An environmentally friendly coating and formaldehyde adsorption technology, applied in the field of coatings, to achieve the effect of improving comprehensive performance, improving indoor air, and good adsorption performance

Inactive Publication Date: 2016-07-13
刘云
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In practical application, it is found that the formaldehyde purification efficiency of the coating reaches 86.8-88.2%, and the persistence of formaldehyde purification effect reaches 72.8-74.0%. The toluene purification efficiency reaches 52.1-54.2%, and the toluene purification effect persistence reaches 34.8-36.0%. Improvement, but people in modern society have higher requirements for quality of life, so higher requirements are put forward for more efficient and more environmentally friendly coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Formaldehyde-adsorbing waterborne environment-friendly coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A formaldehyde-absorbing water-based environmental protection paint, comprising the following raw materials in parts by weight: 20 parts of styrene-acrylate resin liquid; 22 parts of pure acrylic acid emulsion; 13 parts of 2-imidazolidinone; 1-(2-hydroxyethyl)- 8 parts of 2-imidazolidinone; 8 parts of polyether modified polysiloxane; 11 parts of vinyl acetate-ethylene copolymer emulsion; 8 parts of nano-activated carbon; 7 parts of nano-titanium dioxide; 12 parts of calcined kaolin; 9 parts of anion additive; 3 parts; 8 parts of glycerin; 3 parts of hydroxyethyl cellulose; 1 part of cellulose ether; 11 parts of acrylate-styrene-vinyl acetate terpolymer; poly(N-isopropylacrylamide) modified 7 parts of magnesium hydroxide; 70 parts of deionized water.

[0024] Preferably, the liquid-solid content of the styrene-acrylate resin is 37-40wt%.

[0025] Preferably, the particle size of the nano activated carbon is 20-50nm.

[0026] Preferably, the particle size of the nano ti...

Embodiment 2

[0037] A formaldehyde-absorbing water-based environmental protection coating, comprising the following raw materials in parts by weight: 26 parts of styrene-acrylate resin liquid; 17 parts of pure acrylic emulsion; 15 parts of 2-imidazolidinone; 1-(2-hydroxyethyl)- 12 parts of 2-imidazolidinone; 6 parts of polyether modified polysiloxane; 12 parts of vinyl acetate-ethylene copolymer emulsion; 7 parts of nano-activated carbon; 9 parts of nano-titanium dioxide; 14 parts of calcined kaolin; 9 parts of negative ion additives; 6 parts; 6 parts of glycerin; 6 parts of hydroxyethyl cellulose; 2 parts of cellulose ether; 13 parts of acrylate-styrene-vinyl acetate terpolymer; poly(N-isopropylacrylamide) modified 8 parts of magnesium hydroxide; 80 parts of deionized water.

[0038] The preparation method is the same as in Example 1.

Embodiment 3

[0040] A formaldehyde-absorbing water-based environmental protection paint, comprising the following raw materials in parts by weight: 22 parts of styrene-acrylate resin liquid; 20 parts of pure acrylic acid emulsion; 17 parts of 2-imidazolidinone; 1-(2-hydroxyethyl)- 10 parts of 2-imidazolidinone; 5 parts of polyether modified polysiloxane; 13 parts of vinyl acetate-ethylene copolymer emulsion; 5 parts of nano-activated carbon; 9 parts of nano-titanium dioxide; 14 parts of calcined kaolin; 9 parts of negative ion additive; 7 parts; 8 parts of glycerol; 6 parts of hydroxyethyl cellulose; 2 parts of cellulose ether; 15 parts of acrylate-styrene-vinyl acetate terpolymer; poly(N-isopropylacrylamide) modified 11 parts of magnesium hydroxide; 80 parts of deionized water.

[0041] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to view more

Abstract

A formaldehyde-adsorbing waterborne environment-friendly coating comprises, by weight, 20-26 parts of styrene-acrylate resin liquid, 17-22 parts of pure acrylic emulsion, 13-17 parts of 2-imidazolidone, 8-12 parts of 1-(2-hydroxyethyl)-2-imidazolidone, 5-8 parts of polyether-modified polysiloxane, 11-13 parts of acetate-ethylene copolymer emulsion, 5-8 parts of active carbon nanoparticles, 7-9 parts of nanometer titania, 12-14 parts of calcined kaolin, 7-9 parts of anion additives, 3-7 parts of lauric acid, 6-8 parts of glycerol, 3-6 parts of hydroxyethyl cellulose, 1-2 parts of cellulose ether, 11-15 parts of acrylate-styrene-vinylacetate terpolymer, 7-11 parts of poly(N-isopropyl acrylamide) modified magnesium hydroxide and 60-80 parts of deionized water.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a formaldehyde-absorbing water-based environmental protection coating. Background technique [0002] Paint is a chemical mixture paint that can firmly cover the surface of objects for protection, decoration, marking and other special purposes. The relatively authoritative book "Painting Technology" in the Chinese coatings industry defines it as follows: "Painting is a material that can be coated on the surface of an object by different construction techniques to form a firm adhesion, a certain strength, and a continuous coating. Solid film. The film formed in this way is commonly called coating film, also known as paint film or coating.” It belongs to organic chemical polymer materials, and the formed coating film belongs to the type of polymer compound. According to the classification of modern chemical products, coatings belong to fine chemical products. Modern coatings are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D133/04C09D5/18C09D5/14C09D7/12
CPCC09D125/14C08K2201/011C08L2201/02C08L2205/02C08L2205/035C09D5/14C09D5/18C09D7/61C09D7/62C09D7/63C09D7/65C08L33/08C08L33/04C08L31/04C08K13/06C08K9/08C08K2003/2224C08K5/3445C08K3/04C08K2003/2241
Inventor 刘云张文海
Owner 刘云
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap