A technology of coarse-grained steel and molten steel, applied in the direction of improvement of process efficiency, furnace type, furnace, etc., can solve problems such as not meeting the grain size requirements of coarse-grained steel
Active Publication Date: 2016-03-23
WUYANG IRON & STEEL
View PDF5 Cites 8 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
If it is not properly controlled, the Al content in steel can easily exceed 0.005%, and it does not meet the grain size requirements of coarse-grained steel.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1－7
[0020] Examples 1-7: See Table 1 for the specific process of the method for smelting coarse-grained steel and the Al and Si contents of the product (finished product).
[0021] Table 1: Process parameters and Al, Si content of the embodiment
[0022]
[0023] A steel company produced 80 furnaces of coarse-grained steel with the requirement of Al≤0.005wt% by using the above-mentioned method for smelting coarse-grained steel. The steel types include SA515Gr65 and SA515Gr70, and the Al content of all finished steels is between 0.002% and 0.005%. , The passing rate of flaw detection of the rolled steel plate is 100%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a method for smelting coarse-grained steel. The method comprises an electric arc furnace (EAF) primary smelting process, a ladle furnace (LF) refining process and a vacuum degassing (VD) furnace vacuum treatment process. The method for smelting the coarse-grained steel is characterized in that high manganese or silicon manganese alloy and lime are added along with a steel stream in the tapping process of the EAF primary smelting process; in the LF refining process, molten steel is deoxidized and desulfurizes, and the chemical composition and the temperature of the molten steel are adjusted; in the VD furnace vacuum treatment process, the alloy composition is slightly adjusted, vacuum treatment is conducted, the temperature is adjusted, and the molten steel enters a continuous casting process or a mold casting process to be poured into a coarse-grained ingot blank. According to the method for smelting the coarse-grained steel, operation is easy and convenient, not only the effects of deoxidizing, desulfurizing, and removing impurities through the LF can be ensured, but also it can be ensured that Al in the steel accounts for 0.005% or less, what is more, the oxygen content and the sulfur content in the steel are low, the impurities are few, and a rolled steel plate meets the flaw detection requirements.
Description
technical field [0001] The invention belongs to the field of iron and steel metallurgy, in particular to a method for smelting coarse grain steel. Background technique [0002] Coarse-grained steel belongs to killed steel, and the internal quality of the steel is required to be high. Essential grain size refers to the tendency of steel to grow austenite grains under certain conditions. Measure austenite grains after holding at 930±10°C for 3-8 hours. If the grain size is 1-4, it is essentially coarse-grained steel; if the grain size is 5-8, it is essentially fine-grained steel. . In the smelting process of grain steel, Al and or Si are often used for deoxidation; among them, the steel deoxidized by Al contains AlN particles, and the grains are not easy to grow when heated at a certain temperature, so it is called fine grain steel; the steel deoxidized by Si , does not contain the second phase particles that can inhibit the growth of the grain, and the grain grows graduall...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): C21C5/52C21C7/06C21C7/10
CPCC21C5/52C21C7/06C21C7/10Y02P10/20
Inventor 兰瑞金赵向政
Owner WUYANG IRON & STEEL