Rubber glove with antimicrobial and skin care functions

A technology of rubber gloves and efficacy, applied in the field of surgical gloves, can solve problems such as adverse reactions of human skin, user skin allergies, and increased hand sweating, so as to avoid allergic problems, avoid poor stretch performance, and avoid allergies. effect of symptoms

Inactive Publication Date: 2014-08-13
GUILIN HBM HEALTHCARES
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Powdered gloves usually use talcum powder or modified starch as a release agent to lubricate the surface of the glove, but talc powder is likely to cause skin allergies to users, and even cause adverse reactions to human skin. Modified starch contains more protein components , can also cause skin adverse reactions after being absorbed by human skin
On the other hand, after wearing natural latex gloves or nitrile latex gloves for a long time, the amount of sweating in the hands will increase significantly, which is not only conducive to the proliferation of certain bacteria, viruses, and fungi on the surface of the hand, damaging the health of the user, but also will produce peculiar smell

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber glove with antimicrobial and skin care functions
  • Rubber glove with antimicrobial and skin care functions
  • Rubber glove with antimicrobial and skin care functions

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A rubber glove with antibacterial and skin care effects, wherein the rubber latex is composed of the following components, by weight:

[0026]

[0027] The antibacterial and skin care active ingredients are composed of cinnamon extract and houttuynia cordata extract, and the weight ratio is 1:2.

[0028] The preparation method is as follows:

[0029] A. To formulate rubber latex for dipping, mix natural rubber, emulsified liquid paraffin, colloidal sulfur, zinc oxide, accelerator ZDBC, accelerator ZMBT, antibacterial and skin care active ingredients, and mix them evenly and adjust the solid content to 25-32%;

[0030] B. After the mold is dried, first impregnate the coagulant, which is 15% by weight calcium nitrate or calcium chloride solution;

[0031] C. Dry the mold, and then immerse the mold with the rubber latex prepared above, then crimp it, then immerse it in warm water at 45°C for 2 minutes, take it out, and dry it at a high temperature of 140°C for 20 minutes;

[0032] D....

Embodiment 2

[0034] A rubber glove with antibacterial and skin care effects, wherein the rubber latex is composed of the following components, by weight:

[0035]

[0036] The antibacterial and skin care active ingredients are composed of cinnamon extract and houttuynia cordata extract, and the weight ratio is 3:4.

[0037] The preparation method is as follows:

[0038] A. To prepare rubber latex for dipping, mix natural rubber, emulsified liquid paraffin, colloidal sulfur, zinc oxide, accelerator ZDBC, accelerator ZMBT, antibacterial and skin care active ingredients, and mix them evenly and adjust the solid content to 32%;

[0039] B. After the mold is dried, first impregnate the coagulant, which is 8% by weight calcium nitrate or calcium chloride solution;

[0040] C. Dry the mold, and then immerse the mold with the rubber latex prepared above, then crimp it, then immerse it in warm water at 45°C for 2 minutes, take it out, and dry it at a high temperature of 120°C for 40 minutes;

[0041] D. Cool,...

Embodiment 3

[0043] A rubber glove with antibacterial and skin care effects, wherein the rubber latex is composed of the following ingredients, preferably, by weight:

[0044]

[0045] The antibacterial and skin care active ingredients are composed of cinnamon extract and houttuynia cordata extract, with a weight ratio of 2:3.

[0046] The preparation method is as follows:

[0047] A. To prepare rubber latex for dipping, mix natural rubber, emulsified liquid paraffin, colloidal sulfur, zinc oxide, accelerant ZDBC, accelerant ZMBT, antibacterial and skin care active ingredients, and mix them evenly and adjust the solid content to 28%;

[0048] B. After the mold is dried, first impregnate the coagulant, which is a 10% by weight calcium nitrate or calcium chloride solution;

[0049] C. Dry the mold, and then immerse the mold with the rubber latex prepared above, then crimp it, then immerse it in warm water at 45°C for 2 minutes, take it out, and dry it at a high temperature of 130°C for 30 minutes;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber glove with antimicrobial and skin care functions, which comprises a rubber latex and an antimicrobial and skin care active component. The rubber glove is characterized in that the rubber latex is composed of the following components in parts by weight: 70-80 parts of natural rubber, 20-30 parts of nitrile-butadiene rubber, 5-8 parts of emulsified liquid paraffin, 0.6-1.2 parts of colloid sulfur, 0.4-1.0 part of zinc oxide, 0.2-0.4 part of accelerator ZDBC, 0.3-0.5 part of accelerator ZMBT and 0.7-1.5 parts of antimicrobial and skin care active component. The antimicrobial and skin care active component is composed of a cinnamon extract and a herba houttuyniae extract in a weight ratio of (1-3):(2-4). The antimicrobial and skin care active component is added into the matrix of the operating glove, so that the antimicrobial and skin care active component can resist microbes and enhance the safety performance of the operating glove when in use.

Description

Technical field [0001] The invention relates to surgical gloves, in particular to a rubber glove with antibacterial and skin care effects. Background technique [0002] Gloves have a barrier protection function and can well protect the safety of users, and they have been widely used in people's production and life. According to different uses, it can be divided into medical gloves, industrial gloves and household gloves; according to the different materials used in production, it can be divided into natural rubber gloves, nitrile gloves, PVC gloves, and so on. [0003] At present, natural latex gloves and nitrile latex gloves are usually divided into powder type and powder-free type. In order to lubricate the surface of the glove, powdered gloves usually use talc powder or modified starch as a release agent. However, talc powder can easily cause skin allergies and even cause adverse reactions to human skin. Modified starch contains more protein ingredients , It can also cause adv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/02C08K13/02C08K3/06C08K3/22C08K5/098C08K5/39C08K5/47A61B19/04
Inventor 胡智强
Owner GUILIN HBM HEALTHCARES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com