nzfo-bto type ferromagnetic electroceramic composite nanofiber microwave absorber, absorbing coating and preparation method

A technology of composite nanofibers and microwave absorbers, applied in the direction of coatings, artificial filaments made of inorganic materials, etc., can solve the problems of difficult large-scale production, complex process, cumbersome operation, etc., and achieve short preparation cycle, simple process, The effect of easy operation

Active Publication Date: 2016-06-08
JIANGSU UNIV OF SCI & TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Purpose of the invention: for above-mentioned existing problems and deficiencies, a kind of chemical composition of the present invention is ( n ) Ni x Zn 1-x Fe 2 o 4 / (1- n ) BaTiO 3 (0≤ x ≤1,0n <100mol%), a ferromagnetic / ferroelectric ceramic composite nanofiber microwave absorber with excellent wave-absorbing properties and a preparation method thereof, to solve the application blank of the magnetoelectric ceramic composite nanofiber in the field of electromagnetic wave absorption, and the existing problems of the existing preparation technology Technical problems such as complex process, cumbersome operation, high cost, and difficulty in large-scale production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • nzfo-bto type ferromagnetic electroceramic composite nanofiber microwave absorber, absorbing coating and preparation method
  • nzfo-bto type ferromagnetic electroceramic composite nanofiber microwave absorber, absorbing coating and preparation method
  • nzfo-bto type ferromagnetic electroceramic composite nanofiber microwave absorber, absorbing coating and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] According to the ferromagnetic phase Ni 0.5 Zn 0.5 Fe 2 o 4 with ferroelectric BaTiO 3 The molar ratio is 7:3, respectively weigh 0.3659g tetrabutyl titanate, 0.2746 barium acetate, 0.3121 nickel acetate, 0.2753g zinc acetate, 1.7720g iron acetylacetonate and add them to the mixture consisting of 10.7800g acetic acid and 4.6200g ethanol In the solvent (the mass ratio of ethanol to acetic acid is about 0.43), stir magnetically at room temperature until all metal salts are completely dissolved, then weigh 1.6000g polyvinylpyrrolidone (PVP, with an average molecular weight of 1300000) and add it to the above solution, continue Magnetic stirring for about 2 hours forms a homogeneous, transparent and stable spinning precursor solution, wherein the mass percentage of PVP is 8%, and the mass percentage of all metal salts is 15%. The prepared spinning solution is moved into the electrospinning device (Chinese patent 201110201848.7) composed of a DC high-voltage power supply...

Embodiment 2

[0022] Basic process is the same as embodiment 1, and difference is: Ni 0.5 Zn 0.5 Fe 2 o 4 with BaTiO 3 The molar ratio is 5:5, the masses of tetrabutyl titanate, barium acetate, nickel acetate, zinc acetate and iron acetylacetonate are 0.6646g, 0.4988g, 0.2430g, 0.2143g and 1.3793g respectively, and the chemical composition is (50mol% ) Ni 0.5 Zn 0.5 Fe 2 o 4 / (50mol%)BaTiO 3 The ferromagnetic / ferroelectric composite nanofiber microwave absorber has an average diameter of about 220nm, and the ferromagnetic phase Ni 0.5 Zn 0.5 Fe 2 o 4 The average grain size is 45nm, the ferroelectric phase BaTiO 3 The average grain size is 50nm; when the absorber loading is 60% and the coating thickness is 4.0mm, the monolayer (50mol%) Ni 0.5 Zn 0.5 Fe 2 o 4 / (50mol%)BaTiO 3 - The minimum reflectivity of the silicone absorbing coating reaches –28dB at 6.3GHz.

Embodiment 3

[0024] Basic process is the same as embodiment 1, and difference is: Ni 0.5 Zn 0.5 Fe 2 o 4 with BaTiO 3 The molar ratio is 9:1, the masses of tetrabutyl titanate, barium acetate, nickel acetate, zinc acetate and iron acetylacetonate are 0.1127g, 0.0846g, 0.3708g, 0.3271g and 2.1049g respectively, and the chemical composition is (90mol% ) Ni 0.5 Zn 0.5 Fe 2 o 4 / (10mol%)BaTiO 3 The ferromagnetic / ferroelectric composite nanofiber microwave absorber has an average diameter of about 260nm, and the ferromagnetic phase Ni 0.5 Zn 0.5 Fe 2 o 4 The average grain size is 43nm, the ferroelectric phase BaTiO 3 The average grain size is 20nm; when the absorber loading is 60% and the coating thickness is 4.5mm, the monolayer (90mol%) Ni 0.5 Zn 0.5 Fe 2 o 4 / (10mol%)BaTiO 3 - The minimum reflectivity of the silicone absorbing coating reaches –26dB at 7.6GHz.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a NZFO-BTO type ferromagnetic electroceramic composite nanofiber microwave absorber, a wave-absorbing coating and a preparation method. BaTiO 3 Composed of nanocrystals, Ni x Zn 1-x Fe 2 o 4 The average grain size of BaTiO is 20-50nm. 3 The average grain size of the fiber is 20-70nm, the two-phase grains are evenly distributed along the fiber axis, and the fiber diameter is about 100-300nm. The magnetoelectric composite nanofiber prepared by the present invention has strong absorption almost in the entire 2-18 GHz frequency band, and has the advantages of wide frequency band, strong absorption, low cost, and wide range control of electromagnetic parameters and microwave absorption characteristics. It has good application prospects in shielding, anti-electromagnetic interference and pollution.

Description

technical field [0001] The invention belongs to the field of electromagnetic wave absorbing materials, in particular to a ferromagnetic / ferroelectric composite absorbing material with a one-dimensional nanostructure and a preparation method thereof, specifically Ni-Zn ferrite / BaTiO 3 Composite nanofiber microwave absorber and its preparation technology. Background technique [0002] With the rapid development and wide application of electronic and communication equipment using GHz frequency electromagnetic waves, the resulting electromagnetic interference and electromagnetic radiation pollution are becoming more and more serious. At the same time, the demand for electromagnetic stealth in modern weapons and equipment is also increasing. In order to eliminate or reduce electromagnetic interference and electromagnetic pollution, and effectively reduce the radar signature of weapons and equipment to improve their survivability and defense capabilities and overall combat perform...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F9/08C09D7/12C04B35/26C04B35/468
Inventor 向军李佳乐叶芹刘敏徐加焕
Owner JIANGSU UNIV OF SCI & TECH