A kind of manufacturing method of recombined decorative material

A technology for reorganizing decorative materials and manufacturing methods, which is applied in the field of wood processing and can solve problems such as unnatural transition of product texture and color, single panel dyeing process technology, etc.

Active Publication Date: 2018-05-25
ZHEJIANG SHENGHUA YUNFENG GREENEO
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the above problems, the present invention provides a manufacturing method for recombined decorative materials by modifying the dyeing vat and the veneer hanging cage, and changing the way of forming blanks, which solves the problem of single veneer dyeing technology in the production process of existing recombined decorative materials. 1. The problem of unnatural texture and color transition of the product makes the texture and color of the finished product very realistic, and there will be no gradual transfer of texture and color

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 1) Rotate and cut AYOUS logs into veneers with a length of 2580mm, a width of 360mm, and a thickness of 0.75mm, and bleach the veneers: put the veneers into the bleaching tank, use 35% hydrogen peroxide as the bleaching agent, and adjust the bleaching agent The concentration of the solution is 3%, the pH value=11 of the bleach solution is adjusted with 30% sodium hydroxide solution, the bleaching aid is sodium silicate, and the bleaching time is 45 minutes;

[0031] 2) drying the veneer prepared in step 1) in a dryer, and controlling the moisture content of the veneer at 10%; controlling the moisture content of the veneer can prevent the deformation of the product in the subsequent process;

[0032] 3) Put a stainless steel partition between the adjacent veneers, and fold and bend the veneer to form a "V" shape according to the part that needs to be dyed on the veneer in the horizontal direction of the veneer, and put it into the horizontal The dyeing cage is waiting to...

Embodiment 2

[0041] 1) Rotate and cut AYOUS logs into veneers with a length of 2580mm, a width of 680mm, and a thickness of 0.75mm, and bleach the veneers: put the veneers into the bleaching tank, use 35% hydrogen peroxide as the bleaching agent, and adjust the bleaching agent The concentration of the solution is 3%, the pH value=11 of the bleach solution is adjusted with 30% sodium hydroxide solution, the bleaching auxiliary agent is sodium silicate, and the bleaching time is 45 minutes;

[0042] 2) drying the veneer prepared in step 1) in a dryer, and controlling the moisture content of the veneer at 10%; controlling the moisture content of the veneer can prevent the deformation of the product in the subsequent process;

[0043] 3) Put a stainless steel partition between the adjacent veneers, and fold and bend the veneer to form a "V" shape according to the part that needs to be dyed on the veneer in the horizontal direction of the veneer, and put it into the horizontal The dyeing cage is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for manufacturing a recombined decorative material, which comprises the steps of making veneers from logs, folding, bending and dyeing the veneers, drying the veneers after dyeing, repairing the veneers, forming blanks of the veneers, gluing them, and pressing them into wooden squares. , wood maintenance, lumber, and then sliced ​​into recombined decorative veneers. The present invention solves the problem of single color, unnatural transition, dark and light texture of technical wood by changing the structure of the dyeing vat and veneer dyeing cage, and adjusting the veneer cage method, the height of the dye solution level and the billet assembly method. Problems such as transfer may occur, and the recombined decorative material product produced by the method of the invention is very realistic.

Description

technical field [0001] The invention relates to the technical field of wood processing, in particular to a method for manufacturing recombined decorative materials. Background technique [0002] Due to the depletion of natural precious wood resources, people have been using less and less high-grade wood materials in the decoration and decoration of buildings and homes. As a substitute, recombined decorative materials have developed rapidly and have been The field of decoration and decoration in the world occupies a pivotal position. The recombined decorative material is to cut the ordinary fast-growing wood into veneers, after bleaching, dyeing and other different coloring treatments, the veneers of different colors are assembled into billets, and then glued into wooden squares. Planed to obtain a product similar to the grain of natural precious wood. [0003] As a reprocessed material, recombined decorative materials account for more than 95% of the wood content. In the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B27D1/04B27K5/02
Inventor 赵忠庆盛娜吕华庞小仁
Owner ZHEJIANG SHENGHUA YUNFENG GREENEO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap