Three-dimensional elastic rotating color changing fiber and spinneret plate thereof

A three-dimensional, spinneret technology, applied in fiber processing, filament/thread forming, conjugated synthetic polymer artificial filament, etc., can solve problems such as unsmooth spinning, spinneret angle, and two-component cracking And other problems, to achieve the effect of improving moisture absorption and perspiration function, good visual effect, and good color rotation effect

Active Publication Date: 2014-07-16
TAICANG RONGWEN SYNTHETIC FIBER
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, in the spinning process, the two-component high polymer often has a "bend angle" problem at the spinneret due to different viscosities during the spinning process and cannot be spun smoothly, or the two components are cracked

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Three-dimensional elastic rotating color changing fiber and spinneret plate thereof
  • Three-dimensional elastic rotating color changing fiber and spinneret plate thereof
  • Three-dimensional elastic rotating color changing fiber and spinneret plate thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0027] 1. Raw materials and their specific indicators:

[0028] ECDP chips: intrinsic viscosity 0.58dl / g, melting point 240°C

[0029] PET chips: intrinsic viscosity 0.87dl / g, melting point 265°C

[0030] 2. Spinning process conditions:

[0031] The ECDP slices with an intrinsic viscosity of 0.58dl / g were vacuum-dried at 100°C for 8 hours, and the PET slices with an intrinsic viscosity of 0.87dl / g were dried; the two slices were sent to a twin-screw extruder for melt extrusion, The melts of the two components use two sets of metering pumps respectively, enter the composite spinning assembly through the melt pipe, and are sprayed out from the spinneret; into, spinneret micropores such as figure 1 As shown, the diameter of the circular hole is 0.34mm; the channel center height of the connecting section is 0.02mm, and the length of the connecting section is 0.04mm. The arrangement of the spinneret microholes is as follows: image 3 shown. The spinning temperature ECDP is 28...

example 2

[0034] Take the preparation of side-by-side composite ECDP / PET side-by-side composite fibers as an example.

[0035] 1. Raw materials and their specific indicators:

[0036] ECDP chips: intrinsic viscosity 0.51dl / g, melting point 238°C

[0037] PET chips: intrinsic viscosity 0.72dl / g, melting point 262°C

[0038] 2. Spinning process conditions:

[0039] The ECDP chips with an intrinsic viscosity of 0.51dl / g were vacuum-dried at 100°C for 15 hours, and the PET chips with an intrinsic viscosity of 0.72dl / g were dried; the two kinds of chips were sent to a twin-screw extruder for melt extrusion, The melts of the two components use two sets of metering pumps respectively, enter the composite spinning assembly through the melt pipeline, and are sprayed out from the spinneret; the spinneret micropores of the spinneret are formed by connecting two identical ellipses through the connecting section , spinneret micropores such as figure 2As shown, the long diameter of the elliptica...

example 3

[0042] Take the preparation of side-by-side composite ECDP / PET side-by-side composite fibers as an example.

[0043] 1. Raw materials and their specific indicators:

[0044] ECDP chips: intrinsic viscosity 0.55dl / g, melting point 240°C

[0045] PET chips: intrinsic viscosity 0.80dl / g, melting point 265°C

[0046] 2. Spinning process conditions:

[0047] The ECDP chips with an intrinsic viscosity of 0.55dl / g were vacuum-dried at 100°C for 10 hours, and the PET chips with an intrinsic viscosity of 0.80dl / g were dried; the two kinds of chips were sent to a twin-screw extruder for melt extrusion, The melts of the two components use two sets of metering pumps respectively, enter the composite spinning assembly through the melt pipe, and are sprayed out from the spinneret; into, spinneret micropores such as figure 1 As shown, the diameter of the circular hole is 0.40mm; the channel center height of the connecting section is 0.03mm, and the length of the connecting section is 0.0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Lengthaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a three-dimensional elastic rotating color changing fiber and a spinneret plate for manufacturing the three-dimensional elastic rotating color changing fiber. The specific rotating color changing effect of the three-dimensional elastic rotating color changing fiber is ensured through the dye-uptake difference between two components of the three-dimensional elastic rotating color changing fiber and a three-dimensional spiral crimp structure of a parallel composite fiber. The three-dimensional elastic rotating color changing fiber and the spinneret plate are characterized in that each micropore of the spinneret plate for producing the three-dimensional elastic rotating color changing fiber is shaped like the Arabic numeral eight; a composite spinning assembly and a specially-shaped spinneret assembly are adopted; moisture absorption and sweat releasing performance of the three-dimensional elastic rotating color changing fiber can be improved due to grooves in the surface of the three-dimensional elastic rotating color changing fiber. The three-dimensional elastic rotating color changing fiber has the stable crimp resilience and is simple in manufacturing process, the elastic range of the three-dimensional elastic rotating color changing fiber can be adjusted according to the heat treatment technology, and the three-dimensional elastic rotating color changing fiber can be widely applied to sports wear, underwear, woven tapes and the like.

Description

technical field [0001] The invention relates to a three-dimensional elastic color-spinning fiber and a spinneret for manufacturing the three-dimensional elastic color-spinning fiber. Background technique [0002] With DuPont launching large-scale production of Lycra (Lycra) products, elastic fiber has attracted widespread attention. It is called spandex in China. The elongation of polyurethane elastic fiber is very large, and its strength and aging resistance are better than rubber. Silk, get people's favor. However, due to the complex production equipment and process of polyurethane elastic fiber, the high cost of raw materials and processing, and serious pollution, its application is greatly restricted. [0003] Side-by-side composite fibers use two polymer materials with different shrinkage properties to produce side-by-side structure fibers. This is a type of curly elastic fiber made of two polymers with different structures or properties through bi-component composite ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01D5/28D01D5/253D01F8/14
Inventor 史原王朝生郁铭芳李夏全潇陶景良苏立平肖庆浦雪强金志明朗俊逸
Owner TAICANG RONGWEN SYNTHETIC FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap