Preparation method of carbon material high-temperature oxidation-resistant coating by coating and sintering

A high-temperature anti-oxidation and carbonaceous material technology, which is applied in the field of inorganic coating materials for oxidation protection of carbon materials, can solve complex procedures, poor uniformity and composition controllability of anti-oxidation coatings, and poor interlayer bonding within the coating and other problems, to achieve the effect of reducing the preparation process, shortening the preparation cycle, and strong binding force

Active Publication Date: 2014-12-10
AEROSPACE RES INST OF MATERIAL & PROCESSING TECH +1
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a coating and sintering preparation method of high-temperature (temperature above 1500°C) anti-oxidation coating for carbonaceous materials, which adopts the coating and sintering method to prepare SiC/SiC-MoSi of carbonaceous materials 2 The anti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] Example 1

[0024] The coating and sintering preparation method of a carbonaceous material high-temperature anti-oxidation coating of the present invention has a density of 1.9g / cm 3 The carbon / carbon composite material is the base material. After the surface is cleaned, it is dried for later use; it includes the following steps:

[0025] (1) Brush slurry I on the surface of the cleaned carbon / carbon composite material; the slurry I includes silicone resin and Si powder, and the mass ratio of silicone resin and Si powder is 1:1. Brush the surface of the carbon / carbon composite material with 1mm thick slurry I, and dry it in a drying oven at 120°C for 1 hour.

[0026] (2) Then continue to brush slurry II on the surface of the carbon / carbon composite material of the brush slurry I obtained in step (1); the slurry II includes silicone resin, Si powder and Mo powder, silicone resin: Si The mass ratio of powder: Mo powder is 3:3:2. Brush the reaction slurry II with a thickness of...

Example Embodiment

[0032] Example 2

[0033] The coating and sintering preparation method of a high-temperature anti-oxidation coating of carbonaceous material according to the present invention has a density of 1.7g / cm 3 The high-strength graphite is the base material. After the surface is cleaned, it is dried for later use; it includes the following steps:

[0034] (1) Brush slurry I on the cleaned graphite surface; said slurry I includes phenolic resin and Si powder, and the mass ratio of phenolic resin and Si powder is 1:2. Brush slurry I on the surface of the graphite material and dry it in a drying oven at 120°C for 1 hour. The slurry I finally generates a SiC base layer.

[0035] (2) Then continue to brush slurry II on the graphite material surface of the brush slurry I obtained in step (1); the slurry II includes phenolic resin, Si powder and Mo powder, phenolic resin: Si powder: Mo The mass ratio of powder is 3:5:1.5. Brush the reaction slurry II on the surface of the graphite material, and...

Example Embodiment

[0041] Example 3

[0042] The coating and sintering preparation method of a carbonaceous material high-temperature anti-oxidation coating of the present invention has a density of 1.9g / cm 3 The carbon / carbon composite material is the base material. After the surface is cleaned, it is dried for later use; it includes the following steps:

[0043] (1) Brush the slurry I on the surface of the cleaned carbon / carbon composite material; the slurry I includes phenolic resin and Si powder, and the mass ratio of phenolic resin and Si powder is 1:1.

[0044] (2) Then continue to brush slurry II on the surface of the carbon / carbon composite material of the brushing slurry I obtained in step (1); the slurry II includes phenolic resin, Si powder and Mo powder, phenolic resin: Si The mass ratio of powder: Mo powder is 3:5:2.

[0045] (3) Carry out high-temperature sintering of the carbon / carbon composite material of the brushed slurry I and slurry II obtained in step (2) at 1800°C for 2 hours, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Weight loss rateaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of a carbon material high-temperature oxidation-resistant coating by coating and sintering. The method comprises the following steps: (1) brushing a slurry I on a cleaned carbon material surface; (2) continuing brushing a slurry II on the carbon material surface brushed with the slurry I in the step (1); (3) carrying out high-temperature sintering on the carbon material brushed with the slurry I and slurry II at 1300-1800 DEG C for 2-3 hours, and naturally cooling to room temperature; (4) repeating the brushing and sintering in the step (1) to step (3) 1-3 times; (5) carrying out seal treatment on the coating surface of the carbon material obtained in the step (4) by using ethyl orthosilicate; and (6) repeating the ethyl orthosilicate brushing and drying in the step (5) 1-4 times to obtain a seal layer on the coating surface of the carbon material. The method is simple to operate, has the advantages of short preparation period and high material utilization ratio, and can obviously lower the coating preparation cost.

Description

technical field [0001] The invention belongs to the field of inorganic coating materials for oxidation protection of carbon materials, and in particular relates to a coating and sintering preparation method of a high-temperature anti-oxidation coating of carbon materials. Background technique [0002] Carbon materials have excellent high-temperature mechanical properties and good thermal shock resistance, and are widely used in aerospace and other fields. However, carbon materials begin to undergo significant oxidation reactions in an oxidizing environment above 500 °C, and their properties are fatally damaged. Coating an anti-oxidation coating on the surface of carbon materials is the main method to solve the oxidation of carbon materials at high temperatures (especially above 1200 °C). [0003] Carbonaceous material anti-oxidation coating SiC / SiC-MoSi 2 The system has good anti-oxidation properties, the reason is that SiC and carbonaceous materials have good chemical and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/89
Inventor 吴宁宁李同起张中伟焦星剑李钰梅刘风亮张震俸翔
Owner AEROSPACE RES INST OF MATERIAL & PROCESSING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap