A kind of coating for tinplate and its production process and application

A production process and technology of tinplate, applied in anti-corrosion coatings, coatings and other directions, can solve the problems of low solvent resistance and high temperature resistance of acrylic acid, limit the use range of tinplate coatings, and reduce the quality of tinplate printing patterns, etc., to achieve strong adhesion performance, enhance the use value, and improve the effect of printing quality

Active Publication Date: 2018-06-19
DONGGUAN K LASER TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high hardness of the material of tinplate, the baking temperature of the glue and varnish used for laminating the coating is relatively high, and the glue and ink used in printing are highly corrosive, which often cause damage to the coating used for tinplate. Erosion leads to a decline in the quality of tinplate printing patterns, so the coating used for tinplate must have a certain performance of high temperature resistance and solvent resistance
Most of the coatings on the market use acrylic acid as a coating for tinplate. The solvent resistance and high temperature resistance of acrylic acid are not high, which cannot meet the needs of printing on tinplate materials.
In addition, the existing tinplate coatings on the market are transfer coatings that can only be used as transfer coatings, and composite coatings that can only be used as composite coatings and cannot be used universally, which limits the scope of use of tinplate coatings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of coating for tinplate and its production process and application
  • A kind of coating for tinplate and its production process and application
  • A kind of coating for tinplate and its production process and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A coating for tinplate, which comprises the following raw materials by weight:

[0046] Hydroxy-containing acrylic resin 10kg

[0047] Melamine formaldehyde resin 77kg

[0048] Ester solvent 5kg

[0049] Ketone solvent 8kg

[0050] Wherein, the ester solvent of this implementation is ethyl acetate solvent, and the ketone solvent is acetone solvent.

[0051] The production technology of above-mentioned coating for tinplate, it comprises the following steps:

[0052] Step 1, weighing: Weigh 10kg of hydroxyl-containing acrylic acid and 77kg of melamine formaldehyde resin and add them to the reaction kettle for mixing;

[0053] Step 2, batching: Add 5kg of ethyl acetate solvent and 8kg of acetone solvent into the reaction kettle described in step 1, and then stir at 30°C for 40min to prepare the coating for tinplate;

[0054] The finished coating prepared in this embodiment is properly stored in an environment with humidity controlled at 40%.

[0055] A coating for ti...

Embodiment 2

[0059] A coating for tinplate, which comprises the following raw materials by weight:

[0060] Hydroxy-containing acrylic resin 10kg

[0061] Melamine formaldehyde resin 78kg

[0062] Ester solvent 4kg

[0063] Ketone solvent 8kg

[0064] Wherein, the ester solvent in this implementation is butyl acetate solvent, and the ketone solvent is methyl butanone solvent.

[0065] The production technology of above-mentioned coating for tinplate, it comprises the following steps:

[0066] Step 1, weighing: Weigh 10kg of hydroxyl-containing acrylic acid and 78kg of melamine formaldehyde resin and add them to the reaction kettle for mixing;

[0067]Step 2, batching: Add 4kg of ethyl acetate solvent and 8kg of acetone solvent into the reaction kettle described in step 1, and stir at 20°C for 40min to prepare the coating for tinplate;

[0068] The finished coating prepared in this embodiment is properly stored in an environment with humidity controlled at 40%.

[0069] A coating for ...

Embodiment 3

[0073] A coating for tinplate, which comprises the following raw materials by weight:

[0074] Hydroxy-containing acrylic resin 9kg

[0075] Melamine formaldehyde resin 80kg

[0076] Ester solvent 5kg

[0077] Ketone solvent 6kg

[0078] Wherein, the ester solvent of this implementation is ethyl acetate solvent, and the ketone solvent is acetone solvent.

[0079] The production technology of above-mentioned coating for tinplate, it comprises the following steps:

[0080] Step 1, weighing: Weigh 9kg of hydroxyl-containing acrylic acid and 80kg of melamine formaldehyde resin and add them to the reaction kettle for mixing;

[0081] Step 2, batching: Add 5kg of ethyl acetate solvent and 6kg of acetone solvent into the reaction kettle described in step 1, and stir at 30°C for 50min to prepare the coating for tinplate;

[0082] The finished coating prepared in this embodiment is properly stored in an environment with humidity controlled at 30%.

[0083] A coating for tinplate ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of paint for painting tinplates, and specifically relates to a paint for tinplate, a production technology and applications thereof. The paint for tinplate comprises the following components in percentage by weight: 5 to 10% of hydroxyl containing acrylic acid, 70 to 80% of melamine-formaldehyde resin, 2 to 8% of ester solvent, and 5 to 10% of ketone solvent. Compared with the prior art, the paint has a performance on resisting solvent and high temperature; and when the paint is painted on a tinplate, the formed coating can resisting the corrosion of adhesive glue and high temperature during the adhering process. The provided paint has a strong adhesive property, can be applied to various products, can be directly painted on a material as a compound coating, is also capable of being co-used with an aqueous release layer as a transfer coating, and meets the requirements of printing on tinplate.

Description

technical field [0001] The invention relates to the technical field of coatings for tinplate printing, in particular to a coating for tinplate and its production process and application. Background technique [0002] With the development of society, people's pursuit of life is getting higher and higher, especially the pursuit of commodities is not limited to quality, and they also have higher requirements for the appearance of commodity packaging. Therefore, product manufacturers use a wide variety of packaging materials to decorate commodities in order to improve the competitiveness of commodities. Among them, tinplate is used as the substrate of the packaging material, and then a coating is pasted on the substrate to print patterns. It looks high-end and atmospheric, and has been welcomed by major packaging industries. However, due to the high hardness of the material of tinplate, the baking temperature of the glue and varnish used for laminating the coating is relatively...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D161/28C09D133/00C09D5/08
CPCC08L2201/08C09D5/08C09D161/28C08L33/00
Inventor 张恒
Owner DONGGUAN K LASER TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap