A kind of ultra-high-strength, high-toughness, high-corrosion-resistant cunisinbsn elastic copper alloy and preparation method thereof

An elastic copper alloy and high corrosion resistance technology, which is applied in the field of ultra-high strength, high toughness, high corrosion resistance CuNiSiNbSn elastic copper alloy and its preparation, CuNiSiNbSn elastic copper alloy and its preparation field, can solve the lack of industrialization preparation process and restrict electrical appliances Industrial development, low alloy elongation and other problems, to achieve the effect of good corrosion resistance, high strength and excellent electrical conductivity

Inactive Publication Date: 2016-08-17
CENT SOUTH UNIV +1
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The non-vacuum secondary remelting mentioned in it will bring huge energy consumption in the process of industrial production
(2) The preparation method described in the patent "A preparation method of ultra-high strength and high stress relaxation resistance CuNiSiAl elastic copper alloy" (ZL201010571290.7) makes the prepared alloy have good comprehensive properties, but the elongation of the alloy The rate is low, and there is no description of the industrial preparation process
(3) The composition and preparation process described in the patent "A CuNiSi-based Elastic Copper Alloy and Its Preparation Method" (CN201310025570.1) make the prepared alloy have excellent properties, but there are also low elongation and Lack of description of industrial preparation process
Due to the existing elastic copper alloy composition and / or preparation process, the existing elastic copper alloy cannot have high strength and excellent corrosion resistance and plastic toughness that meets the requirements, which seriously restricts the new generation of electrical appliances. industrial development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultra-high-strength, high-toughness, high-corrosion-resistant cunisinbsn elastic copper alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] According to the components corresponding to Example 1 in Table 1, prepare according to the technical process described in Example 1, and each condition parameter in the preparation process is shown in Table 1. Each condition parameter corresponding to Example 1;

[0065] The specific operation process is as follows:

[0066] Step 1 Melting and Casting

[0067] Select electrolytic copper, electrolytic nickel (nickel source), elemental silicon (silicon source), elemental niobium (niobium source), electrolytic tin (tin source), copper-magnesium master alloy (magnesium source), and copper-magnesium alloy according to the designed alloy composition. After the chromium master alloy (chromium source), the prepared electrolytic copper is first added to the intermediate frequency induction melting furnace, and the temperature is raised to 1300-1320 °C, and then the prepared electrolytic nickel, elemental silicon, elemental niobium, electrolytic tin, copper- Chromium master all...

Embodiment 2

[0087] According to the components corresponding to Example 2 in Table 1, prepare according to the technical process described in Example 2, and each condition parameter in the preparation process is shown in Table 1. Each condition parameter corresponding to Example 2;

[0088] The specific operation process is as follows:

[0089] Step 1 Melting and Casting

[0090]Select electrolytic copper, electrolytic nickel (nickel source), elemental silicon (silicon source), elemental niobium (niobium source), electrolytic tin (tin source), copper-magnesium master alloy (magnesium source), and copper-magnesium alloy according to the designed alloy composition. After the chromium master alloy (chromium source), the prepared electrolytic copper is first added to the intermediate frequency induction melting furnace, and the temperature is raised to 1300-1320 °C, and then the prepared electrolytic nickel, elemental silicon, elemental niobium, electrolytic tin, copper- Chromium master allo...

Embodiment 3

[0110] According to the components corresponding to Example 3 in Table 1, prepare according to the technical process described in Example 3, and each condition parameter in the preparation process is shown in Table 1. Each condition parameter corresponding to Example 3;

[0111] The specific operation process is as follows:

[0112] Step 1 Melting and Casting

[0113] Select electrolytic copper, electrolytic nickel (nickel source), elemental silicon (silicon source), elemental niobium (niobium source), electrolytic tin (tin source), copper-magnesium master alloy (magnesium source), and copper-magnesium alloy according to the designed alloy composition. After the chromium master alloy (chromium source), the prepared electrolytic copper is first added to the intermediate frequency induction melting furnace, and the temperature is raised to 1310-1330 °C, and then the prepared electrolytic nickel, elemental silicon, elemental niobium, electrolytic tin, copper- Chromium master all...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to an ultrahigh-strength high-toughness high corrosion-resisting CuNiSiNbSn elastic copper alloy and a preparation method thereof, and belongs to the technical field of elastic alloy preparation. The ultrahigh-strength high-toughness high corrosion-resisting CuNiSiNbSn elastic copper alloy is prepared from the following components in percentage by mass: 6.0-7.5% of Ni, 1.0-1.4% of Si, 0.8-1.2% of Nb, 0.5-0.8% of Sn, 0.1-0.15% of Mg, 0.1-0.15% of Cr and the balance of Cu and inevitable impurities. The alloy preparation process comprises the following steps: smelting, performing semicontinuous casting, uniformly annealing, carrying out hot rolling, carrying out cold rolling, performing solid solution, performing combined aging (pre-aging treatment, cold-rolling and aging treatment), performing finish rolling, and annealing at low temperature. The ultrahigh-strength high-toughness high corrosion-resisting CuNiSiNbSn elastic copper alloy can meet requirements of various conductive elastic devices and is applicable to ultrahigh-strength high-toughness high corrosion-resisting conductive elastic devices requested in the electronic industry and electrical engineering, the automobile industry and the ocean transportation industry.

Description

technical field [0001] The present invention relates to an ultra-high-strength, high-toughness, high-corrosion-resistant CuNiSiNbSn-based elastic copper alloy and a preparation method thereof, in particular to a CuNiSiNbSn-based elastic copper alloy with ultra-high strength, high toughness, and high corrosion resistance and a preparation method thereof; The technical field of elastic alloy preparation. Background technique [0002] Conductive elastic alloys are indispensable and important materials in electronics and electrical engineering, machine instruments, ocean transportation, and automobile industry. It is widely used in the manufacture of various elastic components, such as micro switches, diaphragms, capsules, elastic sensitive components, energy storage components, frequency components, reeds, repeaters, etc. The performance of the elastic element determines the accuracy, reliability and life of the instrument as a whole. With the development of modern industry a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C9/06C22C1/03C22F1/08
CPCC22C1/03C22C9/06C22F1/08
Inventor 李周雷前潘志勇肖柱
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap