A kind of anti-alkali ceramic coating material and preparation method thereof

A ceramic coating and anti-alkali technology, which is applied in the field of anti-alkali ceramic coating materials and its preparation, can solve the problems of low matching degree of physical and chemical properties, high cost, and insufficient bonding strength, etc., and achieve good anti-alkali performance and improved The effect of improving the service life and mechanical strength

Inactive Publication Date: 2017-11-17
WUHAN UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These ceramic coatings can improve the alkali resistance of the surface of the sagger to a certain extent, but there are also the following problems: (1) The material preparation process is complicated, the cost is high, and the process performance is not good, which affects the performance of the alkali-resistant coating; (2) The matching degree of physical and chemical properties between the alkali-resistant coating and the sagger substrate is low, the bonding strength is not enough, the coating is easy to crack and fall off, and the actual number of repeated uses is still limited; (3) The firing temperature of the alkali-resistant coating is poorly adjustable, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-alkali ceramic coating material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of anti-alkali ceramic coating material, the composition of raw material and batching are as follows table 1 (parts by mass):

[0034] Table 1 (Kg)

[0035] spinel

11.0

γ-LiAlO 2

15.0

spodumene

12.0

ZrO 2

1.0

α-Al 2 o 3

3.0

SiO 2

8.0

[0036] Composite phosphate glue (bonding agent)

19.0

Citric Acid Solution (30%)

31.0

[0037] The spodumene in Table 1 is "natural spodumene" (the same applies hereinafter).

[0038] The above-mentioned preparation method of an alkali-resistant ceramic coating material comprises the following steps: 1) selecting raw materials according to the ratio of the above-mentioned raw materials; 2) mixing the raw materials to obtain an alkali-resistant ceramic coating material.

[0039] When in use, the anti-alkali ceramic coating material (after the above raw materials are uniformly mixed to make a well-flowing ceramic slurry) is directly...

Embodiment 2

[0042] A kind of anti-alkali ceramic coating material, the composition of raw material and batching are as follows table 2 (parts by mass):

[0043] Table 2 (Kg)

[0044] spinel

10.0

γ-LiAlO 2

14.5

spodumene

14.0

ZrO 2

1.5

α-Al 2 o 3

3.0

SiO 2

7.0

Composite phosphate glue (bonding agent)

35.0

Citric Acid Solution (30%)

15.0

solid to liquid ratio

50.00:50.00

[0045] The above-mentioned preparation method of an alkali-resistant ceramic coating material comprises the following steps: 1) selecting raw materials according to the ratio of the above-mentioned raw materials; 2) mixing the raw materials to obtain an alkali-resistant ceramic coating material.

[0046] When in use, the anti-alkali ceramic coating material (after the above raw materials are uniformly mixed to make a well-flowing ceramic slurry) is directly coated in various ways on the refractory sagger to be used o...

Embodiment 3

[0049] A kind of anti-alkali ceramic coating material, the composition of raw material and batching are as follows table 3 (parts by mass):

[0050] Table 3 (Kg)

[0051] spinel

9.0

γ-LiAlO 2

18.0

spodumene

13.0

ZrO 2

2.0

α-Al 2 o 3

5.0

SiO 2

3.0

Composite phosphate glue (bonding agent)

20.0

Citric Acid Solution (30%)

30.0

solid to liquid ratio

50.00:50.00

[0052] The above-mentioned preparation method of an alkali-resistant ceramic coating material comprises the following steps: 1) selecting raw materials according to the ratio of the above-mentioned raw materials; 2) mixing the raw materials to obtain an alkali-resistant ceramic coating material.

[0053] When in use, the anti-alkali ceramic coating material (after the above raw materials are uniformly mixed to make a well-flowing ceramic slurry) is directly coated in various ways on the refractory sagger to be used or...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melting pointaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an alkali resistant ceramic coating material and a preparation method thereof which are mainly applied in lithium battery production. The alkali resistant ceramic coating material is characterized by being formed by mixing the raw materials including composite powder, a binding agent and an additive, and the raw materials comprise, by mass, 50 parts of the composite powder, 10-40 parts of the binding agent and 15-40 parts of the additive. The alkali resistant ceramic coating material has the advantages that the coating is good in alkali resistance, capable of being fired in a wide temperature range and low in preparation cost.

Description

technical field [0001] The invention relates to an alkali-resistant ceramic coating material and a preparation method thereof, which are mainly used in the production of lithium batteries. Background technique [0002] At present, lithium batteries are more and more widely used, and have become an indispensable part of information technology, and the competition is becoming more and more fierce. In the production of lithium batteries, positive and negative electrode materials are one of the key materials. However, due to the erosion and volatilization of strong alkaline substances in the high-temperature synthesis of this type of material, it will have a great corrosion effect on the refractory material saggar of the fired synthetic material, resulting in a greatly shortened service life of the refractory saggar and affecting normal operation. The quality of the negative electrode material increases the manufacturing cost of the lithium battery. The main technical measure ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66
Inventor 张强
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com