Water-based flash-rust inhibitor and application thereof

A technology of flash rust inhibitor and anti-flash rust agent, used in coatings, anti-corrosion coatings, epoxy resin coatings, etc. Inhibition effect has a large influence, to achieve stable flash rust inhibition effect, ensure flash rust inhibition effect, and good flash rust inhibition effect.

Inactive Publication Date: 2016-08-03
SICHUAN YANDING WATER BASED ENVIRONMENT FRIENDLY PAINT CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] According to the current research status, the causes of flash rust in the construction process of water-based paint are complex and diverse, and there is no conclusion. As a result, most of the research and development of existing flash rust inhibitors start from the one-sided flash rust mechanism, and cannot effectively solve the flash rust fundamentally. question
Moreover, the flash rust inhibition effect of the existing flash rust inhibitors is greatly affected by the construction environment. With the change of the construction environment, the flash rust inhibition effect is different.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The water-based flash rust inhibitor of Example 1 comprises, by weight, 2-4 parts of an organic amine containing a lone pair of electrons, 2-3 parts of nitrite and 1-3 parts of an anti-flash rust agent.

[0031] The water-based flash rust inhibitor of Example 1 is suitable for spraying construction of water-based paints in high-temperature and low-humidity environments. The environment of high temperature and low humidity is specifically: the temperature is higher than 35° C., and the humidity is 10% to 20%.

[0032] Wherein, the organic amine containing a lone pair of electrons is selected from but not limited to dimethylethanolamine (DMEA) or multifunctional amine additive AMP-95.

[0033] Specifically, nitrite can be used as the inorganic salt corrosion inhibitor. The nitrite can be potassium nitrite or sodium nitrite.

[0034] The anti-flash rust agent adopts a commercially available anti-flash rust agent based on passivation as the anti-flash rust principle. For...

Embodiment 2

[0039] The water-based flash rust inhibitor of Example 2 comprises, by weight, 8-10 parts of an organic amine containing a lone pair of electrons, 5-8 parts of an inorganic salt corrosion inhibitor and 13-20 parts of an anti-flash rust agent.

[0040] The water-based flash rust inhibitor of Example 2 is suitable for spraying construction of water-based paints in low-temperature and high-humidity environments. The low-temperature and high-humidity environment is specifically: lower than 5° C., and the humidity is 80% to 90%.

[0041] Wherein, the organic amine containing a lone pair of electrons is selected from but not limited to dimethylethanolamine (DMEA) or multifunctional amine additive AMP-95.

[0042] Specifically, nitrite can be used as the inorganic salt corrosion inhibitor. The nitrite can be potassium nitrite or sodium nitrite.

[0043] The anti-flash rust agent adopts a commercially available anti-flash rust agent based on passivation as the anti-flash rust princi...

Embodiment 3

[0049] A water-based flash rust inhibitor of this embodiment 3, by weight, the water-based flash rust inhibitor includes 5-7 parts of organic amines containing lone pairs of electrons, 3.1-4 parts of inorganic salt corrosion inhibitors and anti-flash rust inhibitors 4 to 12 parts of rust agent.

[0050] The water-based flash rust inhibitor of Example 3 is suitable for spraying construction of water-based paints in environments with medium temperature and medium humidity. Wherein, the medium temperature and medium humidity environment is 5° C. to 35° C., and the humidity is greater than 20% and less than 90%.

[0051] Wherein, the organic amine containing a lone pair of electrons is selected from but not limited to dimethylethanolamine (DMEA) or multifunctional amine additive AMP-95.

[0052] Specifically, nitrite can be used as the inorganic salt corrosion inhibitor. The nitrite can be potassium nitrite or sodium nitrite.

[0053] The anti-flash rust agent adopts a commerci...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a water-based flash-rust inhibitor and application thereof. The water-based flash-rust inhibitor is prepared from, by weight, 2-10 parts of organic amine of lone pair electrons, 2-8 parts of an inorganic salt type corrosion inhibitor and 1-20 parts of a flash-rust inhibitor and further contains 15-30 parts of strontium chromate. The water-based flash-rust inhibitor serves as the flash-rust inhibitor to be applied to water-based paint. The water-based flash-rust inhibitor has an excellent flash-rust inhibiting effect, can still guarantee that no flash-rust phenomenon is produced in the construction process of the water-based paint in extreme construction environments, such as a low-temperature and high-humidity environment and a high-temperature and low-humidity environment and is good and stable in flash-rust inhibiting effect. The water-based flash-rust inhibitor is especially applied to water-based acrylic paint or water-based alkyd paint. The water-based paint added with the water-based flash-rust inhibitor is coated on a metal base material during construction, has a very good flash-rust inhibiting effect, and especially for steel parts, particularly the steel parts subjected to submerged-arc welding, has a very good flash-rust inhibiting effect.

Description

technical field [0001] The invention relates to the technical field of anti-flash rust of water-based paints, in particular to a water-based flash rust inhibitor and application thereof. Background technique [0002] Water-based paint is a paint that uses water as a diluent and does not contain organic solvents. The paint film is plump, crystal clear, and flexible, and has the characteristics of water resistance, wear resistance, aging resistance, yellowing resistance, dry block, and convenient use. It can be used on various materials such as wood, metal, plastic, glass, and building surfaces. However, when the water-based paint is applied to the metal substrate, rust spots appear during the drying process, that is, flash rust occurs, which affects its application on the metal substrate to a certain extent. Therefore, flash rust inhibitors for water-based paints have been developed to improve the quality of water-based paint films. [0003] According to the current resear...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D5/08C09D167/08C09D163/00
CPCC09D5/08C09D163/00C09D167/08C08L63/00C08K5/17C08K3/28C08L67/08C08K3/24
Inventor 汪锋
Owner SICHUAN YANDING WATER BASED ENVIRONMENT FRIENDLY PAINT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products