A kind of odor-removing putty paste for indoor board joints and its preparation method

A putty paste, odor technology, applied in the direction of filling slurry, etc., can solve problems such as inability to solve, and achieve the effect of long-term efficacy

Inactive Publication Date: 2017-03-01
长春坤翔环保技术有限公司 +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] But above-mentioned technical scheme can not solve the technical problem of harmful gas such as formaldehyde released from exposed sections such as interior decoration floors, MDF boards and bare surfaces

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of odor-removing putty paste for indoor board joints and its preparation method
  • A kind of odor-removing putty paste for indoor board joints and its preparation method
  • A kind of odor-removing putty paste for indoor board joints and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] Embodiment 1: A kind of preparation method of indoor board joint deodorization putty paste can be implemented according to the following method:

[0055] Glue making: First add 143 kg of purified tap water to the rubber making reaction tank, preheat to 50°C, then mix 2 kg of konjac gum, 2 kg of seaweed gum, and 4 kg of guar gum according to their weight fractions and then stir Add it to the reaction tank, disperse and swell until a uniform colloid is formed;

[0056] Premixing: Put 186 kg of purified tap water in a stirring tank, add 3 kg of dispersant sodium hexametaphosphate under stirring, and disperse and stir for 30 minutes. Weigh 0.2 kg of colloid-doped silver nano-titanium dioxide with a solid content of 15%, and 0.8 kg of colloidal nano-zinc oxide with a solid content of 20%, pre-mix them into 1 kg, and add them to the dispersion under stirring; 150 kg of diatomite, 100 kg of attapulgite, 100 kg of sepiolite, 300 kg of heavy calcium carbonate, and 650 kg of ful...

Embodiment 2

[0058] Embodiment 2: A kind of preparation method of indoor panel joint deodorization putty paste can also be implemented according to the following method:

[0059] Glue making: First add 143 kg of purified tap water to the rubber making reaction tank, preheat to 50°C, then mix 2 kg of konjac gum, 2 kg of seaweed gum, and 4 kg of guar gum according to their weight fractions and then stir Add it to the reaction tank, disperse and swell until a uniform colloid is formed;

[0060] Premixing: Put 188 kg of purified tap water in a stirring tank, add 3 kg of dispersant sodium hexametaphosphate under stirring, and disperse and stir for 30 minutes. Weigh 0.6 kg of colloid-doped silver nano-titanium dioxide with a solid content of 15%, and 2.4 kg of colloidal nano-zinc oxide with a solid content of 20%, pre-mixed into 3 kg, and add it to the dispersion under stirring; 100 kg of diatomite, 150 kg of attapulgite, 150 kg of sepiolite, 250 kg of heavy calcium carbonate, and 650 kg of ful...

Embodiment 3

[0062] Embodiment 3: A kind of preparation method of indoor board joint deodorizing putty paste for indoor board joints can also be implemented according to the following method:

[0063] Glue making: First add 143 kg of purified tap water to the rubber making reaction tank, preheat to 50°C, then mix 2 kg of konjac gum, 2 kg of seaweed gum, and 4 kg of guar gum according to their weight fractions and then stir Add it to the reaction tank, disperse and swell until a uniform colloid is formed;

[0064] Premixing: Put 190 kg of purified tap water in a stirring tank, add 3 kg of dispersant sodium hexametaphosphate under stirring, and disperse and stir for 30 minutes. Weigh 1 kg of colloid-doped silver nano-titanium dioxide with a solid content of 15%, 4 kg of colloidal nano-zinc oxide with a solid content of 20%, pre-mix them into 5 kg, and add them to the dispersion under stirring; put them in the V-type powder machine 100 kg of diatomite, 150 kg of attapulgite, 150 kg of sepiol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
voidageaaaaaaaaaa
Login to View More

Abstract

Peculiar-smell-removing putty paste for indoor plate seaming and a manufacturing method thereof are disclosed. The putty paste and the method are characterized in that: the putty paste comprises natural inorganic compounds, a colloid nanometer mixture, an ecological adhesive, a dispersing agent, a defoaming agent and water; and the putty paste comprises 55-80% by mass of the natural inorganic compounds, 1-10% by mass of the colloid nanometer mixture, 3-10% by mass of the ecological adhesive, 1-5% by mass of the dispersing agent, 1-3% by mass of the defoaming agent and 10-60% by mass of the water. The putty paste and the method are advantageous in that: harmful gas adsorption functions of diatomite, attapulgite and sepiolite are fully utilized; a nanometer material capable of degrading harmful gases under conditions of visible light is added into the absorption materials; and the efficacy of removing peculiar smell of the putty paste is longer.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a putty and a preparation method thereof. Background technique [0002] With the development of the economy, the continuous improvement of living standards and the renewal of aesthetic concepts, it has become a new fashion to gradually pursue high-end decoration in entertainment, living, and office rooms. Especially in recent years, urban and rural transformation and the rapid rise of the real estate industry have led to the general development of decoration materials production. As a result, the decoration of new houses has become more complex and upscale, the old houses have also been renovated and redecorated, and public places are more complex in design and luxurious in decoration. The consumption trend of social and economic development is becoming more and more fierce. Due to the release of harmful gases such as decoration materials, paint coatings, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 李波
Owner 长春坤翔环保技术有限公司