Fireproof manmade quartz stone slab with superhardness and manufacturing method of fireproof manmade quartz stone slab

A technology of artificial quartz stone and quartz stone plate, which is applied in the field of building materials manufacturing, can solve the problems of restricting the application of artificial quartz stone, poor fire performance, poor wear resistance, etc., and achieve the goal of improving hardness, simple manufacturing method, and broad market prospects Effect

Inactive Publication Date: 2015-04-22
田忠和
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the artificial quartz stone plates currently on the market have relatively low hardness, poor wear resistance, and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Weigh 30kg of calcined quartz stone of 6-80 mesh, 60kg of quartz powder of 325 mesh, 5kg of cullet, 20kg of red silica powder of 50-100 mesh, 5kg of sillimanite powder of 100-150 mesh, 10kg of zirconium silicate powder of 100-200 mesh, Oxygen resin 5kg, 0.5kg of γ-methacryloxypropyltrimethoxysilane (KH570) and peroxy-2-ethylhexanoic acid tert-butyl mixture that the weight ratio is 4:1, pigment 0.3kg, The pigment is composed of titanium dioxide and blue water according to the mass ratio of 18:1; the above-mentioned components are evenly mixed, and the mixed material is evenly spread on the plate making mold, and then the plate making mold is sent into the forming press, When the air pressure reaches -0.1MPa during vacuuming, vibrate at a pressure of 2.5-3.5MPa for 2-3 minutes to form, and then send it to a curing furnace for curing. The curing temperature is 90-95°C and the time is 30-40 minutes. "Man-made quartz stone plate.

Embodiment 2

[0023] Weigh 80kg of calcined quartz stone of 6-80 mesh, 30kg of 325-mesh quartz powder, 10kg of cullet, 10kg of 50-100 mesh leucoporite powder, 15kg of 100-150 mesh kyanite powder, 1kg of 100-200 mesh yttrium-stabilized zirconia powder, phenolic 10kg of resin, 0.3kg of γ-aminopropyltriethoxysilane (KH550) and peroxy-2-ethylhexanoic acid tert-butyl mixture in a weight ratio of 4:1, 0.8kg of pigment, said pigment is made of titanium White powder, iron yellow powder, iron black powder, phenolphthalein blue powder and blue water are composed according to the mass ratio of 312:6:25:1:28; the above components are evenly mixed, and the mixed materials are evenly spread on the plate making mold , and then send the plate mold into the forming press, when the air pressure reaches -0.1MPa during vacuuming, vibrate for 2-3 minutes under the pressure of 2.5-3.5MPa to form, and then send it to the curing furnace for curing. The curing temperature is 90-95°C, and the time is It takes 30 to ...

Embodiment 3

[0025] Weigh 65kg of calcined quartz stone of 6-80 mesh, 45kg of quartz powder of 325 mesh, 8kg of cullet, 12kg of white foam stone powder of 50-100 mesh, 8kg of andalusite powder of 100-150 mesh, 5kg of zirconium silicate powder of 100-200 mesh, polyurethane resin 8kg, 0.4kg of γ-glycidyl etheroxypropyltrimethoxysilane and peroxy-2-ethylhexanoic acid tert-butyl ester mixture that the weight ratio is 4:1, 0.5kg of pigment, described pigment is made of titanium dioxide, Zhongluo yellow powder, iron black powder, chrome green powder and blue water are composed according to the mass ratio of 300:30:1:2:27; the above-mentioned components are evenly mixed, and the mixed materials are evenly spread on the plate making mold, Then send the plate making mold into the molding press, when the air pressure reaches -0.1MPa during vacuuming, vibrate for 2-3 minutes under the pressure of 2.5-3.5MPa to form, and then send it to the curing furnace for curing. The curing temperature is 90-95 ° C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fireproof manmade quartz stone slab with superhardness and a manufacturing method of the fireproof manmade quartz stone slab. The manmade quartz stone slab is manufactured from the following components in parts by weight: 30-80 parts of 6-80-mesh calcined quartz stones, 30-60 parts of 325-mesh quartz powder, 5-10 parts of cullet, 10-20 parts of 50-100-mesh red-silica powder or quartzitic sandstone powder, 5-15 parts of 100-150-mesh kyanite powder or andalusite powder or sillimanite powder, 1-10 parts of 100-200-mesh zirconium silicate or yttria-stabilized zirconia powder, 5-10 parts of unsaturated resins, 0.3-0.5 part of auxiliary, and 0.3-0.8 part of pigment. According to the fireproof manmade quartz stone slab, the red-silica powder, quartzitic sandstone powder, kyanite powder or andalusite powder or sillimanite powder, and zirconium silicate or yttria-stabilized zirconia powder is added in a manufacturing process, so that the compressive property and the fireproof flame retardant performance of the manmade quartz stone slab are improved; meanwhile, by using the calcined quartz stones, the hardness of the manmade quartz stone slab is improved, so that the fireproof manmade quartz stone slab with superhardness is relatively wearproof, difficult to scratch and long in service life.

Description

technical field [0001] The invention belongs to the technical field of building material manufacturing, in particular to a fireproof, superhard artificial quartz stone plate and a manufacturing method thereof. Background technique [0002] Compared with artificial marble slabs, artificial quartz stone slabs have the characteristics of high curvature, high compressive strength, high Mohs hardness, and low water absorption. They are gradually favored by users at home and abroad, and are widely used in cabinets, bathrooms, offices and The floor, wall decoration and home furnishing industry of large shopping malls. However, the artificial quartz stone plates currently on the market have relatively low hardness, poor wear resistance, and poor fire resistance, which limit the application of artificial quartz stone in a wider range and need to be solved urgently. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a fire-p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/14C04B26/12C04B26/16C04B14/06C04B14/04
Inventor 田忠和
Owner 田忠和
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap