A kind of preparation method of high temperature resistant modified sulfonated phenolic resin for drilling fluid

A technology of sulfonated phenolic resin and high temperature resistance, applied in the field of resin, can solve problems such as not being able to meet the needs of drilling, and achieve the effect of excellent performance

Active Publication Date: 2017-11-07
TIANJIN BO XING ENG SCI & TECH LIMITED COMPANY OF CNPC +2
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Sulfonated phenolic resin will also play a more important role as the main anti-high temperature treatment agent, but the current temperature resistance of the product is generally 180°C, and it will gradually fail to meet the drilling needs of high-temperature wells and ultra-high-temperature wells in the future

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of high temperature resistant modified sulfonated phenolic resin for drilling fluid
  • A kind of preparation method of high temperature resistant modified sulfonated phenolic resin for drilling fluid
  • A kind of preparation method of high temperature resistant modified sulfonated phenolic resin for drilling fluid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A method for preparing a high temperature resistant modified sulfonated phenolic resin for drilling fluid provided by an embodiment of the present invention comprises the following steps:

[0037] 1) Add 1 mol of phenol, 0.5 mol of formaldehyde and 0.001 mol of phosphoric acid into the reactor in sequence, mix and stir for 10 minutes, keep the temperature at 70°C, and react for 20 minutes.

[0038] 2) Dissolve 1.0 mol of sodium sulfite in 100 mL of water, and slowly add 0.5 mol of formaldehyde under stirring to prepare a sulfonating agent.

[0039] 3) After the reaction in the above step 1), add 1.0 moles of sodium hydroxide and 0.01 moles of formaldehyde, and keep the temperature at 60° C., add the sulfonating agent in the above step 2) to the reactor in batches, and continue the reaction for 100 minutes.

[0040] 4) After the reaction, cool down and discharge the material, keep the temperature of the material at 55° C., and obtain the product of Example 1 by spray dry...

Embodiment 2

[0042] A method for preparing a high temperature resistant modified sulfonated phenolic resin for drilling fluid provided by an embodiment of the present invention comprises the following steps:

[0043] 1) Add 1.0 moles of p-cresol, 1.0 moles of acetaldehyde and 0.1 moles of hydrochloric acid to the reactor in sequence, mix and stir for 10 minutes, keep the temperature at 80°C, and react for 100 minutes.

[0044] 2) Dissolve 1.0 mole of sodium bisulfite in 100 mL of water, and slowly add 1.0 mole of formaldehyde under stirring to prepare a sulfonating agent.

[0045] 3) After the reaction in the above step 1), add 0.001 mol of potassium hydroxide and 0.6 mol of acetaldehyde, and keep the temperature at 70° C., add the sulfonating agent in the above step 2) to the reactor in batches, and continue the reaction for 20 minutes.

[0046] 4) After the reaction, cool down and discharge the material, keep the temperature of the material at 65° C., and obtain the product of Example 2 ...

Embodiment 3

[0048] A method for preparing a high temperature resistant modified sulfonated phenolic resin for drilling fluid provided by an embodiment of the present invention comprises the following steps:

[0049] 1) Add 1.0 moles of p-ethylphenol, 1.0 moles of formaldehyde and 1.5 moles of acetic acid to the reactor in sequence, mix and stir for 10 minutes, keep the temperature at 80°C, and react for 300 minutes.

[0050]2) Dissolve 1.0 mol of sodium metabisulfite in 100 mL of water, and slowly add 1.0 mol of formaldehyde under stirring to prepare a sulfonating agent.

[0051] 3) After the reaction in the above step 1), add 0.5 moles of barium hydroxide and 0.7 moles of formaldehyde, and keep the temperature at 80° C., add the sulfonating agent in the above step 2) to the reactor in batches, and continue the reaction for 300 minutes.

[0052] 4) After the reaction, cool down and discharge the material, keep the temperature of the material at 75° C., and obtain the product of Example 3 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a high-temperature-resistant modified sulfonated phenolic resin for drilling fluid, which comprises the following steps: 1) adding phenolic reactants, aldehyde reactants and acid catalysts into a reaction kettle, mixing and stirring, React at 50-110°C for 10-400min; 2) Add alkali catalyst and aldehyde reactant to the reactor, keep the temperature between 50-110°C and add sulfonating agent in batches, react for 10-600min; 3) End of reaction Afterwards, the temperature is lowered and the material is discharged, and the product is obtained by spray drying. The temperature resistance of the modified sulfonated phenolic resin product prepared by the invention can reach 200°C. Under the aging condition of 200°C, the high-temperature and high-pressure filtration of the drilling fluid can be effectively reduced compared with the base slurry, and the salt resistance can reach 15% NaCl salt concentration. .

Description

technical field [0001] The invention relates to the field of resins, in particular to a preparation method of modified sulfonated phenolic resin for drilling fluid. Background technique [0002] Sulfonated phenolic resin (SMP) is a high-temperature and salt-resistant fluid loss reducer developed in the 1970s. It, together with sulfonated lignite (SMC) and sulfonated tannin (SMT), constitute the famous "three Sulfur drilling fluid". The drilling fluid system reduces downhole complex accidents, improves the success rate of deep well drilling, and greatly promotes the technological progress of high-temperature deep well drilling fluids in China. Now sulfonated phenolic resin has become one of the treatment agents that are widely used and must be used in high-temperature well sections. In the future, with the depletion of shallow oil and gas resources, the world's exploration and development will gradually develop into deep strata. Deep well and ultra-deep well oil and gas dr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G8/28C09K8/035
Inventor 张勇王彪刘晓栋刘建军马永乐朱红卫马学勤
Owner TIANJIN BO XING ENG SCI & TECH LIMITED COMPANY OF CNPC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com