Preparation method for anti-bacteria pure cotton fabric

A fabric and pure cotton technology, which is applied in the field of preparation of antibacterial pure cotton fabrics, can solve the problems of easy aggregation, migration and uneven dispersion of silver nanoparticles, and achieve the effects of saving pharmaceutical raw materials, avoiding easy aggregation, and uniform and stable growth

Inactive Publication Date: 2015-12-23
ZHEJIANG SCI-TECH UNIV
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these types of antibacterial agents have the disadvantages of easy aggregation, migration and uneven dispersion of silver nanoparticles.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for anti-bacteria pure cotton fabric
  • Preparation method for anti-bacteria pure cotton fabric
  • Preparation method for anti-bacteria pure cotton fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] A preparation method of antibacterial pure cotton fabric, comprising the following steps:

[0070] (1) Preparation of photo-induced free radical polymer composite finishing solution:

[0071] Every 1 kilogram of photo-induced free radical macromolecule composite finishing liquid is made up of the following components: the degree of etherification is 78% sulfonated polyetheretherketone 4g; hydrogen atom donor polymer 7g; crosslinking agent 1.8wt% (crosslinking agent Weight accounts for the percentage of sulfonated polyether ether ketone and hydrogen atom donor polymer total weight); An appropriate amount of acetic acid adjusts the pH value of the finishing solution to 5; the balance is deionized water; the hydrogen atom donor polymer is polyvinyl alcohol, The joint agent is glutaraldehyde;

[0072] Preparation steps: Put sulfonated polyether ether ketone and 400mL deionized water into a 3-liter stirring container, heat to 50°C under stirring, and dissolve to form soluti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method for an anti-bacteria pure cotton fabric. The preparation method comprises the following steps that 4-17 g of sulfonated poly ether ether ketone, 7-19 g of hydrogen atom donor polymers, 1.8-11.3 wt% of cross-linking agents, an appropriate amount of acetic acid for regulating the pH value of finishing liquor to 2-5 and the balance deionized water are mixed into 1 kg of solutions; a pure cotton fabric is coated with the finishing liquor on a flat screen printing machine; the fabric is pre-dried in a drying oven with the temperature of 100 DEG C for 10-25 min; the fabric is baked in a baking machine with the temperature of 160 DEG C for 35-80 s; the fabric is coated with foam finishing liquor containing silver salt through a foam finishing method, and then vacuum drying is performed on the fabric; the fabric is placed in an photochemical reactor and radiated with 350-nm ultraviolet light to reduce silver ions to generate silver nanoparticles, and the anti-bacteria pure cotton fabric is prepared. The anti-bacteria pure cotton fabric is soft in handfeel and excellent in anti-bacteria property, overcomes the defect that the anti-bacteria property gradually becomes worse due to problems such as silver ion dispersion and migration of a traditional nano-silver anti-bacteria fabric and can be applied to the field of anti-bacteria protection suits.

Description

technical field [0001] The invention relates to a preparation method of an antibacterial pure cotton fabric, belonging to the field of functional textiles. Background technique [0002] In daily life, people will inevitably come into contact with various microorganisms. These microorganisms will rapidly grow and reproduce in a suitable environment, spread diseases, pollute the environment, and affect people's physical and mental health. Therefore, antibacterial substances are widely used Used in daily textiles such as non-woven fabrics, underwear, footwear, towels, bedding and decorative fabrics. With the development of society, people are more and more fond of antibacterial functional clothing, and their requirements are getting higher and higher. The antibacterial agents used must not only be efficient and safe, but also environmentally friendly, efficient, durable and safe. Development is getting more and more attention. Therefore, it is very meaningful to study the ant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/83D06M15/41D06M15/61D06M15/333D06M13/11D06M13/123D06M23/04D06M101/06
Inventor 林俊雄王鹏
Owner ZHEJIANG SCI-TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com