A kind of sulfurized state hydrogenation catalyst and its preparation method and application

A technology of hydrogenation catalyst and sulfide state, which is applied in the field of preparation of sulfide state hydrogenation catalyst, and can solve the problem of low sulfide degree

Active Publication Date: 2017-05-24
CHINA PETROLEUM & CHEM CORP +1
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] The object of the present invention is to overcome the defect that the degree of sulfidation obtained by sulfurizing the hydrogenation catalyst by the existing method is low, and to provide a method for preparing a sulfided hydrogenation catalyst capable of increasing the degree of sulfidation, obtained by the method Sulfide state hydrogenation catalyst and the application of said sulfide state hydrogenation catalyst in hydrodearomatization reaction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of sulfurized state hydrogenation catalyst and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The preparation method of the sulfurized state hydrogenation catalyst provided by the invention comprises the following steps:

[0026] (1) Prepare an oxidized state hydrogenation catalyst, the oxidized state hydrogenation catalyst includes a carrier and an organic alcohol compound and an active metal oxide supported on the carrier, and the organic alcohol compound exists at 200-400°C at least one exothermic peak;

[0027](2) In the presence of a vulcanization medium, the temperature of the hydrogenation catalyst in the oxidized state is sequentially raised from room temperature at a rate of 1-20°C / h to each release temperature of the organic alcohol compound between 200-400°C; Constant temperature vulcanization at the temperature corresponding to the heat peak peak value for 1-5 hours, and then increase the temperature at a rate of 1-20°C / h from the highest exothermic peak peak value of the organic alcohol compound between 200-400°C The corresponding temperature is in...

Embodiment 1

[0046] This example is used to illustrate the sulfided hydrogenation catalyst provided by the present invention and its preparation method.

[0047] Prepare oxidation state hydrogenation catalyst A1 according to a conventional method, which includes alumina carrier and NiO and MoO supported on alumina carrier 3 Active metal components and ethylene glycol, wherein the molar ratio of carbon atoms to Ni metal atoms in the oxidation state hydrogenation catalyst A1 is 2:1, based on the total weight of the oxidation state hydrogenation catalyst, NiO and MoO 3 The mass content is respectively 3% and 15%. Oxidized state hydrogenation catalyst A1 can decompose and release CO at 230°C-295°C and 300°C-400°C through the temperature-programmed oxidation method (heating rate is 10°C / min, the same below). 2 , CO 2 The temperatures corresponding to the release peaks were 260°C and 350°C, respectively. The oxidized state hydrogenation catalyst A1 is vulcanized by a dry vulcanization method,...

Embodiment 2

[0055] This example is used to illustrate the sulfided hydrogenation catalyst provided by the present invention and its preparation method.

[0056] Oxidation state hydrogenation catalyst B1 was prepared according to a conventional method, which included an alumina support and NiO and WO supported on the alumina support. 3 Active metal components and ethylene glycol, wherein the molar ratio of carbon atoms to Ni metal atoms in the oxidation state hydrogenation catalyst B1 is 2:1, based on the total weight of the oxidation state hydrogenation catalyst, NiO and WO 3 The mass content is respectively 2.5% and 20.5%. Oxidation hydrogenation catalyst B1 can decompose and release CO at temperatures between 200°C-295°C and 300°C-400°C as measured by the temperature-programmed oxidation method 2 , CO 2 The temperatures corresponding to the release peaks were 260°C and 350°C, respectively. The oxidized state hydrogenation catalyst B1 is vulcanized by a dry vulcanization method, and t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
boiling pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a vulcanized hydrogenation catalyst, a preparation method therefor and an application thereof. The preparation method of the vulcanized hydrogenation catalyst comprises the following steps: (1) preparing an oxidized hydrogenation catalyst, wherein the oxidized hydrogenation catalyst comprises a carrier and an organic alcohol compound and an active metal oxide loaded on the carrier; the organic alcohol compound has at least one exothermic peak at 200-400 DEG C; and (2) in the presence of a curing media, successively increasing the temperature of the oxidized hydrogenation catalyst from the room temperature to a temperature corresponding to each exothermic peak of the organic alcohol compound at 200-400 DEG C at a rate of 1-20 DEG C / h; performing a constant temperature vulcanization for 1-5 hours; then increasing the temperature by 20-150 DEG C from atemperature corresponding to the highest temperature exothermic peak of the organic alcohol compound at 200-400 DEG C at the rate of 1-20 DEG C / h; and performing the constant temperature vulcanization for 1-5 hours. By adopting the preperation method provided by the invention, the degree of vulcanization of metals in the catalyst and the proportion of a three-layer-packed structure are improved, thus facilitating the improvement of the catalyst on hydrodearomatization activity.

Description

technical field [0001] The invention relates to a preparation method of a sulfide hydrogenation catalyst, a sulfide hydrogenation catalyst obtained by the method and an application of the sulfide hydrogenation catalyst in hydrogenation dearomatization reaction. Background technique [0002] Hydroprocessing is a pillar technology in the modern oil refining industry, which plays an important role in producing clean fuels, improving product quality, making full use of petroleum resources and raw material pretreatment. With the development of economy, environmental protection and society, oil refining enterprises have continuously put forward higher requirements for the activity and stability of hydrogenation catalysts, and the activity and selectivity of hydrogenation catalysts need to be continuously improved. Among them, the activity of hydrodearomatization is an important index to measure the performance of hydrogenation catalyst. [0003] Aromatic hydrocarbons are one of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/883B01J23/888B01J23/882C10G45/08
Inventor 陈文斌龙湘云李明丰刘学芬赵新强刘清河王奎聂红丁石
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com