Preparation method of pink zirconia ceramic

A zirconia ceramic, pink technology, applied in the field of preparation of pink zirconia ceramics, can solve the problems of high energy consumption, high mold material requirements, rising production costs, etc., to achieve simple and easy-to-use preparation process and low production process cost , cost reduction effect

Inactive Publication Date: 2015-06-03
GUANGDONG JANUS SMART GRP CO LTD +1
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, adopting this method to prepare colored zirconia ceramics has high requirements on the performance of the sintering furnace, and the hot-pressing sintering process and equipment are complicated, the production control requirements are very strict, the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of pink zirconia ceramic

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0035] Examples:

[0036] Weigh 20 grams of polyvinyl alcohol and dissolve it in 1000 grams of water, pour it into a 5L ball mill tank after fully dissolving, add 1000 grams of yttria-containing stable tetragonal zirconia powder (purity 99%, average particle size 0.5μm) and 50 Gram erbium oxide, ball milled for 24 hours, the suspension is poured out, after drying to remove water, the ceramic powder is milled and passed through a 500-mesh screen, dried and cold isostatically pressed to prepare a diameter of 28 mm and a thickness of 8 mm zirconia round cake. Then put it into a high-temperature sintering furnace for debinding and sintering into pink zirconia ceramic products.

[0037] The integrated process segment of debinding and sintering can be expressed as:

[0038]

[0039] The fired zirconia ceramic products are tested by experiments. Among them, the Archimedes principle is used to detect the density, the microhardness tester is used to test the material's Vickers hardness, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of pink zirconia ceramic. The preparation method comprises the following steps: with zirconia powder as a raw material of a ceramic matrix, adding erbium oxide powder to the zirconia powder to be used as a colorant and adding a binder to form a mixed material; preparing a ceramic body by using the mixed material; and carrying out multi-stage sintering treatment on the ceramic body to obtain a pink zirconia ceramic product, wherein the multi-stage sintering treatment at least comprises the following stages: firstly sintering for 7-9h at the temperature of room temperature to 600 DEG C, then sintering for 4-8h at the temperature of 600 DEG C-1200 DEG C, and then sintering for 6-8h at the temperature of 1200 DEG C-1500 DEG C. By utilizing the preparation method of the pink zirconia ceramic, zirconia can be stably colored to pink by pigment on premise of ensuring complete compactness of sintering of zirconia, and low manufacturing cost is maintained simultaneously.

Description

technical field [0001] The invention relates to a preparation method of pink zirconia ceramics. Background technique [0002] Zirconia ceramic is a very important structural ceramic material. It has very excellent mechanical properties, with a bending strength of up to 1000MPa and a fracture toughness of up to 10MPa m1 / 2. It has the reputation of ceramic steel, so it is widely used in industrial machinery and daily life. have more and more widespread applications. [0003] Zirconia ceramic products for civilian use often require beautiful appearance, such as color, luster, etc.; but the ceramic products sintered from pure zirconia powder are white, and a single color is difficult to meet people's growing demand for zirconia ceramic decorations. Therefore, it is imperative to develop zirconia ceramic products of different colors. [0004] However, since the sintering temperature of zirconia materials used as structural ceramics is generally higher than 1400°C, and the high-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/48C04B35/64
Inventor 钟辉
Owner GUANGDONG JANUS SMART GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap