Penetrating primer for solid wood furniture

A furniture and solid wood technology, applied in the field of paint and coatings, can solve problems such as poor quality, collapse transparency, and bulging tendons

Active Publication Date: 2021-02-09
河南立邦长润发科技材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention patent with the authorization number CN103360903 uses acid-alcohol resin and modified acrylic resin to prepare a high-strength anti-bulging PU crystal transparent primer coating. This coating can solve the problem of dark wood furniture such as willow and ebony. Problems such as bulging tendons, collapse and poor transparency caused by the product
However, this kind of paint uses glass powder, which may have the problem of uneven painting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Penetrating primer for solid wood furniture
  • Penetrating primer for solid wood furniture
  • Penetrating primer for solid wood furniture

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Solid wood furniture penetrating primer, including: main paint and curing agent, wherein, the main paint includes:

[0033]

[0034] Curing agents include:

[0035] Hexamethylene diisocyanate 41kg;

[0036] Toluene diisocyanate trimer 14kg;

[0037] 40kg of the second solvent.

[0038] Among them, the acid value of the strong wetting alkyd resin is 4±2mgKOH / g, and the viscosity is 4500±1000mPa . s / 25°C, the hydroxyl content is 120-130%, the water content is ≤0.1%, the density is 1.01g / ml / 20°C, and the flash point is about 23°C.

[0039] Wherein, the first solvent is selected from one or more of toluene, xylene, cyclohexanone, propylene glycol methyl ether acetate, and butyl acetate.

[0040] Wherein, the second solvent is selected from one or more of butyl acetate, ethyl acetate, and cyclohexanone.

[0041] A solid wood furniture penetrating primer was prepared according to the above-mentioned components.

Embodiment 2

[0043] Solid wood furniture penetrating primer, including: main paint and curing agent, wherein, the main paint includes:

[0044]

[0045] Curing agents include:

[0046] Hexamethylene diisocyanate 42kg;

[0047] Toluene diisocyanate trimer 16kg;

[0048] 41kg of the second solvent.

[0049] Among them, the acid value of the strong wetting alkyd resin is 4±2mgKOH / g, the viscosity is 4500±1000mPa·s\25℃, the hydroxyl content is 120-130%, the moisture content is ≤0.1%, and the density is 1.01g / ml\ 20°C, the flash point is about 23°C.

[0050] Wherein, the first solvent is selected from one or more of toluene, xylene, cyclohexanone, propylene glycol methyl ether acetate, and butyl acetate.

[0051] Wherein, the second solvent is selected from one or more of butyl acetate, ethyl acetate, and cyclohexanone.

[0052] A solid wood furniture penetrating primer was prepared according to the above-mentioned components.

Embodiment 3

[0054] Solid wood furniture penetrating primer, including: main paint and curing agent, wherein, the main paint includes:

[0055]

[0056] Curing agents include:

[0057] Hexamethylene diisocyanate 43kg;

[0058] Toluene diisocyanate trimer 15kg;

[0059] 41kg of the second solvent.

[0060] Among them, the acid value of the strong wetting alkyd resin is 4±2mgKOH / g, and the viscosity is 4500±1000mPa . s\25℃, the hydroxyl content is 120-130%, the water content is ≤0.1%, the density is 1.01g / ml\20℃, and the flash point is about 23℃.

[0061] Wherein, the first solvent is selected from one or more of toluene, xylene, cyclohexanone, propylene glycol methyl ether acetate, and butyl acetate.

[0062] Wherein, the second solvent is selected from one or more of butyl acetate, ethyl acetate, and cyclohexanone.

[0063] A solid wood furniture penetrating primer was prepared according to the above-mentioned components.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
flash pointaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses special osmosis primer paint for solid wood furniture. The special osmosis primer paint comprises main paint and a curing agent. The main paint is prepared from, by weight, 40-60 parts of highly-wetting alkyd resin, 0.4-0.7 part of a polysiloxane antifoaming agent, 0.3-1.8 parts of a substrate wetting agent, 0.02-0.2 part of an organic tin drier and 40-50 parts of a first solvent. The curing agent is prepared from, by weight, 40-45 parts of hexamethylene diisocyanate, 13-18 parts of toluene diisocynate tripolymer and 39-44 parts of a second solvent. After the special osmosis primer paint for the solid wood furniture is painted on solid oak wood base materials and cured, the primer paint is subjected to thermal cycling in a thermal cycling machine for 40 times, wherein each-time thermal cycling refers to keeping at 80DEG C for 4h and at -20DEG C for 4h, and consequently paint defects such as peeling and mildewing are avoided.

Description

technical field [0001] The invention relates to a paint coating, in particular to a special penetrating primer for solid wood furniture. Background technique [0002] Wood is a structural material widely used in the furniture manufacturing and construction industries. In order to beautify wood products and prolong their service life, they need to be protected. At the same time, unlike other structural materials, wood has greater water content and water absorption than other materials; and the paint will also penetrate into the wood, so these will have an adverse effect on the coating. [0003] The invention patent with the authorization number CN101817906 uses acrylic monomers containing various polar groups as raw materials and adds various additives to prepare a water-based acrylic wood sealing coating. This coating has certain wettability to wood , and the latex particles can penetrate into the wood fiber conduit to form a film, which can prevent the moisture in the wat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/14C09D7/63C09D7/65C09D5/00C08G18/68
CPCC08G18/68C09D5/002C09D175/14C09D7/65C08L83/04
Inventor 李平梁文文
Owner 河南立邦长润发科技材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products