Graphite furnace lining used for high purity graphitization furnaces, and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A high-purity graphite and graphite furnace technology, applied in the field of graphite materials and its preparation, can solve the problems of low purity, high price, low strength, etc.
Active Publication Date: 2016-06-08
DATONG XINCHENG NEW MATERIAL CO LTD
View PDF5 Cites 6 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The temperature of the graphite furnace lining is as high as 3000-3300°C, so the lining material must be resistant to high temperature, oxidation resistance, low ash content and thermal shock resistance. In addition, the purity of the graphite material for the furnace lining has a direct impact on the performance of the graphitized product. If the graphite furnace lining If the impurity content is too high, impurities will be introduced into the graphitization product, thereby affecting the performance of the high-purity graphite product. Conventional graphite materials cannot meet the lining requirements of high-purity graphitization furnaces
At this stage, the lining of high-purity graphitization furnaces is mostly made of carbon-carbon composite materials, which have low purity, low strength, and are expensive. In addition, the lining is still a wearing part, which greatly increases the production cost.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0045] (1) Crushing, sieving, and batching: crush the calcined petroleum coke, and sieve it into specifications of 0.5mm
[0046] Wherein, among the above-mentioned 80 parts by weight of calcined coke: calcined coke with 0.5mm
Embodiment 2
[0057] (1) Crushing, sieving, and batching: crush the calcined petroleum coke, and sieve it into specifications of 0.5mm
[0058] Wherein, among the above-mentioned 82 parts by weight of calcined coke: calcined coke with 0.5mm
Embodiment 3
[0069] (1) Crushing, sieving, and batching: crush the calcined petroleum coke, and sieve it into specifications of 0.5mm
[0070] Wherein, among the above-mentioned 81 parts by weight of calcined coke: calcined coke with 0.5mm
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
coking value
aaaaa
aaaaa
particle diameter
aaaaa
aaaaa
density
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a graphite furnace lining used for high purity graphitization furnaces, and a preparation method thereof, and belongs to the technical field of graphite processing. The preparation method comprises steps of crushing, sieving, material preparing, dry blending, wet blending, moulding, primary roasting, primary dipping, secondary roasting, secondary dipping, tertiary roasting, and graphitization. In the raw materials of the graphite furnace lining, an aggregate is composed of calcined coke, pitch coke, and needle coke at a mass ratio of 80-82:10-15:5-8; wherein calcined coke is composed of particles with four following different particle size ranges: 0.5mm<=particle size<0.8mm, 0.335mm<=particle size <0.5mm, 0.075mm<=particle size<0.335mm, and particle size<0.075mm, and the weight amounts of the four particles account for 1 to 2%, 35 to 40%, 27 to 31%, and 27 to 37% respectively. Purity of the graphite furnace lining prepared via the preparation method is high; bulk density is large; porosity is low; ash content is low; oxidation resistance, compressive strength, and rupture strength are extremely excellent; and application requirements on high purity graphitization furnace linings are satisfied.
Description
technical field [0001] The invention relates to a graphite material and a preparation method thereof, in particular to a graphite lining for a high-purity graphitization furnace and a preparation method thereof. Background technique [0002] High-purity graphite refers to graphite with a carbon content greater than 99.99%. High-purity graphite has the advantages of high temperature resistance, corrosion resistance, thermal shock resistance, small thermal expansion coefficient, self-lubricating, small resistivity and easy machining. It is widely used in metallurgy, machinery, environmental protection, chemical industry, electronics, medicine, military industry and aerospace fields, and its position in the national economy is becoming more and more important. [0003] At present, my country's graphite industry technology is still at the low level in the world, and the products are mostly raw materials and primary processed products, and the high impurities in the products limi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.