyethylene ether phosphate of 6 weight parts, 2 It is prepared by mixing octylphenol polyoxyethylene ether in parts by weight, polyethylene emulsion finish...

Embodiment 2

[0023] Add cocoons and permeate in the vacuum infiltration device at a mass ratio of 1:15. The permeate is prepared by mixing a relaxing agent and distilled water at a mass ratio of 1.2:100. The pH of the permeate is adjusted to 8.0. The temperature of the vacuum infiltration treatment is 35°C and the vacuum degree is 0.09Mpa. The vacuum infiltration device is equipped with an ultrasonic emitting component below the liquid surface of the permeate. During the vacuum infiltration treatment, the ultrasonic transmitting component emits ultrasonic waves to the permeate. The ultrasonic power is 40KHZ, and the ultrasonic power is 800W. The time of vacuum infiltration treatment is 3min; The reliever used is the hydrogen peroxide of 20 weight parts, the polyacrylamide of 5 weight parts, 1 weight part of borax, the isomerism tridecanol polyoxyethylene ether phosphate of 6 weight parts, 1 It is obtained by mixing and preparing octylphenol polyoxyethylene ether, 3 parts by weight of polye...

Embodiment 3

[0028] Add cocoon and permeate in the vacuum osmosis device according to the mass ratio of 1:13. The permeate is prepared by mixing relaxing agent and distilled water according to the mass ratio of 1.3:100. The pH of the permeate is adjusted to 7.8. The temperature of the vacuum infiltration treatment is 37°C and the vacuum degree is 0.08Mpa. The vacuum infiltration device is equipped with an ultrasonic emitting component below the liquid surface of the permeate. During the vacuum infiltration treatment, the ultrasonic transmitting component emits ultrasonic waves to the permeate. The ultrasonic power is 40KHZ, and the ultrasonic power is 800W. The time of vacuum infiltration treatment is 3.5min; The reliever used is 15 parts by weight of hydrogen peroxide, polyacrylamide of 5.5 parts by weight, 1 part by weight of borax, 6.5 parts by weight of isomerized tridecanol polyoxyethylene ether phosphate, It is prepared by mixing 1.5 parts by weight of octylphenol polyoxyethylene eth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for increasing the reelability percentage of raw silk. The method comprises the steps of conducting vacuum penetrating treatment and upper-trough immersion treatment on silkworm cocoons, wherein vacuum penetrating treatment is completed in a vacuum penetrating device, the cocoons and penetrating fluid of which the mass ratio is 1:10-15 are added to the vacuum penetrating device, the penetrating fluid is prepared by mixing a reelability agent and distilled water of which the mass ratio is 1.2-1.5;100, vacuum penetrating treatment is conducted under the conditions that the temperature is 35 DEG C-40 DEG C and the vacuum degree is 0.08 Mpa-0.09 Mpa, the vacuum penetrating device is provided an ultrasonic emission assembly below the fluid level of the penetrating fluid, the ultrasonic emission assembly emits ultrasonic waves to the penetrating fluid during vacuum penetrating treatment, and time for vacuum penetrating treatment ranges from 3 min to 3.5 min. By the adoption of the method for increasing the reelability percentage of the raw silk, the cocoon cooking effect can be effectively improved, it is measured that the average reelability percentage can reach 77.8% after silk reeling, and the average length of non-broken cocoon filaments can reach 854 m.

Description

technical field [0001] The invention relates to the field of textile production, in particular to a method for improving the unwinding rate of raw silk. Background technique [0002] Silk is obtained by weaving real silk, and real silk is processed by reeling silkworm cocoons and boiling cocoons. The silk reeling and cocoon cooking process mainly includes cocoon mixing, cocoon peeling, cocoon selection, cocoon cooking, silk reeling, reshaking, and finishing. Among them, the cocoon cooking process is to make use of water, heat or chemical additives to make the cocoon silk glue point sericin properly swell and soften, reduce the adhesive force between the cocoon silk, and make the cocoon silk dissociate sequentially to meet the requirements of reeling. silk production requirements. Different cocoon cooking techniques and technical measures are used in silk reeling production, which have a great impact on the quality of reeled silk. Only when cocoons are cooked well can silk ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01B7/04D01C3/00
Inventor 郭秀华
Owner SHANGLIN ZHONGXING SILK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com