Liquid hardening agent with high wear resistance and preparation method thereof

A hardening agent and high wear-resistant technology, applied in the field of cement infrastructure materials, can solve the problems of easy efflorescence and high cost, and achieve the effects of strong permeability, easy operation and reduced production cost

Active Publication Date: 2016-07-13
HANGZHOU GELING NEW MATERIAL TECH
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, both of the above two hardeners hav...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Liquid hardening agent with high wear resistance and preparation method thereof
  • Liquid hardening agent with high wear resistance and preparation method thereof
  • Liquid hardening agent with high wear resistance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Add 20 parts of absolute ethanol and 10 parts of aluminum nitrate to the high-speed disperser, and disperse at a speed of 2000r / min for 30 minutes until all the solids are dissolved; then add 50 parts of methyl silicate and 1 part of dibutyltin dilaurate , and disperse for 10 minutes at a speed of 200r / min to obtain the high wear-resistant liquid hardener of the present invention.

Embodiment 2

[0033] Add 10 parts of absolute ethanol and 30 parts of aluminum ethylate to the high-speed disperser, and disperse for 30 minutes at a speed of 2000r / min; then add 70 parts of methyl tripolysilicate and 3 parts of dibutyltin dilaurate, Disperse for 10 minutes at a speed of 1 / min to obtain the high wear-resistant liquid hardener of the present invention.

Embodiment 3

[0035] Add 5 parts of absolute ethanol and 5 parts of polyaluminum chloride to the high-speed disperser, and disperse for 30 minutes at a speed of 2000r / min; then add 95 parts of ethyl silicate and 2 parts of dibutyltin diacetate, Disperse at a speed of 10 min for 10 min to obtain the high wear-resistant liquid hardener of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a liquid hardening agent with high wear resistance and a preparation method thereof. In terms of 100% of the mass of the hardening agent, the liquid hardening agent is prepared from the following raw materials: 50-90% of silicate ester, 1-30% of aluminum salts, 1-30% of alcohol and 1-5% of a catalyst, wherein the silicate ester is selected from one or a combination of more of methyl silicate, ethyl silicate, tri(methyl silicate), and preformed polymer of methyl silicate and ethyl silicate; the aluminum salt is selected from one or a combination of more of aluminum chloride, aluminum nitrate, aluminum chlorohydrate, polymer aluminum nitrate, aluminum formate, aluminum acetate, aluminum methoxide, aluminum ethylate and aluminum isopropoxide. According to the liquid hardening agent, silicate ester and the aluminum salt are adopted as the main ingredients, so that the content of the active ingredients is higher than that of a common water-based product, and the permeability is extremely high, and therefore, the hardness and wear resistance of cement can be remarkably improved. Meanwhile, the preparation method is simple and is beneficial to reduction in the industrial production cost.

Description

technical field [0001] The invention belongs to the technical field of cement infrastructure materials, and in particular relates to a high wear-resistant liquid hardener and a preparation method thereof. Background technique [0002] As the most important modern building material, cement-based building materials have the characteristics of high strength, low cost, and various types. However, cement-based building materials often have interconnected capillary pores in the material due to insufficient batch stability, inadequate construction and maintenance, and even disadvantages such as sanding and cracking, resulting in reduced performance of the material or loss of certain properties. Function. Through post-improvement of cement-based materials, the performance of cement-based materials can be improved, which has significant environmental and economic benefits. The Chinese invention patent application with publication number CN201110354668.2 discloses a lithium-based co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/65C04B41/64
CPCC04B41/4961C04B41/5009C04B41/5012C04B41/64C04B41/65C04B2111/2038C04B41/463C04B41/4922C04B41/49
Inventor 杨辉徐意吴旭日
Owner HANGZHOU GELING NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap